Three-dimensional printing
A polyol stiffening additive in a powder bed material for three-dimensional (3D) printing is disclosed herein. In an example, the 3D powder bed material includes an elastomeric build material and a polyol stiffening additive having 3 to 7 carbon atoms that is about 2 weight percent to about 20 weight percent of a total weight of the 3D powder bed material.
1 . A three-dimensional (3D) powder bed material that forms a 3D printed article, the 3D powder bed material consisting of:
an elastomeric build material; and
a polyol stiffening additive having from 3 to 7 carbon atoms, the polyol stiffening additive being present in an amount of from about 2 weight percent to about 20 weight percent of a total weight of the 3D powder bed material.
2 . The 3D powder bed material of claim 1 , wherein the elastomeric build material is a polyamide thermoplastic elastomer (TPA) or a thermoplastic polyurethane (TPU).
3 . The 3D powder bed material of claim 2 , wherein the elastomeric build material comprises 100 weight percent of the TPA or the TPU.
4 . The 3D powder bed material of claim 1 , wherein the polyol stiffening additive is selected from the group consisting of a diol, a triol, a tetrol, and any combination thereof.
5 . The 3D powder bed material of claim 1 , wherein the polyol stiffening additive is pentaerythritol.
6 . The 3D powder bed material of claim 1 , wherein the polyol stiffening additive is less than 10 weight percent of the total weight of the 3D powder bed material.
7 . The 3D powder bed material of claim 1 , wherein the 3D powder bed material, when fused in a 3D printing process, provides the 3D printed article having a Young's Modulus that is increased by at least 10% as compared to a Young's Modulus of a 3D printed article formed from the elastomeric build material in the absence of the polyol stiffening additive.
8 . The 3D powder bed material of claim 1 , wherein the 3D powder bed material, when fused in a 3D printing process, provides the 3D printed article having an ultimate tensile strength that is greater than or equal to 3 megapascals.
9 . The 3D powder bed material of claim 1 , wherein the 3D powder bed material, when fused in a 3D printing process, provides a 3D printed article having an elongation at break that is greater than or equal to 500 percent.
10 . A method of making a three-dimensional (3D) printed article, the method comprising:
applying a 3D powder bed material consisting of a mixture of an elastomeric build material and a polyol stiffening additive having from 3 to 7 carbon atoms to a fabrication bed; and
fusing the 3D powder bed material to form a 3D printed article.
11 . The method of claim 10 , further comprising:
selectively applying a fusing agent to the 3D powder bed material; and
responsive to the selectively applying of the fusing agent to the 3D powder bed material, fusing the 3D powder bed material to form the 3D printed article.
12 . The method of claim 11 , wherein the fusing agent comprises water and an absorber agent, and wherein the fusing of the 3D powder bed material comprises exposing the fabrication bed to radiation energy to selectively fuse portions of the 3D powder bed material in contact with the absorber agent and thereby form the 3D printed article.
13 . A three-dimensional (3D) printed article formed by:
applying a 3D powder bed material consisting of a mixture of an elastomeric build material and a polyol stiffening additive having from 3 to 7 carbon atoms to a fabrication bed;
selectively applying a fusing agent to the 3D powder bed material; and
responsive to the selectively applying of the fusing agent to the 3D powder bed material, fusing the 3D powder bed material to form the 3D printed article.
14 . The 3D printed article of claim 13 , wherein the 3D printed article has a Young's Modulus that is increased by at least 10% as compared to a Young's Modulus of a 3D printed article formed from the elastomeric build material in the absence of the polyol stiffening additive.