High entropy alloy repair of nickel and cobalt superalloys

Inventors: Payank Patel (Montreal, CA); Mary E. Makowiec (Manchester, CT); Joël Larose (Longueuil, CA); Navid Sharifi (Verdun, CA); Pantcho P. Stoyanov (Beaconsfield, CA); Christian Moreau (Boucherville, CA); Richard Chromik (Montreal, CA)
Assignees: Pratt & Whitney Canada Corp.; Concordia University; The Royal Institution for the Advancement of Learning/McGill University
F02C3/14C22C30/00C23C4/08C23C4/129F02C7/28F05D2230/80F05D2300/17
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,680,496
App. No.
18/738,570
Granted
Jul 14, 2026
Kind
B2
Abstract

A method for repairing damage at a damage site on the surface of a nickel- or cobalt-based alloy. The method includes: machining at the damage site; and applying a high entropy alloy (HEA) repair material to the damage site via high velocity oxy-fuel (HVOF) spray, high velocity air-fuel (HVAF) spray, or cold spray.

Claims (72)

1 . A method for repairing damage at a damage site on the surface of a nickel- or cobalt-based alloy component, the method comprising:

machining at the damage site; and

applying a high entropy alloy (HEA) repair material to the damage site via high velocity oxy-fuel (HVOF) spray, high velocity air-fuel (HVAF) spray, or cold spray,

wherein the repair material comprises in atomic percent:

16.0 to 25.0 Fe;

16.0 to 25.0 Co;

16.0 to 25.0 Cr;

16.0 to 25.0 Mn; and

16.0 to 25.0 Ni.

2 . The method of claim 1 wherein:

the applying is via HVOF.

3 . The method of claim 1 wherein:

the surface is full annulus or a sector of an annulus; and

the applying is only to a partial circumferential extent of said full annulus or sector.

4 . The method of claim 1 wherein:

the surface is an inner diameter surface.

5 . The method of claim 1 wherein:

the surface is an axial end surface of a groove.

6 . The method of claim 1 wherein:

the surface is an axial end surface of a radial tab.

7 . The method of claim 1 wherein:

the surface is an inner diameter surface of a mounting pin socket.

8 . The method of claim 1 wherein the repair material comprises in atomic percent:

no more than 1.0 other individually and 5.0 other total.

9 . The method of claim 8 wherein:

the repair material is applied to a thickness of at least 0.50 millimeter;

a powder feed rate of the HVOF spray is 40 g/min. to 50 g/min.; and

a rate of oxygen is 100% to 250% a rate of fuel in the HVOF spray, measured in LPM.

10 . The method of claim 1 wherein:

the repair material is applied to a thickness of at least 0.50 millimeter.

11 . The method of claim 10 wherein the repair material comprises by atomic percent:

no more than 1.0 other individually and 5.0 other total.

12 . The method of claim 1 wherein one or more of:

the repair material is applied to a thickness of at least 0.50 millimeter;

a powder feed rate of the HVOF spray is 40 g/min. to 50 g/min.; and

a rate of oxygen is 100% to 250% a rate of fuel in the HVOF spray, measured in LPM.

13 . The method of claim 1 further comprising:

surface finishing to remove excess repair material;

disengaging the surface of the component from a second component prior to the machining; and

after the applying, reengaging the surface of the component to the second component or to a replacement second component, wherein the reengaging or engaging is without any further thermal sprayed coating atop the repair material.

14 . The method of claim 1 wherein the component is a first component of a gas turbine engine, the gas turbine engine comprising:

one or more compressor sections;

a combustor;

one or more turbine sections; and

a gaspath passing through the one or more compressor sections, the combustor section, and the one or more turbine sections,

wherein:

the first component is sealed to a second component by a seal;

the first component has a substrate;

the substrate has a recess to which the repair material is applied; and

a contact area between the seal and the first component includes the repair material and an adjacent surface of the substrate.

15 . The method of claim 14 wherein:

the contact area is at least 355° and 1° to 5° of that is with the repair material.

16 . The method of claim 14 wherein:

the repair material has a thickness of 0.30 mm to 2.0 mm.

