Gas-barrier laminate
View Patent ↗A gas-barrier laminate with a plastic substrate, an inorganic thin film formed on at least one surface of the plastic substrate, and a coating layer formed by applying a coating material on a surface of the inorganic thin film, wherein said coating layer contains a polyester-based resin having a molecular weight of 3000 to 15000 and a polyurethane-based resin having a molecular weight of 8000 to 30000 at a weight ratio of 5/95 to 95/5, and said gas-barrier laminate has an oxygen permeability of not more than 25 fmol/m 2 /s/Pa; and a gas-barrier laminate comprising a plastic substrate, an inorganic thin film formed on at least one surface of the plastic substrate, and a coating layer formed by applying a coating material on a surface of the inorganic thin film, wherein the gas-barrier laminate exhibits an oxygen permeability of not more than 50 fmol/m 2 /s/Pa as measured with respect to a gas-barrier film obtained by laminating an unstretched polypropylene film having a thickness of 60 μm on the coating layer of the gas-barrier laminate after subjecting the gas-barrier film to hydrothermal treatment at 120° C. for 30 min, and the coating layer has either a hardness of 0.1 to 0.5 GPa as measured at 23° C. in atmospheric air by a nano-indentation hardness testing method, a hardness of 0.03 to 0.5 GPa as measured at 23° C. in water by a nano-indentation hardness testing method, or a ratio of number of carbon atoms derived from carboxyl groups to number of carbon atoms constituting the surface of the coating layer of 0.005 to 0.1.
1. A gas-barrier laminate, comprising:
a plastic substrate;
an inorganic thin film formed on at least one surface of the plastic substrate; and
a coating layer on a surface of the inorganic thin film;
wherein
the coating layer comprises:
a polyester resin having a molecular weight of 3000 to 15000, and
a polyurethane resin having a molecular weight of 8000 to 3000,
a weight ratio of the polyester resin to the polyurethane resin is from 5/95 to 95/5, and
an oxygen permeability of the gas-barrier laminate is not more than 25 fmol/m 2 /s/Pa.
2. The gas-barrier laminate according to claim 1 , wherein the polyester-based resin and the polyurethane-based resin respectively have a glass transition temperature of 55 to 100° C. and an acid value of 1 to 100 mg KOH/g.
3. The gas-barrier laminate according to claim 1 , wherein the coating layer contains a silane coupling agent in an amount of 0.1 to 20% by weight.
4. The gas-barrier laminate according to claim 3 , wherein the silane coupling agent is an epoxy group-containing silane coupling agent, an amino group-containing silane coupling agent or a mixture thereof.
5. The gas-barrier laminate according to claim 1 , wherein the coating material contains a fatty acid, a fatty ester, a fatty amide or a mixture thereof in an amount of 0.05 to 20 parts by weight based on 100 parts by weight of a sum of the polyester-based resin and the polyurethane-based resin.
6. The gas-barrier laminate according to claim 1 , wherein the coating material contains a polyisocyanate as a curing agent and a content of the polyisocyanate in the coating material is 0.8 to 1.5 times a total hydroxyl equivalent of the polyester-based resin and the polyurethane-based resin.
7. The gas-barrier laminate according to claim 6 , wherein the polyisocyanate contains at least one compound having three or more active isocyanate groups in a molecule thereof.
8. The gas-barrier laminate according to claim 1 , wherein the plastic substrate comprises a polyester resin, a polyamide resin, a polyolefin resin, an ethylene-vinyl alcohol copolymer resin or a biodegradable resin.
9. The gas-barrier laminate according to claim 1 , wherein the inorganic thin film is a physically vapor-deposited film or a chemically vapor-deposited film comprising silicon oxide, aluminum oxide, diamond-like carbon or a mixture thereof.
10. The gas-barrier laminate according to claim 1 , further comprising an anchor coat layer disposed between the plastic substrate and the inorganic thin film.
11. The gas-barrier laminate according to claim 10 , wherein the anchor coat layer comprises at least one resin selected from the group consisting of a polyester resin, an urethane resin, an acrylic resin, an alkoxysilyl group-containing resin, an oxazoline group-containing resin and copolymer resins thereof.
12. The gas-barrier laminate according to claim 1 , further comprising a printed layer on a surface of the coating layer, and a heat seal layer on a surface of the printed layer.
13. The gas-barrier laminate according to claim 12 , further comprising at least one paper or plastic substrate disposed between the printed layer and the heat seal layer.
14. The gas-barrier laminate according to claim 13 , wherein the plastic substrate between the printed layer and the heat seal layer comprises a polyester-based resin, a polyamide-based resin, an ethylene-vinyl acetate copolymer resin or a mixture thereof.
15. The gas-barrier laminate according to claim 12 , wherein when the gas-barrier laminate is subjected to hydrothermal treatment under pressure at 120° C. for 30 min, an adhesion strength between the inorganic thin film and the coating layer is not less than 100 g/15 mm, and an adhesion strength between the coating layer and the printed layer is not less than 100 g/15 mm.
16. The gas-barrier laminate according to claim 1 , wherein the gas-barrier laminate is heat-treated at a temperature of not less than 60° C.
17. The gas-barrier laminate according to claim 1 , wherein when the gas-barrier laminate is subjected to hydrothermal treatment under pressure at 120° C. for 30 min, an oxygen permeability of the gas-barrier laminate after being subjected to the hydrothermal treatment is not more than 25 fmol/m 2 /s/Pa.
18. The gas-barrier laminate according to claim 1 , wherein when the gas-barrier laminate is further laminated on coating layer with an unstretched polypropylene film having a thickness of 60 μm and the further obtained laminate subjected to a hydrothermal treatment at 120° C. for 30 min, an oxygen permeability of further laminate is not more than 50 fmol/m 2 /s/Pa.
19. The gas-barrier laminate according to claim 18 , wherein a hardness of the coating layer is from 0.1 to 0.5 GPa as measured at 23° C. in atmospheric air by a nano-indentation hardness testing method.
20. The gas-barrier laminate according to claim 18 , wherein a hardness of the coating layer is from 0.03 to 0.5 GPa as measured at 23° C. in water by a nano-indentation hardness testing method.
21. The gas-barrier laminate according to claim 18 , wherein a ratio of number of carbon atoms derived from carboxyl groups to number of carbon atoms constituting the surface of the coating layer is from 0.005 to 0.1.