Use of residual iron within granulated metallic unit production facilities, and associated systems, devices, and methods
Reduced-waste systems and methods for granulated metallic units (GMUs) production are disclosed herein. A representative method can include receiving a first supply of molten iron and producing GMUs by granulating the molten iron poured onto a target material of a reactor. The method can include removing residual fines of the GMUs via a classifier based on a threshold particle size and mixing the residual fines with a second supply of molten iron to produce additional GMUs.
1 . A method for producing granulated metallic units (GMUs), the method comprising:
receiving a first supply of molten iron;
producing GMUs by granulating the molten iron poured onto a target material of a reactor;
removing residual fines of the GMUs via a classifier, based on a threshold particle size between 1-10 mm; and
mixing the residual fines with a second supply of molten iron, different than the first supply of molten iron, to produce additional GMUs.
2 . The method of claim 1 , wherein mixing the residual fines with the second supply of molten iron comprises melting the residual fines via the second supply of molten iron.
3 . The method of claim 1 , wherein mixing the residual fines comprises adding the residual fines to a transfer vessel, and melting the residual fines in the transfer vessel by adding molten iron to the transfer vessel.
4 . The method of claim 1 , wherein the threshold particle size is between 1-6 mm.
5 . The method of claim 1 , wherein the residual fines comprise less than 5% by weight of the GMUs having the particle size above the threshold particle size.
6 . The method of claim 1 , further comprising producing slag as a byproduct of producing the GMUs, wherein the residual fines comprise no more than 60% by weight of the slag.
7 . The method of claim 1 , further comprising:
producing slag as a byproduct of producing the GMUs;
separating residual iron from the slag;
mixing at least a portion of the residual iron with scrap metal to produce a blend; and
providing at least a portion of the blend to a blast furnace and/or a basic oxygen furnace to produce molten iron.
8 . The method of claim 1 , further comprising maintaining a temperature of the residual fines above a threshold temperature until mixing the residual fines with the second supply of molten iron.
9 . The method of claim 1 , wherein the molten iron is received from a blast furnace.
10 . The method of claim 1 , wherein the molten iron is received from a basic oxygen furnace.
11 . The method of claim 1 , further comprising:
receiving imported residual fines;
mixing the imported residual fines with the second supply of molten iron in a transfer vessel to produce the GMUs.
12 . The method of claim 1 , wherein mixing the residual fines comprises adding the residual fines to a ladle, and melting the residual fines in the ladle by adding molten iron to the ladle.
13 . The method of claim 1 , further comprising:
receiving imported residual iron;
mixing at least a portion of the residual iron with scrap metal to produce a blend; and
providing at least a portion of the blend to a blast furnace and/or a basic oxygen furnace to produce the first supply of molten iron.
14 . The method of claim 1 , further comprising:
producing residual iron as a byproduct of producing the GMUs, the residual iron comprising one or more of thin pig, steel, skulls, sinter, slag, scrap, or iron dust;
mixing at least a portion of the residual iron with scrap metal to produce a blend; and
providing at least a portion of the blend to a blast furnace and/or a basic oxygen furnace to produce the first supply of molten iron.
15 . A method for producing granulated metallic units (GMUs), the method comprising:
receiving a first supply of molten iron from a blast furnace and/or a basic oxygen furnace;
producing GMUs by granulating the molten iron poured onto a target material of a reactor;
removing residual iron as a byproduct of producing the GMUs, the residual iron comprising one or more of thin pig, steel, skulls, sinter, slag, scrap, or iron dust;
mixing at least a portion of the residual iron with scrap metal to produce a blend; and
providing at least a portion of the blend to the blast furnace and/or the basic oxygen furnace to produce a second supply of molten iron, different than the first supply of molten iron, to produce additional GMUs.
16 . The method of claim 15 , wherein removing the residual iron comprises separating the residual iron from slag produced as a byproduct of producing the GMUs.
17 . The method of claim 15 , further comprising:
removing residual fines of the GMUs via a classifier, based on a threshold particle size; and
mixing the residual fines with a second supply of molten iron, different than the first supply of molten iron, to produce additional GMUs.
18 . The method of claim 15 , further comprising removing residual fines of the GMUs based on a threshold particle size between 1-10 mm.