CATALYSTS CONTAINING COPPER, ZINC OXIDE, ALUMINA AND SILICA
A catalyst suitable for use in carbon oxide conversion reactions is described, said catalyst in the form of a shaped unit formed from an oxidic catalyst powder, said catalyst comprising 30-70% by weight of copper oxide, combined with zinc oxide, alumina and silica, having a Si:Al atomic ratio in the range 0.005 to 0.15:1, and having a BET surface area ≥105 m 2 /g and a copper surface area >37 m 2 /g catalyst. The catalyst is prepared by a co-precipitation method using an alumina sol.
1 . A catalyst, suitable for use in carbon oxide conversion reactions, in the form of a shaped unit formed from an oxidic catalyst powder, said catalyst comprising 30-70% by weight of copper oxide (CuO) based on a total weight of the catalyst, as well as zinc oxide (ZnO), alumina and silica, having a Si:Al atomic ratio in a range 0.005:1 to 0.15:1, a BET surface area as determined by nitrogen physisorption ≥ 107m 2 /g, and a copper surface area >37m 2 /g catalyst, and wherein the catalyst further comprises one or more promoter compounds that are compounds of Mg, Co, Mn, V, Ti, Zr or rare earth metals.
2 . The catalyst according to claim 1 , wherein the catalyst is a methanol synthesis catalyst comprising copper oxide in an amount in a range 50 to 70% by weight.
3 . The catalyst according to claim 2 , wherein a weight ratio CuO:ZnO is in a range of 2:1 to 3.5:1.
4 . The catalyst according to claim 2 , wherein the catalyst contains 20 to 30% by weight of the zinc oxide, based on a total weight of the catalyst.
5 . The catalyst according to claim 1 , wherein the catalyst contains 5 to 20% by weight of the alumina, based on a total weight of the catalyst.
6 . The catalyst according to claim 1 , wherein the catalyst has a copper surface area ≥40m 2 /g.
7 . The catalyst according to claim 1 , wherein the catalyst contains 0.05 to 1.50% by weight of the silica, based on the total weight of the catalyst.
8 . The catalyst according to claim 1 , wherein the Si:Al atomic ratio is in a range of 0.03:1 to 0.07:1.
9 . The catalyst according to claim 1 , wherein a Si:Cu atomic ratio is in a range of 0.001:1 to 0.018:1.
10 . The catalyst according to claim 1 , wherein the BET surface area of the catalyst, as determined by nitrogen physisorption, is ≥109m 2 /g.
11 . The catalyst according to claim 1 , wherein the BET surface area of the catalyst, as determined by nitrogen physisorption, is ≥110m 2 /g.
12 . The catalyst according to claim 1 , wherein the BET surface area of the catalyst, as determined by nitrogen physisorption, is ≥115m 2 /g.
13 . The catalyst according to claim 1 , wherein the BET surface area of the catalyst, as determined by nitrogen physisorption, is ≥105m 2 /g up to about 140m 2 /g.