View Patent ↗The invention provides a process for the purification of polymer polyols that ensures a reduction of acrylonitrile, styrene as well as the residual amounts of optionally used chain regulator, and of occurring recombination products of the initiator when azo initiators are used, to levels of <25 ppm of acrylonitrile, <50 ppm styrene, <50 ppm chain regulator and <280 ppm of recombination products by stripping using packed columns.
1. A process for the purification of a polymer polyol, comprising:
A) removing volatile constituents by means of superheated steam using packed columns, from the polymer polyol; and
B) freeing the purified polymer polyol obtained in step A), if necessary, from water that is still contained therein by passing through a packed column,
wherein in step A) a liquid distributor with a droplet site density of more than 400 droplet sites per m 2 of column cross-section feeds the polymer polyol, and the temperature of the process is less than or equal to 160° C.
2. The process according to claim 1 , wherein the columns further include packings having a strip-shaped lamellar structure and a specific surface of about 230 to about 450 m 2 /m 3 .
3. The process according to claim 1 , wherein liquid loading with reference to the column cross-section is from about 0.5 to about 3 m 3 /m 2 hour in stage A) and optionally B).
4. The process according to claim 1 , wherein the stripping agent stream is about 10 to about 20% referred to the PMPO mass flow stream in step A) and optionally B).
5. The process according to claim 1 , wherein polymer polyols purified by the process have a residual water content of ≦500 ppm.
6. The process according to claim 1 , wherein polymer polyols purified by the process have contents of acrylonitrile of ≦25 ppm, styrene of ≦50 ppm, optionally employed chain regulator of ≦50 ppm, and recombination product of the free-radical azo initiators, of ≦280 ppm.
7. The process according to claim 1 , wherein basic polymer polyols are produced by dissolving or dispersing free-radically polymerizable monomers in a base polyol and then polymerizing these monomers by means of free-radical initiators so that a stable dispersion of polymer particles in the base polyol is formed.
8. The process according to claim 7 , wherein the base polyol is a polyether polyol.
9. The process according to claim 7 ,wherein the free-radically polymerizable monomers are selected from the group consisting of styrene and acrylonitrile.
10. The process according to claim 7 , wherein the free-radical starters are selected from the group consisting of azo initiators and organic peroxides.