HYDROGEN STORAGE ALLOY
A hydrogen storage alloy contains Mm, Ni, Mn, Al, and Co and has a main phase having a CaCu 5 -type crystal structure. La and Ce together account for 95 mass % or more of Mm. When the mole ratios of Ni, Mn, Al, and Co with respect to 1 mol of Mm are represented by a, b, c, and d, respectively, d is 0.00 or more and less than 0.15, d/b is 0.00 or more and 0.35 or less, and the sum of a+b+c+d is 5.22 or more and 5.44 or less. The ratio H/E of hardness H (GPa) to composite elastic modulus E (GPa) as measured using a nanoindentation technique is 0.08 or more and 0.15 or less.
1 . A hydrogen storage alloy comprising Mm (Mm represents a misch metal), Ni, Mn, Al, and Co and having a main phase that has a CaCu 5 -type crystal structure,
wherein La and Ce together account for 95 mass % or more of Mm,
d is 0.00 or more and less than 0.15,
d/b is 0.00 or more and 0.35 or less, and
a sum of a+b+c+d is 5.22 or more and 5.44 or less, and
a ratio H/E of hardness H (GPa) to composite elastic modulus E (GPa) as measured using a nanoindentation technique is 0.08 or more and 0.15 or less,
wherein a represents a molar ratio of Ni with respect to 1 mol of Mm
b represents a molar ratio of Mn with respect to 1 mol of Mm,
c represents a molar ratio of Al with respect to 1 mol of Mm, and
d represents a molar ratio of Co with respect to 1 mol of Mm.
2 . The hydrogen storage alloy according to claim 1 , wherein the hardness H is 1 GPa or more and 11 GPa or less.
3 . The hydrogen storage alloy according to claim 1 , wherein a ratio of c-axis length to a-axis length of the CaCu 5 -type crystal structure is 0.8080 or more and 0.8110 or less.
4 . The hydrogen storage alloy according to claim 1 , wherein c/b is 0.30 or more and 0.85 or less.
5 . The hydrogen storage alloy according to claim 1 , wherein a ratio of an area of a segregated phase to an area of a cross section of the hydrogen storage alloy is 0.01% or more and 1.60% or less, the cross section of the hydrogen storage alloy being observed using a scanning electron microscope.