Hydrophobicizing water-redispersible polymer powder
View Patent ↗A water redispersible polymer powder with superior hydrophobicizing properties is a copolymer of vinyl acetate, a vinyl ester of an α-branched monocarboxylic acid, an alkyl(meth)acrylate, and a vinyl ester of a long chain unbranched monocarboxylic acid. The polymer is particularly useful as a hydrophobicizing agent for mineral-based chemical building products such as renders, mortars, etc.
1. A hydrophobicizing, water-redispersible polymer powder comprising:
a) a polymer prepared from monomers comprising
a1) from 50 to 90 parts by weight of vinyl acetate monomer units,
a2) from 5 to 50 parts by weight of vinyl ester monomer units derived from vinyl esters of alpha-branched monocarboxylic acids having up to 20 carbon atoms inclusive,
a3) from 1 to 30 parts by weight of (meth)acrylic ester monomer units derived from alcohols having from 1 to 15 carbon atoms,
a4) from 1 to 40 parts by weight of vinyl ester monomer units derived from long-chain unbranched monocarboxylic acids having from 10 to 20 carbon atoms,
a5) from 0 to 20 parts by weight of ethylene units,
a6) optionally, up to 10 parts by weight of auxiliary monomer units, wherein the parts by weight of monomeric units a1) through a6) of polymer a) add up to 100 parts by weight,
b) from 0.5 to 30% by weight of one or more, water-soluble protective colloids,
c) from 0 to 20% by weight of organosilicon compound(s),
d) from 0 to 20% by weight of fatty acid(s) or derivatives thereof, and
e) from 0 to 30% by weight of antiblocking agent, where the % by weight data are based on the total weight of the polymer a).
2. The hydrophobicizing, water-redispersible polymer powder composition of claim 1 comprising from 20 to 40 parts by weight of vinyl ester monomer units a2) derived from vinyl esters of alpha-branched monocarboxylic acids having from 9 to 15 carbon atoms.
3. The hydrophobicizing, water-redispersible polymer powder composition of claim 2 comprising from 1 to 10 parts by weight of acrylic ester monomer units a3) derived from acrylic esters of unbranched or branched alcohols having from 1 to 15 carbon atoms.
4. The hydrophobicizing, water-redispersible polymer powder composition of claim 3 , comprising from 5 to 20 parts by weight of ethylene monomer units.
5. The hydrophobicizing, water-redispersible polymer powder composition of claim 2 , comprising from 5 to 20 parts by weight of ethylene monomer units.
6. The hydrophobicizing, water-redispersible polymer powder composition of claim 1 comprising from 1 to 10 parts by weight of acrylic ester monomer units a3) derived from acrylic esters of unbranched or branched alcohols having from 1 to 15 carbon atoms.
7. The hydrophobicizing, water-redispersible polymer powder composition of claim 1 , comprising from 5 to 20 parts by weight of ethylene monomer units.
8. The hydrophobicizing, water-redispersible polymer powder composition of claim 1 wherein a polymer a) comprises a1) from 50 to 70 parts by weight of vinyl acetate monomer units, a2) from 20 to 40 parts by weight of monomer units derived from vinyl esters of alpha-branched monocarboxylic acids having from 9 to 15 carbon atoms, a3) from 1 to 10 parts by weight of monomer units derived from acrylic esters of unbranched or branched alcohols having from 1 to 8 carbon atoms, and a4) from 1 to 10 parts by weight of vinyl ester monomer units derived from long-chain, unbranched monocarboxylic acids having from 10 to 20 carbon atoms.
9. The hydrophobicizing, water-redispersible polymer powder composition of claim 1 , comprising partially hydrolyzed or fully hydrolyzed, optionally hydrophobically modified polyvinyl alcohols having a degree of hydrolysis of from 80 to 100 mol % (determined in accordance with DIN 53401) and a Hoppler viscosity in 4% strength aqueous solution of from 1 to 30 mPas (Hoppler method at 20°C., DIN 53015) as a protective colloid b).
