Thin-walled high temperature alloy structures via multi-material additive manufacturing

1. A method for forming a thin-walled structure, the method comprising:

forming a polymer template;

forming a plurality of coating layers, each of the coating layers being formed on the polymer template or on a previously formed layer, the forming of the plurality of coating layers comprising:

forming a first coating layer on the polymer template, the first coating layer comprising one or more chemical elements, including at least 1% by weight of a first metal chemical element, the first coating layer having a thickness of 1 micron or less;

forming a second coating layer on the first coating layer, the second coating layer comprising one or more chemical elements, including at least 1% by weight of a second metal chemical element, different from the first metal chemical element, wherein the forming of the second coating layer comprises co-depositing cobalt and rhenium utilizing electrodeposition;

removing the polymer template; and

performing a heat treatment of one or more of the plurality of coating layers, after removing the polymer template, the performing of the heat treatment comprising heating the plurality of coating layers to a first temperature and maintaining the plurality of coating layers at or above the first temperature during a first time interval, the first temperature and the first time interval being selected such that the chemical elements of the first coating layer and the chemical elements of the second coating layer interdiffuse to form a single continuous layer having a thickness less than 500 microns and comprising two different chemical elements, each chemical element of the single continuous layer having a molar concentration varying by less than 10% within the single continuous layer.

2. The method of claim 1 , wherein the removing of the polymer template is performed before the forming of the second coating layer.

3. The method of claim 1 , wherein the forming of the first coating layer comprises depositing the first coating layer utilizing a process selected from the group consisting of electrodeposition, electroless deposition, chemical vapor deposition, physical vapor deposition, spray coating, and combinations thereof.

4. The method of claim 3 , wherein the forming of the first coating layer comprises depositing a first sub-layer of titanium utilizing electron beam evaporation and, after depositing the first sublayer of titanium, depositing a second sub-layer of platinum utilizing electron beam evaporation.

5. The method of claim 4 , wherein the removing the polymer template comprises removing the polymer template with a polymer removal fluid, the method further comprising removing a portion of the first coating layer in an area sufficiently large to allow the polymer removal fluid to access the polymer template.

6. The method of claim 1 , wherein:

the removing of the polymer template is performed after the forming of the second coating layer, and

the forming of the plurality of coating layers further comprises forming a third coating layer comprising a third metal chemical element.

7. The method of claim 6 , wherein the forming of the third coating layer comprises depositing material utilizing a process selected from the group consisting of aluminum diffusion coating, chromium diffusion coating, titanium diffusion coating, cathodic arc deposition, direct current (DC) bias field cathodic arc physical vapor deposition, plasma enhanced magnetron sputtering, and pack cementation.

8. The method of claim 6 , wherein the forming of the third coating layer comprises depositing chromium or aluminum utilizing pack cementation.

9. The method of claim 1 , wherein the single continuous layer comprises:

a nominal composition consisting of the following nominal proportions:

70% by weight rhenium; and

30% by weight cobalt, or

a composition in which each component differs from its respective nominal proportion by +/−30% of its respective proportion.

10. The method of claim 9 , wherein the composition includes:

between 10% by weight and 30% by weight chromium and/or

between 3% by weight and 15% by weight aluminum.

11. The method of claim 1 , wherein the forming of the polymer template comprises utilizing an act selected from the group consisting of stereolithography, three dimensional printing, additive manufacturing and injection molding.

12. The method of claim 1 , wherein the removing of the polymer template comprises utilizing an act selected from the group consisting of a base etching, an acid etching, a plasma etching, a solvent bath processing, a thermal decomposition and a melting.

13. The method of claim 1 , wherein the first temperature is at least 1100° C. and the first time interval is at least 24 hours.

