BINDER AND PREPARATION METHOD THEREOF, SEPARATOR, ELECTRODE PLATE, ELECTRODE ASSEMBLY, BATTERY CELL, BATTERY, AND ELECTRIC APPARATUS
A binder includes a polyacrylate copolymer and a lithium-containing compound. A preparation method of a binder includes adding monomers of a polyacrylate copolymer to a first emulsifier solution to obtain a pre-emulsion, adding an initiator to the pre-emulsion for reaction to obtain a reaction solution, and adding a lithium-containing substance to the reaction solution to adjust pH value to 7 to 8 and performing filtering to obtain the binder.
1 . A binder, comprising:
a polyacrylate copolymer; and
a lithium-containing compound.
2 . The binder according to claim 1 , wherein monomers of the polyacrylate copolymer comprise acrylate monomers, acrylonitrile monomers, and acrylamide monomers.
3 . The binder according to claim 2 , wherein a molar ratio of the acrylate monomers, the acrylonitrile monomers, and the acrylamide monomers is 1:(0.01 to 0.8):(0.01 to 0.15).
4 . The binder according to claim 2 , wherein:
the acrylate monomers comprise at least one of methyl acrylate, ethyl acrylate, n-butyl acrylate, isobutyl acrylate, sec-butyl acrylate, tert-butyl acrylate, n-propyl acrylate, cyclohexyl acrylate, lauryl acrylate, 2-ethylhexyl acrylate, 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate, methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, 2-ethylhexyl methacrylate, isobornyl methacrylate, lauryl methacrylate, 2-hydroxyethyl methacrylate, and 2-hydroxypropyl methacrylate; and/or
the acrylonitrile monomers comprise at least one of acrylonitrile and methacrylonitrile; and/or
the acrylamide monomers comprise at least one of acrylamide, N-methylolacrylamide, and N-butoxymethacrylamide.
5 . The binder according to claim 1 , wherein in the binder, a mass ratio of lithium to the polyacrylate copolymers is 1:(10 to 1000).
6 . The binder according to claim 1 , wherein the binder has a volumetric median particle size D v 50 of smaller than or equal to 50 μm,.
7 . A separator, comprising the binder according to claim 1 .
8 . An electrode plate, comprising the binder according to claim 1 .
9 . An electrode assembly, comprising the binder according to claim 1 .
10 . A battery cell, comprising the electrode assembly according to claim 9 .
11 . A battery, comprising the battery cell according to claim 10 .
12 . An electric apparatus, comprising the battery cell according to claim 10 .
13 . A preparation method of a binder, comprising:
adding monomers of a polyacrylate copolymer to a first emulsifier solution to obtain a pre-emulsion;
adding an initiator to the pre-emulsion for reaction to obtain a reaction solution; and
adding a lithium-containing substance to the reaction solution to adjust pH value to 7 to 8 and performing filtering to obtain the binder.
14 . The preparation method according to claim 13 , wherein adding monomers of the polyacrylate copolymer to the first emulsifier solution to obtain the pre-emulsion comprises adding acrylate monomers, acrylonitrile monomers, and acrylamide monomers to the first emulsifier solution to obtain the pre-emulsion.
15 . The preparation method according to claim 14 , wherein a molar ratio of the acrylate monomers, the acrylonitrile monomers, and the acrylamide monomers is 1:(0.01 to 0.8):(0.01 to 0.15).
16 . The preparation method according to claim 14 , wherein:
the acrylate monomer comprise at least one of methyl acrylate, ethyl acrylate, n-butyl acrylate, isobutyl acrylate, sec-butyl acrylate, tert-butyl acrylate, n-propyl acrylate, cyclohexyl acrylate, lauryl acrylate, 2-ethylhexyl acrylate, 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate, methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, 2-ethylhexyl methacrylate, isobornyl methacrylate, lauryl methacrylate, 2-hydroxyethyl methacrylate, and 2-hydroxypropyl methacrylate; and/or
the acrylonitrile monomers comprise at least one of acrylonitrile and methacrylonitrile; and/or
the acrylamide monomers comprise at least one of acrylamide, N-methylolacrylamide, and N-butoxymethacrylamide.
17 . The preparation method according to claim 13 , wherein adding the initiator to the pre-emulsion for reaction to obtain the reaction solution comprises:
under a heated reflux condition, adding the pre-emulsion to a second emulsifier solution and adding the initiator for reaction, to obtain the reaction solution.
18 . The preparation method according to claim 13 , wherein:
temperature for the reaction is 20° ° C. to 90° C.; and/or
duration of the reaction is 20 to 40 min.
19 . The preparation method according to claim 13 , wherein in adding the lithium-containing substance to the reaction solution to adjust pH value to 7 to 8 and performing filtering to obtain the binder:
the lithium-containing substance comprises at least one of lithium hydroxide, lithium oxide, lithium carbonate, and monolithic lithium; and/or
a mass ratio of lithium to the polyacrylate copolymer is 1:(10 to 1000).