Environmentally safe concrete or mortar etching composition and methods thereof
View Patent ↗Disclosed herein is an environmentally safe etching composition and method for a concrete or mortar surface. The composition includes, in some embodiments, an aqueous solution of urea, acetic acid, a buffering agent, an anticorrosive agent, and a surfactant with no more than about 30% (w/v) urea and at least about 10% (v/v) acetic acid. The method includes, in some embodiments, obtaining the etching composition; applying the etching composition to the concrete or mortar surface at a prescribed ratio of the etching composition to the concrete or mortar surface; allowing the etching composition to stand on the concrete or mortar surface for a prescribed amount of time; and washing the concrete or mortar surface with water to produce an etched surface of the concrete or mortar.
1. An environmentally safe etching composition for a concrete or mortar surface, comprising:
urea at no more than about 30% (w/v) urea;
acetic acid at greater than about 10% (v/v) acetic acid;
a buffering agent; and
an agent for removing residual lipophilic contamination from the concrete or mortar surface;
wherein the etching composition is an acidic aqueous solution in which the greater the concentration of the acetic acid, the coarser the etching of the concrete or the mortar surface over a prescribed amount of time.
2. The etching composition of claim 1 , wherein the buffering agent is sodium borate at no more than about 20% (w/v) sodium borate.
3. The etching composition of claim 1 , wherein pine oil is the agent for removing the residual lipophilic contamination from the concrete or mortar surface.
4. The etching composition of claim 3 , further comprising:
a fragrance in an amount sufficient to provide the etching composition a pleasant or agreeable scent over the acetic acid.
5. The etching composition of claim 4 , wherein the fragrance is the pine oil at no more than about 0.5% (v/v) pine oil.
6. The etching composition of claim 3 , wherein the agent for removing the residual lipophilic contamination from the concrete or mortar surface further includes a surfactant that functions as both a wetting agent and a detergent at no more than about 1% (w/v) surfactant.
7. The etching composition of claim 6 , wherein:
the etching composition includes at least about 10% (w/v) urea and no more than about 30% (v/v) acetic acid,
and
the etching composition produces a 100-grit etched surface when allowed to stand for the prescribed amount of time on the concrete or mortar surface at one gallon of the etching composition per 300 square feet of the concrete or mortar surface, the prescribed amount of time being about five minutes.
8. The etching composition of claim 7 , further comprising:
sodium borate as a buffering agent at no more than about 20% (w/v) sodium borate with the pine oil also as a fragrance at no more than about 0.5% (v/v) pine oil.
9. The etching composition of claim 6 , wherein the detergent is an ionic detergent.
10. The etching composition of claim 6 , wherein the detergent is a non-ionic detergent.
11. The etching composition of claim 1 , wherein:
the etching composition includes about 15% (w/v) urea, about 16% (v/v) acetic acid, about 15% (w/v) sodium borate as the buffering agent, and a surfactant at about 0.35% (w/v) surfactant,
the surfactant functions as both a wetting agent and a detergent, and
the etching composition produces a 220-grit etched surface when allowed to stand for the prescribed amount of time on the concrete or mortar surface at one gallon of the etching composition per 300 square feet of the concrete or mortar surface, the prescribed amount of time being about five minutes.
12. The etching composition of claim 1 , further comprising:
a fragrance in an amount sufficient to provide the etching composition a pleasant or agreeable scent over the acetic acid; and
a surfactant,
wherein the fragrance is pine oil, the surfactant functions as a detergent, and both the pine oil and the detergent function as the agent for removing the residual lipophilic contamination from the concrete or mortar surface.
13. The etching composition of claim 12 , wherein the pine oil is at no more than about 0.5% (v/v) pine oil and the surfactant is at no more than about 1% (w/v) surfactant.
14. The etching composition of claim 13 , wherein the etching composition includes at least about 10% (w/v) urea, no more than about 30% (v/v) acetic acid, and no more than about 20% (w/v) sodium borate as the buffering agent, the etching composition producing a 100-grit etched surface when allowed to stand for the prescribed amount of time on the concrete or mortar surface at one gallon of the etching composition per 300 square feet of the concrete or mortar surface, the prescribed amount of time being about five minutes.
15. The etching composition of claim 13 , wherein the etching composition includes about 15% (w/v) urea, about 16% (v/v) acetic acid, about 15% (w/v) sodium borate as the buffering agent, and about 0.35% (w/v) surfactant, the etching composition producing a 220-grit etched surface when allowed to stand for the prescribed amount of time on the concrete or mortar surface at one gallon of the etching composition per 300 square feet of the concrete or mortar surface, the prescribed amount of time being about five minutes.