17 . The method of claim 14 wherein the repair material comprises in atomic percent:

no more than 1.0 other individually and 5.0 other total.

18 . The method of claim 17 wherein:

the repair material has a thickness of 0.30 mm to 2.0 mm.

19 . The method of claim 14 wherein:

the second component has a radially outwardly open groove axially capturing the seal and the first component encircles the seal; or

the first component has a radially outwardly open groove axially capturing the seal and the second component encircles the seal.

20 . The method of claim 14 wherein:

the first component comprises a counterface of the seal; and

the seal is selected from the group consisting of piston seal rings, brush seals, and finger seals.

21 . The method of claim 1 wherein the component has:

a contact surface for contacting another component; and

the machining forms:

a recess at the contact surface to which the repair material is applied.

22 . The method of claim 21 wherein at least one of:

the component is in a gas turbine engine comprising: one or more compressor sections; a combustor; one or more turbine sections; and a gaspath passing through the one or more compressor sections, the combustor section, and the one or more turbine sections;

the another component is a seal or a locating pin; and

the contact area between the component and the another component includes the HEA-repair material and an adjacent surface of a substrate of the first component.

Assignments (2)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Jun 11, 2026
From: PATEL, PAYANK; STOYANOV, PANTCHO P.; MOREAU, CHRISTIAN; SHARIFI, NAVID
To: CONCORDIA UNIVERSITY
Reel/Frame 074921/0909 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Jun 11, 2026
From: LAROSE, JOEL; MAKOWIEC, MARY E.
To: PRATT & WHITNEY CANADA CORP.
Reel/Frame 074922/0001 →
Continuity (2)
Provisional Application 63472264 · Jun 9, 2023
Related Publication 20240410312A1 · Dec 12, 2024
References Cited (53)
US 5866518A · Dellacorte et al. · 1999 [cited by applicant]
US 8753417B1 · Dellacorte et al. · 2014 [cited by applicant]
US 11643939B2 · Stoyanov et al. · 2023 [cited by applicant]
US 20030033702A1 · Berry · 2003 [cited by examiner]
US 20030148141A1 · Zhao · 2003 [cited by examiner]
US 20050217110A1 · Topal · 2005 [cited by applicant]
US 20060248718A1 · Szela · 2006 [cited by examiner]
US 20110146848A1 · Bewlay · 2011 [cited by examiner]
US 20110168679A1 · Qi · 2011 [cited by examiner]
US 20150118516A1 · Boileau · 2015 [cited by examiner]
US 20160069184A1 · Ribic · 2016 [cited by examiner]
US 20160201169A1 · Vecchio · 2016 [cited by examiner]
US 20170122561A1 · Nagaraj · 2017 [cited by examiner]
US 20200149417A1 · McCaffrey · 2020 [cited by examiner]
US 20200291532A1 · Delfan-Azari · 2020 [cited by examiner]
US 20200318737A1 · Stoyanov et al. · 2020 [cited by applicant]
US 20210156007A1 · Chen · 2021 [cited by examiner]
US 20210270369A1 · Harrington et al. · 2021 [cited by applicant]
US 20220065122A1 · Stoyanov et al. · 2022 [cited by applicant]
US 20220325797A1 · Stoyanov et al. · 2022 [cited by applicant]
US 20240410045A1 · Islas Encalada et al. · 2024 [cited by applicant]
US 20240410046A1 · Patel et al. · 2024 [cited by applicant]
CN 104561878A · 2015 [cited by applicant]
CN 110117788A · 2019 [cited by applicant]
CN 113930754A · 2022 [cited by applicant]
CN 114032489A · 2022 [cited by applicant]
CN 114231882A · 2022 [cited by applicant]
CN 114369786A · 2022 [cited by applicant]
