LOW IMPURITY LIGNOCELLULOSIC CARBON
Presently described are chemically activated lignocellulosic carbon adsorbent materials comprising high surface area, high microporosity, and low impurities, and methods of making the same. The described structures provide unexpected advantages as compared to currently available materials.
1 . An activated lignocellulosic carbon material comprising a chemically activated lignocellulosic carbon, wherein the chemically activated lignocellulosic carbon is treated with at least one of an acid wash, a heat treatment or combination thereof, thereby having a reduced impurity level as compared to an untreated activated carbon.
2 . The activated lignocellulosic carbon material of claim 1 , wherein the impurity comprises at least one of ash, iron, potassium, sulfur, calcium, sodium, zinc, phosphorus, silicon, copper, cobalt, aluminum, magnesium, nickel, chromium, barium, selenium, or a combination thereof.
3 . The activated lignocellulosic carbon material of claim 2 , wherein the chemically activated lignocellulosic carbon has a reduction in the amount of phosphorus as compared to untreated activated carbon.
4 . The activated lignocellulosic carbon material of claim 3 , wherein the chemically activated lignocellulosic carbon has a phosphorus content of less than about 800 ppm.
5 . The activated lignocellulosic carbon material of claim 1 , wherein the chemically activated lignocellulosic carbon has a ratio of micropore volume to total pore volume ratio of at least 50%.
6 . The activated lignocellulosic carbon of claim 1 , wherein the chemically activated lignocellulosic carbon has a ratio of micropore volume to total pore volume ratio of less than 50%.
7 . The activated lignocellulosic carbon of claim 1 , wherein the chemically activated lignocellulosic carbon has a has a BET surface of at least 1200 m 2 /g.
8 . The activated lignocellulosic carbon of claim 7 , wherein the chemically activated lignocellulosic carbon has a BET surface of at least 1300 m 2 /g.
9 . The activated lignocellulosic carbon of claim 1 , wherein the chemically activated lignocellulosic carbon is activated by phosphoric acid.
10 . The activated lignocellulosic carbon of claim 1 , wherein the lignocellulosic carbon comprises at least one of peat, wood, wood dust, wood flour, cotton linters, nut shells or pits, carbohydrates, fruit pits or fruit stones, sawdust, palm, vegetables such as rice hull or straw, natural polymers, coconut shells or combinations thereof.
11 . The activated lignocellulosic carbon of claim 10 , wherein the lignocellulosic carbon comprises wood or sawdust or both.
12 . The activated lignocellulosic carbon of claim 5 , wherein the chemically activated lignocellulosic carbon comprises a micropore volume, based on the total pore volume, of more than 60%.
13 . An activated lignocellulosic carbon material comprising a chemically activated lignocellulosic carbon wherein the chemically activated lignocellulosic carbon has less than about 800 ppm of phosphorus.
14 . The activated lignocellulosic carbon material of claim 13 , wherein the chemically activated lignocellulosic carbon is treated with at least one of an acid wash, a heat treatment or combination thereof, thereby having a reduced impurity level as compared to an untreated activated carbon.
15 . The activated lignocellulosic carbon material of claim 14 , wherein the impurity is at least one of ash, iron, potassium, sulfur, calcium, sodium, zinc, silicon, copper, cobalt, aluminum, magnesium, nickel, chromium, barium, selenium, or a combination thereof as compared to untreated activated carbon.
16 . The activated lignocellulosic carbon material of claim 13 , wherein the chemically activated lignocellulosic carbon has a ratio of micropore volume to total pore volume ratio of at least 50%.
17 . The activated lignocellulosic carbon material of claim 13 , wherein the chemically activated lignocellulosic carbon has a has a BET surface of at least 1200 m 2 /g.
18 . The activated lignocellulosic carbon material of claim 17 , wherein the chemically activated lignocellulosic carbon has a BET surface of at least 1300 m 2 /g.
19 . The activated lignocellulosic carbon material of claim 13 , wherein the chemically activated lignocellulosic carbon is activated by phosphoric acid.
20 . The activated lignocellulosic carbon material of claim 13 , wherein the lignocellulosic carbon comprises at least one of peat, wood, wood dust, wood flour, cotton linters, nut shells or pits, carbohydrates, fruit pits or fruit stones, sawdust, palm, vegetables such as rice hull or straw, natural polymers, coconut shells or combinations thereof.
21 . The activated lignocellulosic carbon material of claim 20 , wherein the lignocellulosic carbon comprises wood or sawdust or both.
22 . The activated lignocellulosic carbon material of claim 13 , wherein the chemically activated lignocellulosic carbon comprises a ratio of micropore volume to total pore volume ratio of less than about 50%.
23 . The activated lignocellulosic carbon of claim 13 , wherein the chemically activated lignocellulosic carbon comprises a micropore volume, based on the total pore volume, of more than 60%.
24 . A chemically activated lignocellulosic carbon material comprising a chemically activated lignocellulosic carbon having at least one of a Brunauer-Emmet-Teller (BET) surface area of at least 500 m 2 /g, a ratio of micropore volume to total pore volume ratio of at least 50%, a ratio of micropore volume to total pore volume ratio of less than 50% or a combination thereof, wherein the chemically activated lignocellulosic carbon is treated with an acid wash or heat, thereby having a reduced impurity level as compared to an untreated activated carbon.
25 . The activated lignocellulosic carbon material of claim 24 , wherein the impurity is at least one of ash, iron, potassium, phosphorus, sulfur, calcium, sodium, zinc, silicon, copper, cobalt, aluminum, magnesium, nickel, chromium, barium, selenium, or a combination thereof as compared to untreated activated carbon.
26 . The chemically activated lignocellulosic carbon material of claim 25 , wherein the chemically activated lignocellulosic carbon has a phosphorus content of less than about 500 ppm.
27 . The chemically activated lignocellulosic carbon material of claim 24 , wherein the chemically activated lignocellulosic carbon has a BET surface of at least 1300 m 2 /g.
28 . The chemically activated lignocellulosic carbon material of claim 24 , wherein the chemically activated lignocellulosic carbon comprises a micropore volume, based on the total pore volume, of more than 60%.