NICKEL OXIDE SOL-GEL INK
A method for preparing a nickel oxide precursor ink comprising: preparing a solvent comprising diols and alcohol amines; adding nickel nitrate into the solvent to form a nickel nitrate containing solution; adding at least one metal acetate into the nickel nitrate containing solution to form a nickel nitrate and metal acetate containing solution; adding water to the nickel nitrate and metal acetate containing solution to form a nickel oxide precursor mixture; heating the nickel oxide precursor mixture to 60 to 75 Celsius; and cooling the nickel oxide precursor mixture to form the nickel oxide precursor ink.
1 . A method for depositing a nickel oxide layer comprising:
preparing a substrate;
depositing a nickel oxide precursor ink onto the substrate, wherein the nickel oxide precursor ink comprises:
a solvent comprising diols, alcohol amines, and water;
Ni(NO 3 ) 2 ·6H 2 O; and
at least one metal acetate selected from the group consisting of Ni(CH 3 CO 2 ) 2 ·4H 2 O and Cu(CH 3 CO 2 ) 2 ·1H 2 O;
annealing the nickel oxide precursor ink at a temperature between 250° to 400° Celsius for between 10 minutes and 6 hours; and
cooling the nickel oxide precursor ink to form the nickel oxide layer.