CN 114411081A · 2022 [cited by applicant]
CN 114669820A · 2022 [cited by applicant]
CN 114669956A · 2022 [cited by applicant]
CN 114703472A · 2022 [cited by applicant]
CN 111763904B · 2022 [cited by applicant]
CN 115401195A · 2022 [cited by applicant]
CN 115418595A · 2022 [cited by applicant]
CN 115449790A · 2022 [cited by applicant]
CN 112553564B · 2023 [cited by applicant]
Xiao et al. (Applicant's Specification paragraph [0012]) (Year: 2020). [cited by examiner]
Payank Patel et al., “Microstructurral and Tribological Behavior of Thermal Spray CrMnFeCoNi High Entropy Alloy Coatings”, J Therm Spray Tech, Mar. 9, 2022, pp. 1285-1301, Springer, Berlin, Germany. [cited by applicant]
Lei Li et al., “High-Temperature Friction and Wear Features of Nickel-Based Ssingle Crystal Superalloy”, Tribology Letters, Jan. 21, 2020, Springer, Berlin, Germany. [cited by applicant]
European Search Report dated Jul. 17, 2024 for European Patent Application 24181134.8. [cited by applicant]
Yan Cui et al., “Wear Resistance of FeCoCrNiMnAlx High-Entropy Alloy Coatings at High Temperature”, Applied Surface Science, May 15, 2020, p. 145736, vol. 512, Elsevier, Amsterdam, the Netherlands. [cited by applicant]
European partial search report dated Oct. 4, 2024 for European Patent Application No. 24181087.8. [cited by applicant]
Extended European Search Report dated Jan. 3, 2025 for European Patent Application No. 24181087.8. [cited by applicant]
Yang et al., “Electroplasticity in the Al0.6CoCrFeNiMn High Entropy Alloy Subjected to Electrically-Assisted Uniaxial Tension”, Journal of Materials Science & Technology, Jun. 10, 2023, pp. 209-221, vol. 148, Elsevier, … [cited by applicant]
He et al., “Effects of Al Addition on Structural Evolution and Tensile Properties of the FeCoNiCrMn High Entropy Alloy System”, Acta Materialia, Jan. 2014, pp. 105-113, vol. 62, Elsevier, Amsterdam, the Netherlands. [cited by applicant]
Luo et al., “Tribological Behavior of High Entropy Alloy Coatings: A Review”, Coatings, Sep. 29, 2022, p. 1428, vol. 12, issue 10, MDPI, Basel, Switzerland. [cited by applicant]
Tian et al., “Microstructure and Wear Behavior of Atmospheric Plasma-Sprayed AlCoCrFeNiTi High-Entropy Alloy Coating”, Journal of Materials Engineering and Performance, December, Oct. 18, 2016, pp. 5513-5521, vol. 25, A… [cited by applicant]
Xiao et al., “Microstructure and Wear Behavior of FeCoNiCrMn High Entropy Alloy Coating Deposited by Plasma Spraying”, Surface & Coatings Technology, Jan. 31, 2020, p. 125430, vol. 385, Elsevier, Amsterdam, the Netherla… [cited by applicant]
Lobel et al., “Microstructure and Wear Behavior of the High-Velocity-Oxygen-Fuel Sprayed and Spark Plasma Sintered High-Entropy Alloy AlCrFeCoNi”, Advanced Engineering Materials, Dec. 23, 2020, p. 2001253, vol. 23, Wile… [cited by applicant]
Patel et al., “Microstructural and Tribological Behavior of Thermal Spray CrMnFeCoNi High Entropy Alloy Coatings”, Journal of Thermal Spray Technology, Apr. 2022, pp. 1285-1301, vol. 31, Springer, Berlin, Germany. [cited by applicant]
Li et al., “Subsonic-Flame-Sprayed CoCrFeNi, AlCoCrFeNi and MnCoCrFeNi-Based High-Entropy Alloy Coatings and Their Tribological Behaviors”, Journal of Thermal Spray Technology, Nov. 23, 2022, pp. 96-110, vol. 32, Spring… [cited by applicant]
Li et al., “A Low-Cost Second Generation Single Crystal Superalloy DD6”, Superalloys 2000, Jan. 2000, pp. 777-783, TMS (The Minerals, Metals & Materials Society), Pittsburgh, Pennsylvania. [cited by applicant]