Method to increase the adherence of coating materials on ferrous materials
Method to increase the adherence of coating materials on ferrous materials, comprising the step of: before the reduction of iron ores and/or on the agglomerates thereof, contacting same with a dispersion containing at least a particulate material, thus forming a composite coating of at least a material that cannot be substantially hardened in the aqueous mean and at least a material that can be hardened in the aqueous mean.
1. A method of operating a direct reduction furnace with a reduction in the formation of agglomerates and increasing the adherence of non-hardenable coating materials on ferrous materials comprising contacting the ferrous material with an aqueous mixture of the non-hardenable coating materials and a material which hardens in the presence of water thereby forming a coating film on the ferrous material surface.
2. The method of claim 1 wherein the material used to harden the coating film is selected from the group consisting of Portland cements, pozzolanic cements, aluminous cements and mixtures thereof.
3. The method of claim 2 wherein the cements have particle size distribution between 0.01 micrometer and 100 micrometers.
4. The method of claim 2 wherein the weight ratio of cement to ferrous material is between 1 to 40 and 1 to 5.
5. The method of claim 1 wherein the non-hardenable material used to coat the ferrous material surface is selected from the group consisting of bentonite clays, bauxite, aluminum containing clay and mixtures thereof.
6. The method of claim 5 wherein the non-hardenable material has particle size distribution between 0.01 micrometer and 500 micrometers.
7. The method of claim 5 wherein the non-hardenable material has particle size distribution between 0.05 micrometer and 100 micrometers.
8. The method of claim 5 wherein the non-hardenable material ranges from 0.01% by weight to approximately 2% by weight in relation to the dry weight of the ferrous material to be coated.
9. The method of claim 1 , wherein the ferrous material is pellet, briquette, sized or fine ore.
10. The method of claim 1 , wherein the sum of hardenable plus non-hardenable material in the water dispersion ranges from 1 to 80% by weight of the dispersion.