Iron-based brazing foil and method for brazing
View Patent ↗Disclosed are amorphous, ductile brazing foils with a composition consisting essentially of Fe Rest Ni a Cr b Si c B d P e , wherein 0 atomic %≦a<25 atomic %; 0 atomic %≦b≦15 atomic %; 1 atomic %≦c≦10 atomic %; 4 atomic %≦d≦15 atomic %; 1 atomic %≦e≦9 atomic %; any impurities≦0.5 atomic %; rest Fe, wherein 2 atomic %≦c+e≦10 atomic % and 15 atomic %≦c+d+e≦22 atomic %, or consisting essentially of Fe Rest Ni a Cr b Mo f Cu g Si c B d P e , wherein 0 atomic %≦a<25 atomic %; 0 atomic %≦b≦15 atomic %; 1 atomic %<c≦10 atomic %; 4 atomic %≦d≦15 atomic %; 1 atomic %≦e≦9 atomic %; 0 atomic %<f≦3 atomic %; 0 atomic %≦g≦3 atomic %; any impurities≦0.5 atomic %; rest Fe, wherein 2 atomic %≦c+e≦10 atomic % and 15 atomic %≦c+d+e≦22 atomic %. Also disclosed are brazed objects formed using these foils, particularly exhaust gas recirculation coolers and oil coolers, and methods for making the brazing foils and for making the brazed parts.
1. An amorphous, ductile brazing foil having a composition consisting essentially of
Fe Rest Ni a Cr b Mo f Cu g Si c B d P e ,
wherein 0 atomic %≦a<25 atomic %; 0 atomic %≦b≦15 atomic %; 1 atomic %<c≦10 atomic %; 4 atomic %≦d≦15 atomic %; 1 atomic %≦e≦9 atomic %; 0 atomic %<f≦3 atomic %; 0 atomic %≦g≦3 atomic %; any impurities≦0.5 atomic %; rest Fe, wherein 2 atomic %≦c+e≦10 atomic % and 15 atomic %≦c+d+e≦22 atomic %.
2. The amorphous, ductile brazing foil according to claim 1 , wherein the content of Ni, a, is such that 5 atomic %≦a<25 atomic %.
3. The amorphous, ductile brazing foil according to claim 1 , wherein the content of Ni, a, is 0 atomic %.
4. The amorphous, ductile brazing foil according to claim 1 , wherein the content of Cr, b, is such that 2 atomic %≦b≦15 atomic %.
5. The amorphous, ductile brazing foil according to claim 1 , wherein the brazing foil is at least 50% amorphous.
6. The amorphous, ductile brazing foil according to claim 5 , wherein the brazing foil is at least 80% amorphous.
7. The amorphous, ductile brazing foil according to claim 1 , having a thickness D of at least 25 μm.
8. The amorphous, ductile brazing foil according to claim 7 , wherein the thickness D is such that 25 μm≦D≦40 μm.
9. The amorphous, ductile brazing foil according to claim 1 , having a width B such that 20 mm≦B≦200 mm.
10. The amorphous, ductile brazing foil according to claim 9 , wherein the width B is such that 40 mm≦B≦200 mm.
11. The amorphous, ductile brazing foil according to claim 1 , having a liquidus temperature of less than 1180° C.
12. The amorphous, ductile brazing foil according to claim 11 , wherein the liquidus temperature is less than 1160° C.
13. The amorphous, ductile brazing foil according to claim 1 , wherein the molybdenum content, f, and the copper content, g, are such that 0.2≦f≦1.5 atomic % and 0.5≦g≦1.5 atomic %.
14. A brazed object comprising a first component and a second component, permanently joined by adhesive force to the first component by a brazing seam formed from the brazing foil according to claim 1 .
15. The brazed object according to claim 14 , wherein one or both of the first component and the second component comprise austenitic stainless steel, a nickel alloy, or a cobalt alloy.
16. The brazed object according to claim 14 , wherein the brazing seam has a thickness>20 μm.
17. The brazed object according to claim 14 , wherein the brazed object is an exhaust gas recirculation cooler or an oil cooler.