PHOSPHOR AND METHOD FOR PRODUCING SAME
Provided is a phosphor coated with aluminum oxide, wherein when peak separation is performed on a 1 H-NMR spectrum of the phosphor in a range where a 1 H chemical shift value is from 0.5 to 11 ppm, peaks 1, 2 and 3 are obtained. Peak 1 has a top at a 1 H chemical shift value of 4.0 to 5.5 ppm, peak 2 has a top at a 1 H chemical shift value of 2.0 to 2.8 ppm, and peak 3 has a top at a 1 H chemical shift value of 0.5 to 1.5 ppm. A ratio S 2 /(S 1 +S 2 +S 3 ) is 0.39 or less, wherein S 1 represents an integral value of peak 1 in a range where a 1 H chemical shift value is from −2 to 12 ppm, S 2 represents an integral value of peak 2 in the same range, and S 3 represents an integral value of peak 3 in the same range.
1 . A phosphor coated with aluminum oxide, wherein when peak separation is performed on a 1 H-NMR spectrum of the phosphor in a range where a 1 H chemical shift value is from 0.5 to 11 ppm, a peak 1, a peak 2, and a peak 3 are obtained, wherein the peak 1 is a peak having a peak top at a 1 H chemical shift value of 4.0 to 5.5 ppm, the peak 2 is a peak having a peak top at a 1 H chemical shift value of 2.0 to 2.8 ppm, and the peak 3 is a peak having a peak top at a 1 H chemical shift value of 0.5 to 1.5 ppm, and
a ratio S 2 /(S 1 +S 2 +S 3 ) is 0.39 or less,
wherein S 1 represents an integral value of the peak 1 in a range where a 1 H chemical shift value is from −2 to 12 ppm,
S 2 represents an integral value of the peak 2 in the same range,
S 3 represents an integral value of the peak 3 in the same range, and
the ratio S 2 /(S 1 +S 2 +S 3 ) is a ratio of S 2 to the sum of S 1 , S 2 , and S 3 .
2 . A phosphor coated with aluminum oxide, wherein in a one-dimensional graph plotting an average diffraction intensity against a magnitude Q of a scattering vector, a ratio S 4 /BG 4 is 0.09 or more,
wherein S 4 represents an integral value of a peak in a range where Q is from 17 to 26 nm −1 and
BG 4 represents an integral value of a background signal in the same range,
wherein the one-dimensional graph is created by obtaining an electron diffraction pattern of the phosphor by nanobeam electron diffractometry using a transmission electron microscope and averaging diffraction intensities in a radial direction from a center of a transmission spot.
3 . The phosphor according to claim 1 , wherein the aluminum oxide is amorphous.
4 . The phosphor according to claim 1 , wherein the phosphor has a specific surface area of 1 to 10 m 2 /g.
5 . The phosphor according to claim 1 , wherein the phosphor has an aluminum content of 10000 to 100000 ppm as measured by ICP emission spectrometry.
6 . A method for producing a phosphor coated with aluminum oxide, comprising coating a phosphor as a base material with aluminum oxide by atomic layer deposition, and then heating the resultant at 200 to 800° C.