10. The hydrophobicizing, water-redispersible polymer powder composition of claim 1 , comprising from 0.1 to 20% by weight, based on the polymer a), of one or more organosilicon compounds c) selected from the group consisting of silicic esters, silanes, polysilanes, organosilanols, disiloxanes, oligosiloxanes, polysiloxanes, carbosilanes, polycarbosilanes, carbosiloxanes, polycarbosiloxanes, and polysilylenedisiloxanes.
11. The hydrophobicizing, water-redispersible polymer powder composition of claim 1 , comprising from 0.1 to 20% by weight, based on the polymer a), of one or more compounds d) selected from the group consisting of fatty acids having from 8 to 22 carbon atoms, their metal soaps, their amides, and their esters with monohydric alcohols having from 1 to 14 carbon atoms, with glycol, with polyglycol, with polyalkylene glycol, with glycerol, with monoethanolamine, diethanolamine and triethanolamine, and with monosaccharides.
12. A process for producing hydrophobicizing, water-redispersible polymer powder compositions of claim 1 , comprising polymerizing by free-radically initiated emulsion polymerization in an aqueous medium and subsequently drying the resulting aqueous polymer dispersion.
13. The polymer powder of claim 1 , wherein component (c) is not present.
14. The polymer powder of claim 1 , wherein component (d) is not present.
15. The polymer powder of claim 1 , wherein neither component (c) nor component (d) are present.
16. The polymer powder of claim 1 , wherein no component a5) is present.
17. A chemical building product comprising at least one polymer of claim 1 , and at least one hydraulically settable inorganic binder selected from the group consisting of cement, water, glass, gypsum, and lime.
18. The product of claim 17 which is a building adhesive, render, knifing filler, flooring screed, self-leveling composition, sealing slurry, jointing mortar, or paint.
19. The composition of claim 17 , further comprising portland cement.
20. The composition of claim 19 , further comprising calcium carbonate.
21. A hydrophobicizing, water-redispersible polymer powder consisting essentially of:
a) a polymer prepared from monomers comprising
a1) from 50 to 90 parts by weight of vinyl acetate monomer units,
a2) from 5 to 50 parts by weight of vinyl ester monomer units derived from vinyl esters of alpha-branched monocarboxylic acids having up to 20 carbon atoms inclusive,
a3) from 1 to 30 parts by weight of (meth)acrylic ester monomer units derived from alcohols having from 1 to 15 carbon atoms,
a4) from 1 to 40 parts by weight of vinyl ester monomer units derived from long-chain unbranched monocarboxylic acids having from 10 to 20 carbon atoms,
a5) from 0 to 20 parts by weight of ethylene units,
a6) optimally, auxiliary monomer units, wherein the parts by weight add up to 100 parts by weight,
b) from 0.5 to 30% by weight of one or more, water-soluble protective colloids,
c) from 0 to 20% by weight of organosilicon compound(s),
d) from 0 to 20% by weight of fatty acid(s) or derivatives thereof, and
e) from 0 to 30% by weight of antiblocking agent, where the % by weight data are based on the total weight of the polymer a).
22. A hydrophobicizing, water-redispersible polymer powder consisting of:
a) a polymer prepared from monomers comprising
a1) from 50 to 90 parts by weight of vinyl acetate monomer units,
a2) from 5 to 50 parts by weight of vinyl ester monomer units derived from vinyl esters of alpha-branched monocarboxylic acids having up to 20 carbon atoms inclusive,
a3) from 1 to 30 parts by weight of (meth)acrylic ester monomer units derived from alcohols having from 1 to 15 carbon atoms,
a4) from 1 to 40 parts by weight of vinyl ester monomer units derived from long-chain unbranched monocarboxylic acids having from 10 to 20 carbon atoms,
a5) from 0 to 20 parts by weight of ethylene units,
a6) optimally, auxiliary monomer units, wherein the parts by weight add up to 100 parts by weight,
b) from 0.5 to 30% by weight of one or more, water-soluble protective colloids,
c) from 0 to 20% by weight of organosilicon compound(s),
d) from 0 to 20% by weight of fatty acid(s) or derivatives thereof, and
e) from 0 to 30% by weight of antiblocking agent, where the % by weight data are based on the total weight of the polymer a).