CATHODE WITH DISORDERED ROCKSALT MATERIAL AND METHOD OF FORMING THE CATHODE
A method for forming a cathode includes milling a suspension of precursors via a micromedia mill to form a mixture of primary particles in the suspension. The precursors include one or more metal compounds. The method includes spray drying the suspension after the milling to form secondary particles. The secondary particles are agglomerations of the primary particles. The method also includes annealing the secondary particles to form a disordered rocksalt powder.
1 - 17 . (canceled)
18 . A method for forming a lithium ion battery, the method comprising:
milling a suspension of precursors to form a mixture of primary particles in the suspension, the precursors including one or more metal compounds;
spray drying the suspension after the milling to form secondary particles, wherein the secondary particles are agglomerations of the primary particles;
annealing the secondary particles to form a disordered rocksalt powder;
milling the disordered rocksalt powder with one or more carbon precursors after the annealing;
mixing the disordered rocksalt powder with one or more solvents to form a slurry;
drying the slurry on a metal current collector to form a composite cathode film;
inserting the composite cathode film into a cell casing such that a separator is disposed between the composite cathode film and an anode; and
supplying an electrolyte into the cell casing.
19 . The method of claim 18 , wherein the electrolyte includes a lithium salt present at a concentration suitable for conducting lithium ions through the electrolyte between the composite cathode film and the anode.
20 . The method of claim 18 , wherein the spray drying forms the secondary particles to have an average particle size no less than 1 micrometer and no greater than 20 micrometers.
21 . The method of claim 18 , wherein the disordered rocksalt powder is represented by formula (i):
Li x N y M z O 2−a F a (i)
where 1 .0<x<1.65; 0.01<y<0.55; 0.1<z<1; 0≤a<0.5; N is one of Ti, Ta, Zr, W, Nb, or Mo; and M is one of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Al, Zr, Y, Mo, Ru, Rh or Sb.
22 . The method of claim 18 , wherein the suspension is comprised of deionized water.
23 . The method of claim 18 , wherein the precursors are comprised of a lithium source.
24 . The method of claim 18 , wherein the suspension containing precursors does not contain a lithium source.
25 . The method of claim 24 , wherein a lithium source is mixed and annealed with the secondary particles to undergo calcination with the secondary particles.
26 . The method of claim 25 , wherein the lithium source is Li 2 CO 3 , LiOH, LiF, or a combination thereof.
27 . The method of claim 18 , wherein the anode is a lithium foil anode.