Composition comprising a polyamide block and polyether block copolymer and a crosslinked rubber powder
The invention relates to a composition comprising, relative to the total weight of the composition: from 20% to 90%, preferably from 40 to 70%, by weight of at least one polyamide block-polyether block copolymer, and from 10% to 80%, preferably from 30% to 60%, by weight, of at least one crosslinked rubber powder notably derived from used tires, from 0 to 5% of additives, preferably from 0.1% to 4%, notably from 1% to 2%; from 0 to 40% of compatibilizers, preferably from 5% to 20%, notably from 10% to 15%.
1 . A composition comprising, relative to the total weight of the composition:
from 20% to 90% by weight, of at least one polyamide block-polyether block copolymer, and
from 10% to 80% by weight, of at least one crosslinked rubber powder notably derived from used tires,
from 0 to 5% of additives by weight;
from 0 to 40% of compatibilizers by weight.
2 . The composition as claimed in claim 1 , in which the crosslinked rubber powder has a specific surface area of between 0.01 m2/g and 100 m2/g.
3 . The composition as claimed in claim 1 , in which the crosslinked rubber powder has a median diameter D50 of between 2 and 500 μm.
4 . The composition as claimed in claim 1 , in which the D90 diameter is between 10 and 800 μm.
5 . The composition as claimed in claim 1 , in which the rubber of the crosslinked rubber powder is a natural or synthetic rubber or a mixture thereof.
6 . The composition as claimed in claim 1 , in which the rubber of the crosslinked rubber powder contains from 0 to 50% by weight of a synthetic rubber or a mixture of synthetic rubbers.
7 . The composition as claimed in claim 1 , in which the rubber of the crosslinked rubber powder contains from 10% to 80% by weight of natural rubber.
8 . The composition as claimed in claim 7 , in which the natural rubber is cis-1,4-polyisoprene or trans-1,4-polyisoprene.
9 . The composition as claimed in claim 1 , in which the crosslinked rubber powder comprises styrene-butadiene rubber.
10 . The composition as claimed in claim 1 , in which the crosslinked rubber powder is obtained by water-jet chopping of a tire.
11 . The composition as claimed in claim 1 , in which the crosslinked rubber powder contains from 1% to 70% of carbon black and/or silica.
12 . The composition as claimed in claim 1 , in which the crosslinked rubber powder comprises less than 10% of fibrous material.
13 . The composition as claimed in claim 1 , in which the crosslinked rubber powder advantageously contains from 0.05% to 5% by weight of zinc oxide.
14 . The composition as claimed in claim 1 , in which the additive is chosen from a catalyst, an antioxidant, a thermal stabilizer, a UV stabilizer, a light stabilizer, a lubricant, a flame retardant, a nucleating agent, a chain extender and a dye.
15 . The composition as claimed in claim 1 , in which the at least one polyamide block-polyether block copolymer has a Shore hardness of between 10 D and 70 D.
16 . The composition as claimed in claim 1 , in which the polyamide blocks of the polyamide block-polyether block copolymer are blocks of polyamide 11, polyamide 12, polyamide 10, polyamide 6, polyamide 6.10, polyamide 6.12, polyamide 10.10 and/or polyamide 10.12; and/or the polyether blocks of the polyamide block-polyether block copolymer are polyethylene glycol and/or polytetrahydrofuran blocks.
17 . A process for preparing a composition as claimed in claim 1 , comprising the following steps:
mixing,
from 20% to 90% by weight of at least one polyamide block-polyether block copolymer, in the molten state and
from 10% to 80% by weight of at least one crosslinked rubber powder,
from 0 to 5% of additives,
from 0 to 40% of compatibilizers,
optionally, forming the mixture into the form of granules, filaments or powder, and/or
recovering the composition obtained.
18 . An article comprising at least one element comprising a composition as claimed in claim 1 , said article being chosen from footwear components, ski pole parts, racket and golf club handles, goalkeeper gloves, treadmills, aquatic equipment, spectacle frame parts, ski mask frames, vibration-isolating parts for electronics and machinery, external battery shells, automotive parts, toys, watch straps, machine buttons, seals or conveyor belt components.
19 . A process for manufacturing an article comprising the steps of:
providing a composition as claimed in claim 1 ;
injection molding of said composition.
20 . A process for recycling an article comprising the following successive steps:
a) recovering, after optional separation, at least part of said article made of thermoplastic material comprising a composition as claimed in claim 1 ,
b) grinding the thermoplastic material to obtain particles,
c) melting the particles to obtain a molten mixture, and
d) optionally, adding other components to the molten mixture,
e) optionally, forming granules, filaments or powders from the molten mixture obtained on conclusion of step c) or d), and
f) optionally, forming the granules, filaments or powders into shape.
21 . A granule, filament or powder which may be obtained according to the recycling process as defined in claim 20 .
22 . An article consisting of or comprising at least one element prepared from granules, filaments or powders as claimed in claim 21 .