14. A method for forming a thin-walled structure, the method comprising:

forming a polymer template;

forming a plurality of coating layers, each of the coating layers being formed on the polymer template or on a previously formed layer, the forming of the plurality of coating layers comprising:

forming a first coating layer on the polymer template, the first coating layer comprising one or more chemical elements, including at least 1% by weight of a first metal chemical element;

forming a second coating layer on the first coating layer, the second coating layer comprising one or more chemical elements, including at least 1% by weight of a second metal chemical element, different from the first metal chemical element;

removing the polymer template; and

performing a heat treatment of one or more of the plurality of coating layers, after removing the polymer template, the performing of the heat treatment comprising heating the plurality of coating layers to a first temperature and maintaining the plurality of coating layers at or above the first temperature during a first time interval, the first temperature and the first time interval being selected such that the chemical elements of the first coating layer and the chemical elements of the second coating layer interdiffuse to form a single continuous layer having a thickness less than 500 microns and comprising two different chemical elements, each chemical element of the single continuous layer having a molar concentration varying by less than 10% within the single continuous layer,

wherein the single continuous layer comprises:

a nominal composition consisting of the following nominal proportions:

73% by weight nickel;

19% by weight chromium;

7% by weight aluminum; and

1% by weight titanium, or

a composition in which each of nickel, chromium, aluminum, and titanium differs from its respective nominal proportion by +/−20% of its respective proportion.

15. A method for forming a thin-walled structure, the method comprising:

forming a polymer template;

forming a plurality of coating layers, each of the coating layers being formed on the polymer template or on a previously formed layer, the forming of the plurality of coating layers comprising:

forming a first coating layer on the polymer template, the first coating layer comprising at least 1% by weight of a first metal chemical element;

forming a second coating layer on the first coating layer, the second coating layer comprising at least 1% by weight of a second metal chemical element, different from the first metal chemical element;

removing the polymer template; and

performing a heat treatment of one or more of the plurality of coating layers, after removing the polymer template, the performing of the heat treatment comprising heating the plurality of coating layers to a first temperature and maintaining the plurality of coating layers at or above the first temperature during a first time interval, the first temperature and the first time interval being selected such that the chemical elements of the first coating layer and the chemical elements of the second coating layer interdiffuse to form a single continuous layer having a thickness less than 500 microns and comprising two different chemical elements, each chemical element of the single continuous layer having a molar concentration varying by less than 10% within the single continuous layer,

wherein the first coating layer has a thickness of between 5 microns and 300 microns, and comprises, as a major component, a substance selected from the group consisting of nickel, cobalt, iron, and combinations thereof, and

wherein the forming of the second coating layer comprises:

depositing one or more sub-layers of chromium, to a combined thickness of 10% to 40% of the thickness of the first coating layer, utilizing an act selected from the group consisting of electroplating, chemical vapor deposition and pack cementation;

depositing one or more sub-layers of aluminum, to a combined thickness of 10% to 40% of the thickness of the first coating layer, utilizing an act selected from the group consisting of electroplating, chemical vapor deposition and pack cementation;

depositing, to a thickness of 1% to 15% of the thickness of the first coating layer, a layer comprising, as a major component, a substance selected from the group consisting of Mo, W, Ta, Ti, and Re, and combinations thereof; and

depositing, to a thickness of less than 2% of the thickness of the first coating layer, a layer comprising, as a major component, a substance selected from the group consisting of Si, C, B, Zr, Hf, Y, and combinations thereof.

16. A method for forming a thin-walled structure, the method comprising:

forming a polymer template;

forming a plurality of coating layers, each of the coating layers being formed on the polymer template or on a previously formed layer, the forming of the plurality of coating layers comprising:

forming a first coating layer on the polymer template, the first coating layer comprising one or more chemical elements, including at least 1% by weight of a first metal chemical element;

forming a second coating layer on the first coating layer, the second coating layer comprising one or more chemical elements, including at least 1% by weight of a second metal chemical element, different from the first metal chemical element;

removing the polymer template; and

performing a heat treatment of one or more of the plurality of coating layers, after removing the polymer template, the performing of the heat treatment comprising heating the plurality of coating layers to a first temperature and maintaining the plurality of coating layers at or above the first temperature during a first time interval, the first temperature and the first time interval being selected such that the chemical elements of the first coating layer and the chemical elements of the second coating layer interdiffuse to form a single continuous layer having a thickness less than 500 microns and comprising two different chemical elements, each chemical element of the single continuous layer having a molar concentration varying by less than 10% within the single continuous layer,

wherein:

the first coating layer comprises, as a major component, a combination of:

cobalt; and

rhenium in a concentration of 10% by weight to 70% by weight;

and the second coating layer comprises, as a major component, a substance selected from the group consisting of chromium, nickel, aluminum, tantalum, silicon, and combinations thereof.