Initiator or linker free functionalization of polyethylene resin with antimicrobial property and methods of fabrication thereof
The present invention generally relates to a thermoplastic resin which is functionalized by an initiator- or linker-free process and imparted with functional properties, and related methods of fabrication. In particular, the present invention relates to methods of covalently modifying the thermoplastic resin using plasma before or after being introduced with an active agent having said functional properties.
1. A linker-free or initiator-free method for fabricating a functionalized thermoplastic resin being covalently bound with a bacteria repellent agent, said method comprising plasma treating the thermoplastic resin before or after mixing with said bacteria repellent agent, and preserving functional groups introduced by said plasma into the backbone of said thermoplastic resin, in order to obtain a covalently grafted conjugate of plasma-treated thermoplastic resin with said bacteria repellent agent.
2. The method of claim 1 , wherein said thermoplastic resin comprises polyethylene (PE) resin.
3. The method of claim 1 , wherein said thermoplastic resin comprises low-density PE (LDPE), linear low-density PE (LLDPE), high-density PE (HDPE), and other polyethylene-based resins.
4. The method of claim 1 , wherein said bacteria repellent agents comprise polyethylene glycol sorbitan monolaurate, polyethylene glycol sorbitan monooleate, poly(ethylene glycol) sorbitol hexaoleate, polyethene-block-poly(ethylene glycol), and alkyl polyglycol ether C16-C18.
5. The method of claim 1 , wherein said bacteria repellent agent comprises polyethylene glycol sorbitan monolaurate which also introduces functional groups into the backbone of the thermoplastic resin under said plasma treatment.
6. The method of claim 1 , wherein said bacteria repellent agent contains reactive groups corresponding to the functional groups introduced by said plasma.
7. The method of claim 1 , wherein said preserving is via vacuum packaging, or dry mixing of said thermoplastic resin with said bacteria repellent agent which contains reactive groups corresponding to the functional groups introduced by said plasma, or both of said vacuum packaging and said dry mixing.
8. The method of claim 7 , wherein said vacuum packaging is carried out in a low oxygen environment and in a sealable container when the thermoplastic resin is mixed with said bacteria repellent agent.
9. The method of claim 8 , wherein said low oxygen environment is established by depressurization in a reaction chamber of a plasma machine, followed by injecting suitable amount of oxygen into the reaction chamber at a regulated pressure, then applying suitable voltage to generate plasma, and after plasma treatment for certain period of time, the remaining oxygen is vented out from the reaction chamber.
10. The method of claim 9 , wherein said thermoplastic resin is transferred to a meshed drum with a rotating speed of 50 Hz, followed by establishing said low oxygen environment, then plasma treating said thermoplastic resin, and mixing plasma-treated thermoplastic resin with said bacteria repellent agent under said low oxygen environment by vigorous shaking and rotating driven by said drum.
11. The method of claim 2 , wherein said bacteria repellent agent is polyethylene glycol sorbitan monolaurate, wherein the concentration of polyethylene glycol sorbitan monolaurate is 1% (v/w).
12. The method of claim 11 , further comprising the step of processing the thermoplastic resin by extrusion after plasma treatment.