High comparative tracking index polycarbonate compositions with improved flame retardant and hydro-stability properties
Polycarbonate compositions include: (a) from about 45 wt % to about 90 wt % of a polycarbonate homopolymer; (b) from about 1 wt % to about 25 wt % of a polycarbonate copolymer; (c) from about 0.1 wt % to about 20 wt % of a first flame retardant component including a brominated flame retardant; (d) from about 0.01 wt % to about 1 wt % of a second flame retardant component including an alkyl sulfonate salt, an aromatic sulfone sulfonate, an aromatic sulfonate salt, or a combination thereof; and (e) from about 0.1 wt % to about 20 wt % of a siloxane-free acrylic core-shell impact modifier. The combined weight percent value of all components does not exceed 100 wt %, and all weight percent values are based on the total weight of the composition.
1. A polycarbonate composition comprising:
a. from about 45 wt % to about 90 wt % of a polycarbonate homopolymer;
b. from about 1 wt % to about 25 wt % of a polycarbonate copolymer;
c. from about 0.1 wt % to about 20 wt % of a first flame retardant component comprising a brominated flame retardant;
d. from about 0.01 wt % to about 1 wt % of a second flame retardant component comprising an alkyl sulfonate salt, an aromatic sulfone sulfonate, an aromatic sulfonate salt, or a combination thereof; and
e. from about 0.1 wt % to about 20 wt % of a siloxane-free acrylic core-shell impact modifier,
wherein the composition comprises less than 0.1 wt % siloxane, and
wherein the combined weight percent value of all components does not exceed 100 wt %, and all weight percent values are based on the total weight of the composition.
2. The thermoplastic composition according to claim 1 , wherein the polycarbonate copolymer comprises a poly(aliphatic ester-carbonate) copolymer comprising from 0.1 to 10 mol % sebacic acid monomer units and 90-99.9 mol % bisphenol-A monomer units.
3. The thermoplastic composition according to claim 2 , wherein the composition comprises from about 1 wt % to about 20 wt % of the poly(aliphatic ester-carbonate) copolymer.
4. The thermoplastic composition according to claim 1 , wherein the composition has a total bromine content of from about 0.5 wt % to about 8 wt %.
5. The thermoplastic composition according to claim 1 , wherein the first flame retardant component comprises a brominated polycarbonate, a brominated polyacrylate, a brominated cyanurate, or a combination thereof.
6. The thermoplastic composition according to claim 1 , wherein the siloxane-free acrylic core-shell impact modifier comprises acrylate rubber as the core.
7. The thermoplastic composition according to claim 1 , wherein the composition further comprises from greater than 0 wt % to about 2 wt % of an anti-drip agent.
8. The thermoplastic composition according to claim 7 , wherein the anti-drip agent comprises styrene acrylonitrile encapsulated polytetrafluoroethylene (SAN-PTFE).
9. The thermoplastic composition according to claim 1 , wherein the composition comprises at least one additional additive comprising an acid scavenger, an anti-drip agent, an antioxidant, an antistatic agent, a chain extender, a colorant, a release agent, a flow promoter, a lubricant, a plasticizer, a quenching agent, an additional flame retardant, a UV stabilizer, a UV reflecting additive, an additional impact modifier, a blowing agent, a reinforcing agent, or a combination thereof.
10. The thermoplastic composition according to claim 1 , wherein the composition does not include a polyester component.
11. The thermoplastic composition according to claim 1 , wherein the composition has a comparative tracking index (CTI) rating of PLC0 as determined in accordance with ASTM D3638.
12. The thermoplastic composition according to claim 1 , wherein the composition has a notched Izod impact strength (NII) retention of at least 10% after 3000 hours of DH85 aging at a temperature of 85° C. and 85% relative humidity, wherein NII is evaluated before and after DH85 aging and is tested at a temperature of 23° C. according to ASTM D256.
13. The thermoplastic composition according to claim 1 , wherein the composition has a UL94 flame retardant rating of V0 at a thickness of 1.0 millimeter (mm).
14. An article comprising the thermoplastic composition according to claim 1 , wherein the article is a component of a consumer electronics device, an electrical connector, an insulating housing, or an insulating material for a solar photovoltaic or electric vehicle.