Gypsum Panel Containing an Acetate Polymer
The present disclosure is directed to a gypsum panel and a method of making such gypsum panel. For instance, the gypsum panel comprises a gypsum core and a first facing material and a second facing material sandwiching the gypsum core, wherein the gypsum core includes gypsum and an acetate polymer. The acetate polymer is present in an amount of less than 1 wt. % based on the weight of the gypsum. The gypsum panel exhibits a nail pull resistance of at least about 70 lb f when tested in accordance with ASTM C1396-17. The method of the present disclosure is directed to making the aforementioned gypsum panel by providing the first facing material, providing a gypsum slurry comprising gypsum, water, and an acetate polymer onto the first facing material, wherein the acetate polymer is present in an amount of less than 1 wt. % based on the weight of the stucco, and providing a second facing material on the gypsum slurry. The gypsum panel exhibits a nail pull resistance of at least about 70 lb f when tested in accordance with ASTM C1396-17.
1 . A gypsum panel comprising a gypsum core and a first facing material and a second facing material sandwiching the gypsum core, wherein the gypsum core comprises gypsum and an acetate polymer and wherein the acetate polymer is present in an amount of less than 1 wt. % based on the weight of the gypsum,
wherein the gypsum panel exhibits a nail pull resistance of at least about 70 lb f when tested in accordance with ASTM C1396-17.
2 . The gypsum panel of claim 1 , wherein the gypsum is present in an amount of at least 60 wt. % based on the weight of the gypsum core.
3 . The gypsum panel of claim 1 , wherein the acetate polymer comprises a vinyl acetate polymer, a cellulose acetate polymer, or a mixture thereof.
4 . The gypsum panel of claim 1 , wherein the acetate polymer includes a vinyl acetate polymer.
5 . The gypsum panel of claim 1 , wherein the vinyl acetate polymer includes a polyvinyl acetate homopolymer.
6 . The gypsum panel of claim 1 , wherein the gypsum core comprises polyvinyl alcohol in an amount of from 0 wt. % to less than 0.5 wt. % based on the weight of the gypsum core.
7 . The gypsum panel of claim 1 , wherein the gypsum core comprises polyvinyl alcohol in an amount of from 0 wt. % to less than 0.2 wt. % based on the weight of the gypsum core.
8 . The gypsum panel of claim 1 , wherein the gypsum core is free of polyvinyl alcohol.
9 . The gypsum panel of claim 1 , wherein the acetate polymer is present in an amount of less than 0.8 wt. % based on the weight of the gypsum.
10 . The gypsum panel of claim 1 , wherein the acetate polymer is present in an amount from about 0.001 wt. % to about 0.1 wt. % based on the weight of the gypsum.
11 . The gypsum panel of claim 1 , wherein the gypsum core further comprises a surfactant utilized for stabilizing the acetate polymer.
12 . The gypsum panel of claim 1 , wherein the gypsum core further comprises a starch.
13 . The gypsum panel of claim 12 , wherein the starch comprises a pearl starch.
14 . The gypsum panel of claim 12 , wherein the starch comprises an acid-modified starch.
15 . The gypsum panel of claim 12 , wherein the starch comprises a pregelatinized starch.
16 . The gypsum panel of claim 12 , wherein the starch is present in the gypsum core in an amount greater than the acetate polymer.
17 . The gypsum panel of claim 1 , wherein the gypsum core comprises expanded perlite in an amount of from 0 wt. % to less than 0.5 wt. % based on the weight of the gypsum core.
18 . The gypsum panel of claim 1 , wherein the gypsum panel exhibits a nail pull resistance of at least about 77 lb f when tested in accordance with ASTM C1396-17.
19 . The gypsum panel of claim 1 , wherein the gypsum panel exhibits a nail pull resistance of at least about 90 lb f when tested in accordance with ASTM C1396-17.
20 . The gypsum panel of claim 1 , wherein the gypsum panel has an NRC value of less than 0.32 when tested in accordance with ASTM E1050-19.
21 . The gypsum panel of claim 1 , wherein the gypsum panel has an NRC value of less than 0.25 when tested in accordance with ASTM E1050-19.
22 . A method for making a gypsum panel, the method comprising:
providing a first facing material;
depositing a gypsum slurry comprising stucco, water, and an acetate polymer onto the first facing material, wherein the acetate polymer is present in an amount of less than 1 wt. % based on the weight of the stucco;
providing a second facing material on the gypsum slurry; and
allowing the stucco to convert to calcium sulfate dihydrate;
wherein the gypsum panel exhibits a nail pull resistance of at least about 70 lb f when tested in accordance with ASTM C1396-17.