EXHAUST GAS CLEANING CATALYST AND PRODUCTION METHOD THEREFOR
An exhaust gas purification catalyst including: a substrate; and an adsorbent portion provided to the substrate and containing a Si-containing adsorbent material. The adsorbent portion includes a plurality of voids, and in a cross section orthogonal to an exhaust gas flow direction, the percentage of a total area of the voids that are present in the adsorbent portion and that each satisfy the expression below is greater than 5% to 30% or less with respect to an apparent area of the adsorbent portion present on the substrate. Expression: L/{2(πS)½}≤1.1. (L is a perimeter of the void in the cross section, and S is an area of the void in the cross section.)
1 . An exhaust gas purification catalyst comprising:
a substrate; and
an adsorbent portion provided to the substrate and containing a Si-containing adsorbent material, wherein:
the adsorbent portion includes a plurality of voids; and
in a cross section orthogonal to an exhaust gas flow direction, the percentage of a total area of the voids that are present in the adsorbent portion and that each satisfy the expression below is greater than 5% to 30% or less with respect to an apparent area of the adsorbent portion present on the substrate:
L
/
{
2
(
π
S
)
1
/
2
}
≤
1.1
,
Expression
wherein L is a perimeter of the void in said cross section, and S is an area of the void in said cross section.
2 . The exhaust gas purification catalyst according to claim 1 , wherein the Si-containing adsorbent material is a zeolite.
3 . The exhaust gas purification catalyst according to claim 2 , wherein the zeolite is a zeolite having at least one type of pore structure selected from 10-membered rings and 12-membered rings.
4 . The exhaust gas purification catalyst according to claim 2 , wherein the zeolite is at least one type of zeolite selected from BEA-type, MSE-type, MFI-type, and YFI-type.
5 . The exhaust gas purification catalyst according to claim 2 , wherein a content by percentage of the zeolite in the adsorbent portion is from 10 to 90 mass %.
6 . The exhaust gas purification catalyst according to claim 1 , wherein the adsorbent portion includes at least one type of noble metal selected from Pt, Pd, and Rh.
7 . The exhaust gas purification catalyst according to claim 1 , wherein a value of said percentage with respect to a thickness of the adsorbent portion is from 0.20 to 1.00%/μm.
8 . The exhaust gas purification catalyst according to claim 1 , wherein an average value of circle equivalent diameters of voids that are present in the adsorbent portion and that satisfy said expression is from 1 to 60 μm.
9 . The exhaust gas purification catalyst according to claim 1 , wherein an average value of the number of voids that are present in the adsorbent portion and that satisfy said expression is from 200 to 800 per 1 mm 2 in cross-sectional area of the adsorbent portion.
10 . The exhaust gas purification catalyst according to claim 1 , wherein a standard deviation of the circle equivalent diameters of voids that are present in the adsorbent portion and that satisfy said expression is less than 25% of the average value of the circle equivalent diameters.
11 . The exhaust gas purification catalyst according to claim 1 , wherein the substrate is a flow-through substrate.
12 . The exhaust gas purification catalyst according to claim 1 , comprising, as the adsorbent portion, an adsorbent layer containing a Si-containing adsorbent material, and further comprising a purification layer containing a catalytically-active component.
13 . The exhaust gas purification catalyst according to claim 1 , wherein the adsorbent portion occupies from 20 to 50 mass % of a total coating amount.
14 . The exhaust gas purification catalyst according to claim 1 , comprising, as the adsorbent portion, an adsorbent layer containing a Si-containing adsorbent material, wherein a thickness of the adsorbent layer is from 20% to 80% of a thickness of an entire coating layer on the substrate.
15 . An exhaust gas purification system comprising:
at least two exhaust gas purification catalysts in an exhaust gas flow path,
wherein
the exhaust gas purification system includes the exhaust gas purification catalyst according to claim 1 as a second or subsequent catalyst from an upstream side of the exhaust gas flow direction.
16 . A method for manufacturing an exhaust gas purification catalyst, the method comprising:
a step of applying a slurry to a substrate, the slurry containing
a Si-containing adsorbent material,
a void former constituted by a crosslinked resin, wherein the percentage of particles of the void former having a roundness of L′/{2 (πS′) 1/2 }≤1.05 is 90% or higher in terms of the number of particles, and
water; and
a step of firing the slurry after being applied to the substrate, to form, on the substrate, an adsorbent layer including the adsorbent material and voids formed by firing and eliminating the void former, wherein:
after stirring the slurry at a rotation speed of from 3000 to 8000 rpm, the slurry is applied to the substrate in a state where the viscosity at 25° C. is from 2000 to 100000 cP; and
in said expression, L′ is an outer perimeter of the void former in an image obtained by observing the void former with a scanning electron microscope, and S′ is an area of the void former in an image obtained by observing the void former with a scanning electron microscope.
17 . The method for manufacturing an exhaust gas purification catalyst according to claim 16 , wherein an amount of the void former in the slurry is from 10 to 60 parts by mass with respect to 100 parts by mass of solid content in the slurry excluding the void former.