Method for hardening running surfaces of roller bearing components
View Patent ↗A method for hardening running surfaces of roller bearing components, in particular outer bearing rings. In order to provide the edge area (functional layer) of the roller bearing components with a deep layer which is particularly hard and resistant to corrosion, the roller bearing component undergoes nitration for a long period of time at a temperature of between 450 and 650° C. for at least 25 hours. During treatment no carburizing and subsequently no quenching takes place.
1. A method for hardening running surfaces of a rolling bearing component made of ease hardened steel, comprising:
plasma nitriding the rolling bearing component made of case hardened steel at a temperature of between 450° C. and 650° C. for a period of time of at least 50 hours and at most 100 hours and generating a hardened functional layer with stress profile starting at greater than 400MPa and is not transformed into an approximately stress free range until a thickness of greater than 0.15 mm,
wherein no carburizing takes place during the nitriding and no quenching subsequently takes place.
2. The method as claimed in claim 1 , wherein the rolling bearing component is subjected to cleaning of a surface to be hardened before the nitriding.
3. The method as claimed in claim 2 , wherein the cleaning is carried out by a surface bombardment with an inert gas at a pressure which is reduced relative to atmosphere.
4. The method as claimed in claim 3 , wherein the cleaning is carried out in an over into which noble gas is initially introduced and a nitriding process gas is subsequently introduced.
5. The method as claimed in claim 1 , wherein the running surfaces to be hardened are carburized before the nitriding.
6. The method as claimed in claim 5 , wherein the roiling bearing component is processed to size before the nitriding.
7. The method of claim 1 , wherein the plasma nitriding is conducted at a temperature between 500° C. and 650° C.
8. The method of claim 1 , wherein the plasma nitriding is conducted for a period of time greater than 60 hours and at most 100 hours.