Zeolite with reduced extra-framework aluminum
The present disclosure generally provides a catalyst composition comprising a zeolite containing iron and/or copper with a reduced amount of extra-framework aluminum. The catalyst composition is useful to catalyze the reduction of nitrogen oxides in exhaust gas in the presence of a reductant.
1. An SCR catalyst composition comprising:
a metal-containing molecular sieve comprising a zeolitic framework of silicon and aluminum atoms; and
extra-framework aluminum atoms that are present in an amount of about less than 15% based on the total integrated peak intensity determined by 27 Al NMR of aluminum species present in the zeolite as measured prior to addition of the metal;
wherein the zeolitic surface area of the catalyst composition ranges from 120 m 2 /g to 250 m 2 /g;
wherein the zeolitic framework is selected from AEI, AFT, AFV, AFX, AVL, CHA, DDR, EAB, EEI, ERI, IFY, IRN, KFI, LEV, LTA, LTN, MER, MWF, NPT, PAV, RHO, RTE, RTH, SAS, SAT, SAV, SFW, TSC, UFI, and combinations thereof; and
wherein the molecular sieve has a silica to alumina molar ratio ranging from 20 to 100.
2. The catalyst composition of claim 1 , wherein the extra framework aluminum atoms are present in an amount of about 0.1% to about 10% based on the total integrated peak intensity determined by 27 Al NMR of aluminum species present in the zeolite.
3. The catalyst composition of claim 2 , wherein the molecular sieve has a pore size of about 3 to about 5 Angstroms.
4. The catalyst composition of claim 1 , wherein the extra framework aluminum atoms are present in an amount of about 0.1% to about 5% based on the total integrated peak intensity determined by 27 Al NMR of aluminum species present in the zeolite.
5. The catalyst composition of claim 1 , wherein the molecular sieve has a pore size of about 3 to about 8 Angstroms.
6. The catalyst composition of claim 1 , wherein the zeolitic framework comprises a d6r unit.
7. The catalyst composition of claim 1 , wherein the zeolitic framework is selected from AEI, CHA, AFX, ERI, KFI, LEV, a CHA-AEI intergrowth, and combinations thereof.
8. The catalyst composition of claim 1 , wherein the zeolitic framework is CHA.
9. The catalyst composition of claim 8 , wherein the molecular sieve is an aluminosilicate zeolite.
10. The catalyst composition of claim 1 , wherein the metal is present in the catalyst composition in an amount of from about 0.01% to about 15.0% by weight, based on the total weight of the metal-containing molecular sieve, calculated as metal oxide.
11. The catalyst composition of claim 1 , wherein the metal is copper, iron, or a combination thereof.
12. The catalyst composition of claim 11 , wherein copper metal is present in the molecular sieve in an amount of from about 0.01% to about 10.0% by weight of final metal-containing zeolite, calculated as copper oxide (CuO).
13. The catalyst composition claim 1 , wherein the molecular sieve further comprises a promoter metal selected from the group consisting of alkali metals, alkaline earth metals, transition metals in Groups IIIB, IVB, VB, VIB VIIB VIIIB, IB, and IIB, Group IIIA elements, Group IVA elements, lanthanides, actinides, and a combination thereof.
14. A catalyst article comprising a catalyst substrate having a plurality of channels adapted for gas flow, each channel having a wall surface in adherence to a catalytic coating comprising the catalyst composition of claim 1 .
15. The catalyst article of claim 14 , wherein the catalyst substrate is a honeycomb comprising a wall flow filter substrate or a flow through substrate.
16. The catalyst article of claim 14 , wherein the catalytic coating is present on the substrate with a loading of at least about 1.0 g/in 3 .
17. A method for reducing NO x level in an exhaust gas comprising contacting the gas with a catalyst for a time and temperature sufficient to reduce the level of NO x in the gas, wherein the catalyst is a catalyst composition according to claim 1 .
18. The method of claim 17 , wherein the NO x level in the exhaust gas is reduced to N 2 and water at a temperature between 200° C. to about 600° C.
19. The method of claim 18 , wherein the NO x level in the exhaust gas is reduced by at least 60% at 200° C.
20. The method of claim 19 , wherein the NO x level in the exhaust gas is reduced by at least 50% at 600° C.
21. An emission treatment system for treatment of an exhaust gas stream, the emission treatment system comprising:
i.) an engine producing an exhaust gas stream;
ii.) a catalyst article according to claim 16 positioned downstream from the engine in fluid communication with the exhaust gas stream and adapted for the reduction of NO x within the exhaust stream to form a treated exhaust gas stream; and
iii.) an injector adapted for the addition of a reductant to the exhaust gas stream to promote reduction of NO x to N 2 and water as the exhaust gas stream is exposed to the catalyst article.
22. The emission treatment system of claim 21 , further comprising a diesel oxidation catalyst.
23. The emission treatment system of claim 21 , wherein the reductant comprises ammonia or an ammonia precursor.