Polymer composition with improved paint adhesion

1. A polypropylene composition (C) comprising:

(a) 50 to 90 parts per weight of a heterophasic propylene copolymer (HECO);

(b) 2 to 25 parts per weight of a plastomer (PL); and

(c) 8 to 25 parts per weight of an inorganic filler (F);

based on the total parts per weight of (a), (b) and (c);

wherein the polypropylene composition (C) has an amount of xylene cold soluble (XCS) fraction of at least 22 wt.-%, based on the weight of the polypropylene composition (C); and

wherein the intrinsic viscosity (IV) of the xylene cold soluble (XCS) fraction of the polypropylene composition (C) is not more than 3.4 dl/g,

wherein the heterophasic propylene copolymer (HECO) comprises

(a) 5 to 49 parts per weight of a first heterophasic propylene copolymer (HECO1) and

(b) 51 to 95 parts per weight of a second heterophasic propylene copolymer (HECO2),

based on the total parts per weight of the first heterophasic propylene copolymer (HECO1) and the second heterophasic propylene copolymer (HECO2); and

wherein the second heterophasic propylene copolymer (HECO2) and the first heterophasic propylene copolymer (HECO1) together fulfil in-equation (I):

MFR [HECO2]/MFR [HECO1]>1.0 (I);

wherein

MFR [HECO2] is a melt flow rate MFR 2 (230° C., 2.16 kg) measured according to ISO 1133 of the second heterophasic propylene copolymer (HECO2) and

MFR [HECO1] is a melt flow rate MFR 2 (230° C., 2.16 kg) measured according to ISO 1133 of the first heterophasic propylene copolymer (HECO1).

2. The polypropylene composition (C) according to claim 1 , wherein the polypropylene composition (C) has:

(a) a melt flow rate MFR 2 (230° C., 2.16 kg) measured according to ISO 1133 of at least 5 g/10 min;

and/or

(b) a tensile modulus measured according to ISO 527-2 of at least 800 MPa;

and/or

(c) a tensile elongation at break measured according to ISO 527-2 of not more than 70%;

and/or

(d) a Charpy Impact Strength (NIS+23) measured according to ISO 179- 1 eA:2000 at +23° C. of at least 10 kJ/m 2 .

3. The polypropylene composition (C) according to claim 1 , wherein

(a) a melt flow rate MFR 2 (230° C., 2.16 kg) measured according to ISO 1133 of the first heterophasic propylene copolymer (HECO1) is not more than 40 g/10 min;

and/or

(b) a melt flow rate MFR 2 (230° C., 2.16 kg) measured according to ISO 1133 of the second heterophasic propylene copolymer (HECO2) is at least 6 g/10 min.

4. The polypropylene composition (C) according to claim 1 , wherein

(a1) the first heterophasic propylene copolymer (HECO1) comprises a xylene cold soluble fraction in the range of 10 to 55 wt.-%, based on the weight of the first heterophasic propylene copolymer (HECO1);

(a2) the xylene cold soluble (XCS) fraction of the first heterophasic propylene copolymer (HECO1) comprises comonomer units derivable from C 2 and/or C 4 to C 12 α-olefin in an amount in the range of 30 to 65 mol %; and

(a3) the xylene cold soluble (XCS) fraction of the heterophasic propylene copolymer (HECO1) has an intrinsic viscosity (IV) of not more than 4.0 dl/g;

and/or

(b1) the second heterophasic propylene copolymer (HECO2) comprises a xylene cold soluble fraction in the range of 10 to 55 wt.-%, based on the weight of the second heterophasic propylene copolymer (HECO2);

(b2) the xylene cold soluble (XCS) fraction of the second heterophasic propylene copolymer (HECO2) comprises comonomer units derivable from C 2 and/or C 4 to C 12 α-olefin in an amount in the range of 30 to 65 mol %; and

(b3) the xylene cold soluble (XCS) fraction of the second heterophasic propylene copolymer (HECO2) has an intrinsic viscosity (IV) of not more than 3.5 dl/g.

5. The polypropylene composition (C) according to claim 1 , wherein the plastomer (PL) is an elastomeric ethylene copolymer (EC) comprising units derivable from ethylene and at least one C 4 to C 20 α-olefin.

6. The polypropylene composition (C) according to claim 1 , wherein the plastomer (PL) is an elastomeric ethylene copolymer (EC) consisting of units derivable from ethylene and 1-octene having

(a) a melt flow rate MFR (190° C.) measured according to ASTM D1238 in the range of 0.1 to 5.0 g/10 min;

and/or

(b) a density in the range of 830 to 890 kg/m 3 ;

and/or

(c) an ethylene content in the range of 70 to 99 mol %.

7. The polypropylene composition (C) according to claim 1 , wherein the inorganic filler (F) is a mineral filler.

8. The polypropylene composition (C) according to claim 7 , wherein the mineral filler is talc with a median particle size (D 50 ) of not more than 5.0 μm.

9. The polypropylene composition (C) according to claim 7 , wherein the the mineral filler is talc with a cut-off particle size (D 95 ) of not more than 8.0 μm.

10. The polypropylene composition (C) according to claim 1 , wherein the polypropylene composition (C) does not comprise other polymers besides the heterophasic propylene copolymer (HECO) and and the plastomer (PL) in an amount exceeding 2.5 wt.-%, based on the weight of the polypropylene composition (C).

11. The polypropylene composition (C) according to claim 1 , wherein the heterophasic propylene copolymer (HECO) and and the plastomer (PL) are the only polymers present in the the polypropylene composition (C).

12. An article comprising the polypropylene composition (C) according to claim 1 .

13. A method of enhancing paint adhesion of a moulded article, the method comprising utilizing a polypropylene composition (C) according to claim 1 in producing the moulded article.