Glass for information recording medium substrate, glass substrate for information recording medium and magnetic disk
View Patent ↗A glass for an information recording medium substrate, which comprises, as represented by mol % based on the following oxides, from 61 to 72% of SiO 2 , from 3 to 11% of Al 2 O 3 , from 0 to 14.3% of Li 2 O, from 0 to 22% of Na 2 O, from 0 to 22% of K 2 O, from 4 to 13% of MgO, from 0 to 6% of TiO 2 and from 0 to 5% of ZrO 2 , provided that the total content of Li 2 O, Na 2 O and K 2 O (R 2 O) is from 10 to 22%, and (a) the ratio of the content of Li 2 O to R 2 O (Li 2 O/R 2 O) is at most 0.52, (b) the ratio of the content of Na 2 O to R 2 O (Na 2 O/R 2 O) is at least 0.35, or (c) the ratio of the content of K 2 O to R 2 O (K 2 O/R 2 O) is at least 0.45.
1. Glass for an information recording medium substrate, which comprises, as represented by mol % based on the following oxides, from 61 to 72% of SiO 2 , from 3 to 11% of Al 2 O 3 , from 0 to 14.3% of Li 2 O, from 0 to 22% of Na 2 O, from 0 to 22% of K 2 O, from 4 to 13% of MgO, from 0 to 6% of TiO 2 and from 0 to 5% of ZrO 2 ,
provided that the total content of Li 2 O, Na 2 O and K 2 O (R 2 O) is from 10 to 22%, and
(a) the ratio of the content of Li 2 O to R 2 O (Li 2 O/R 2 O) is at most 0.52, (b) the ratio of the content of Na 2 O to R 2 O (Na 2 O/R 2 O) is at least 0.35, or (c) the ratio of the content of K 2 O to R 2 O (K 2 O/R 2 O) is at least 0.45.
2. The glass for an information recording medium substrate according to claim 1 , wherein the ratio of Li 2 O/R 2 O is at most 0.5, or the ratio of Na 2 O/R 2 O is at least 0.4.
3. The glass for an information recording medium substrate according to claim 1 , which contains no B 2 O 3 or contains less than 1% of B 2 O 3 .
4. The glass for an information recording medium substrate according to claim 1 , wherein SiO 2 is from 62 to 71%, Al 2 O 3 is from 4 to 11% , Li 2 O is from 0 to 12.4%, Na 2 O is from 0 to 20%, K 2 O is from 0 to 19%, MgO is from 5 to 12%, TiO 2 is from 0 to 5%, ZrO 2 is from 0 to 4%, and R 2 O is from 11 to 20%.
5. The glass for an information recording medium substrate according to claim 1 , wherein SiO 2 is from 63 to 70% , Al 2 O 3 is from 5 to 9% , Li 2 O is from 0 to 10.2% , Na 2 O is from 0 to 19% , K 2 O is from 0 to 12.8% , MgO is from 5 to 11% , TiO 2 is from 0 to 4% , ZrO 2 is from 0 to 4% , and R 2 O is from 13 to 19%.
6. The glass for an information recording medium substrate according claim 1 , which contains neither CaO, SrO nor BaO.
7. The glass for an information recording medium substrate according to claim 1 , which contains at least one of CaO, SrO and BaO in the total content of at most 3%.
8. The glass for an information recording medium substrate according to claim 1 , wherein, Li 2 O is from 0 to less than 5% , Na 2 O is from 0 to 13% , K 2 O is from 0 to 12% , MgO is from 4 to 11% , R 2 O is from 10 to 17% , and CaO is up to 3%.
9. The glass for an information recording medium substrate according to claim 1 , wherein SiO 2 is from 61 to 71% , Al 2 O 3 is from 4 to 11% , Li 2 O is from 0 to 4.5% , Na 2 O is from 0 to 12% , K 2 O is from 0 to 10% , MgO is from 4 to 9% , and CaO is up to 3%.
10. The glass for an information recording medium substrate according to claim 8 , wherein ZrO 2 is from 0.5 to 3%.
11. The glass for an information recording medium substrate according to claim 1 , which has a Young's modulus of at least 76 GPa and a specific modulus of at least 28 MNm/kg.
12. The glass for an information recording medium substrate according to claim 1 , which has a glass transition temperature of at least 500° C.
13. The glass for an information recording medium substrate according to claim 8 , which has a Young's modulus of at least 76 GPa, a specific modulus of at least 30 MNm/kg and a glass transition temperature of at least 510° C.
14. The glass for an information recording medium substrate according to claim 1 , which has an average linear expansion coefficient of at least 56×10 −7 /° C. in a temperature range of from −50 to 70° C.
15. The glass for an information recording medium substrate according to claim 1 , wherein (T L −T 4 )<50° C. , where T L is the liquidus temperature, and T 4 is the temperature at which the viscosity becomes 10 4 dPa·s.
16. The glass for an information recording medium substrate according to claim 1 , which has a density of at most 2.60 g/cm 3 .
17. A glass substrate for an information recording medium, which is made of the glass for an information recording medium substrate as defined in claim 1 .
18. The glass substrate for an information recording medium according to claim 17 , wherein when immersed in 0.01 N nitric acid at 25° C. , the etching rate of glass is at most 0.2 nm/h.
19. The glass substrate for an information recording medium according to claim 17 , wherein when the glass is left under a steam atmosphere at 120° C. at 0.2 MPa for 20 hours, C R =C Li +C Na +C K is at most 12 nmol/cm 2 , where C Li , C Na and C K are the amounts of Li, Na and K which precipitate on a surface of the glass, respectively.
20. A magnetic disk having a magnetic recording layer formed on the glass substrate for an information recording medium as defined in claim 17 , 18 or 19 .