Mortar for eco-masonry element
A mortar for formation of a masonry element includes a co-product from the production of steel and an alkaline solution. A masonry element is formed from the mortar, the masonry element including at least one of a brick, a block, a paver, veneer stone, exterior or interior wall panels, roof tiles, faux slate, faux wood, decorative stone, and a poured structure. A method of forming a masonry element includes providing the mortar and compressing the mortar to form the masonry element.
1. A mortar for formation of a masonry element, comprising:
a co-product from the production of steel, wherein the co-product comprises pickle liquor sludge; and
an alkaline solution.
2. The mortar of claim 1 , further comprising an aggregate material.
3. The mortar of claim 1 , wherein the mortar further comprises at least one calcium source.
4. The mortar of claim 1 , wherein the mortar further comprises at least one aluminosilicate source.
5. The mortar of claim 1 , wherein the mortar further comprises a slag including calcium and/or aluminosilicate sources.
6. The mortar of claim 3 , wherein the calcium source comprises lime and/or dolomite.
7. The mortar of claim 5 , wherein the slag comprises from 35 to 55 wt % of the calcium source and/or from 15 to 35 wt % of silica.
8. The mortar of claim 3 , wherein the calcium source is in the form of a powder having an average particle size in the range of 10 to 80 μm.
9. The mortar of claim 1 , wherein the pickle liquor sludge comprises a product from a pickling bath used in the production of steel.
10. The mortar of claim 9 , wherein the pickling bath comprises at least one of sulfuric acid, hydrochloric acid, and nitric acid, wherein the pickling bath further comprises lime, wherein the steel is immersed in the pickling bath to clean residues from the steel.
11. The mortar of claim 1 , wherein the alkaline solution comprises at least of an alkali hydroxide and an alkali silicate.
12. The mortar of claim 1 , wherein the alkaline solution comprises from 2 to 30 wt % of the total weight of the mortar.
13. The mortar of claim 5 , wherein the calcium and/or aluminosilicate source comprises from 40 to 65 wt % of the total weight of the mortar.
14. The mortar of claim 5 , wherein the mortar comprises the slag and the pickle liquor sludge, wherein the pickle liquor sludge comprises from 5 to 20 wt % of the total weight of the mortar.
15. The mortar of claim 2 , wherein the aggregate material comprises at least one of sand, glass, granite, stone, and steel.
16. The mortar of claim 2 , wherein the mortar comprises up to 75 wt % of the aggregate material, wherein the aggregate material has an average particle size from mesh No. 8 to mesh No. 50.
17. The mortar of claim 1 , wherein the mortar comprises a wet cast mortar or a dry cast mortar.
18. A masonry element formed from the mortar of claim 1 , wherein the masonry element comprises at least one of a brick, a block, a paver, veneer stone, exterior or interior wall panels, roof tiles, faux slate, faux wood, decorative stone, and a poured structure.
19. A method of forming a masonry element, comprising:
mixing a co-product from the production of steel and an alkaline solution to form a mortar, wherein the co-product comprises pickle liquor sludge; and
forming a masonry element from the mortar.
20. The method of claim 19 , further comprising mixing the co-product and the alkaline solution with at least one of a calcium source, an aluminosilicate source, and an aggregate material to form the mortar.