LIGHTWEIGHT COOL ROOF COATING COMPOSITIONS AND LIGHTWEIGHT COOL ROOF COATINGS
Disclosed herein are lightweight cool roof coating compositions and lightweight cool roof coatings. Also disclosed herein are lightweight reflective coating compositions, lightweight reflective coatings, and methods for making and applying the coating compositions of the present disclosure. The lightweight cool roof coating composition of the present disclosure comprises an aqueous polymer emulsion binder; and a pigment-filler component comprising: a reflective pigment, and a silica filler comprising cristobalite, tridymite, and optionally quartz, the silica filler comprising at least 50 wt % cristobalite based on the weight of the silica filler. The lightweight cool roof coating composition has a density (wet) of less than or equal to 1.38 g/cm 3 at a Pigment Volume Concentration (PVC) of 42%.
1 . A lightweight cool roof coating composition comprising:
an aqueous polymer emulsion binder; and
a pigment-filler component comprising:
a reflective pigment, and
a silica filler comprising cristobalite, tridymite, and optionally quartz, the silica filler comprising at least 50 wt % cristobalite based on the weight of the silica filler,
wherein the lightweight cool roof coating composition has a density (wet) of less than or equal to 1.38 g/cm 3 at a Pigment Volume Concentration (PVC) of 42%.
2 . The lightweight cool roof coating composition of claim 1 , wherein the reflective pigment comprises titanium dioxide.
3 . The lightweight cool roof coating composition of claim 2 , wherein the pigment-filler component consists of titanium dioxide and the silica filler.
4 . The lightweight cool roof coating composition of claim 1 , wherein the silica filler comprises:
50-99 wt % cristobalite,
1-30 wt % tridymite, and
0-50 wt % quartz.
5 . The lightweight cool roof coating composition of claim 1 , wherein the silica filler has a d50 particle size of 2-12 μm.
6 . The lightweight cool roof coating composition of claim 5 , wherein the silica filler has:
L* of 97-99,
a* less than 0, and
b* of 0-0.75.
7 . The lightweight cool roof coating composition of claim 1 , wherein the silica filler has a specific gravity of 2.3-2.4.
8 . The lightweight cool roof coating composition of claim 1 , wherein the lightweight cool roof coating composition has a density (wet) of 1.25-1.38 g/cm 3 at a Pigment Volume Concentration (PVC) of 42%.
9 . The lightweight cool roof coating composition of claim 1 , wherein when applied at 20 mils (wet) thickness on a substrate, the lightweight cool roof coating composition forms a lightweight cool roof coating having an L* of 95-99 and an average solar reflectance of at least 0.75.
10 . The lightweight cool roof coating composition of claim 9 , wherein the lightweight cool roof coating has an average total solar absorbance of less than 0.26.
11 . The lightweight cool roof coating composition of claim 1 , wherein the lightweight cool roof coating has a surface density (dry) of 780-865 g/m 2 .
12 . The lightweight cool roof coating composition of claim 1 , wherein the aqueous polymer emulsion binder comprises an acrylic emulsion binder, a silicone emulsion binder, a polyurethane emulsion binder, or combinations thereof.
13 . The lightweight cool roof coating composition of claim 1 comprising 35-50% PVC.
14 . The lightweight cool roof coating composition of claim 1 comprising from 25-40 wt % silica filler based on the total weight of the lightweight cool roof coating composition.
15 . A coated substrate comprising a structural substrate and the lightweight cool roof coating composition of claim 1 disposed thereon.
16 . The coated substrate of claim 15 , wherein the structural substrate is a roof.
17 . The coated substrate of claim 16 , wherein the roof is a low-slope or flat roof.
18 . A method of applying a cool roof to a structure comprising applying the lightweight cool roof coating composition of claim 1 to a roof of a structure.
19 . A method of making the lightweight cool roof coating composition of claim 1 comprising:
combining the reflective pigment and silica filler with water and dispersing to form a mixture, and
adding the aqueous polymer emulsion binder to the mixture and mixing to form the lightweight cool roof coating composition.
20 . A lightweight reflective coating composition comprising:
a binder system comprising an aqueous acrylic emulsion binder, a (meth)acrylate-based binder system, a solvent-based resin binder system, a low-VOC solvent-based binder system, a two-component binder system, or a thermoplastic binder system; and
a pigment-filler component comprising:
a reflective pigment, and
a silica filler comprising cristobalite, tridymite, and optionally quartz, the silica filler comprising at least 50 wt % cristobalite based on the weight of the silica filler, wherein the silica filler has:
L* of 97-99,
a* less than 0, and
b* of 0-0.75.
21 . The lightweight reflective coating composition of claim 20 , wherein the silica filler comprises:
50-99 wt % cristobalite,
1-30 wt % tridymite, and
0-50 wt % quartz.
22 . A coated substrate comprising a substrate and the lightweight reflective coating composition of claim 21 disposed thereon.
23 . The coated substrate of claim 22 , wherein the substrate is cement or asphalt pavement.