Cross-linking agents and thermosetting paints
The present invention relates to new cross-linking agents and thermosetting paints, which lead to improved properties such as scratch resistance of cured thermosetting paints or exhibit good solubility.
1. A cross-linking agent formed from the following starting components:
(A) at least one aliphatic and/or cycloaliphatic polyisocyanate compound having ≧2 to 6 NCO function groups, obtained by trimerization, dimerization or formation of, biuret or allophanate, alone or in mixtures, and excluding polyisocyanates obtained from bis(4-isocyanatocyclohexyl)-methane;
(B) at least one secondary 3-aminopropyltrialkoxysilane, wherein 1 to 90 mol % of the originally free isocyanate groups of said polyisocyanate have been reacted with said secondary 3-aminopropyltrialkoxysilane;
(C) at least one blocking agent, wherein 10 to 99 mol % of the originally free isocyanate groups of said polyisocyanate have been reacted with said blocking agent, and the molar proportions of the reacted isocyanate groups add up to at least 95 mol %.
2. The cross-linking agent of claim 1 , wherein said polyisocyanate is based on a diisocyanate selected from the group consisting of hexamethylene diisocyanate; isophorone diisocyanate; tetramethylxylylene diisocyanate; 1,3-bis(isocyanatomethyl)cyclohexane; 2,2,4-trimethyl-1,6-diisocyanatohexane; 2,4,4-trimethyl-1,6-diisocyanatohexane; 2-methylpentene diisocyanate-1,5; norbornyl diisocyanate; lysine triisocyanate; 4-isocyanatomethyl-1,8-octamethylene diisocyanate; and mixtures thereof.
3. A process for preparing a cross-linking agent, said process comprising reacting (A) at least one aliphatic and/or cycloaliphatic polyisocyanate compound having ≧2 to 6 NCO function groups, obtained by trimerization, dimerization or formation of biuret or allophanate, alone or in mixtures, and excluding polyisocyanates obtained from bis(4-isocyanatocyclohexyl)-methane, with
B) at least one secondary 3-aminopropyltrialkoxysilane, wherein 1 to 90 mol % of the originally free isocyanate groups of said polyisocyanate have been reacted with said 3-aminopropyltrialkoxysilane; and
C) at least one blocking agent, wherein 10 to 99 mol % of the originally free isocyanate groups of said polyisocyanate have been reacted with said blocking agent, and wherein the molar proportions of the reacted isocyanate groups add up to at least 95 mol %.
4. The cross-linking agent of claim 1 , wherein said polyisocyanate is a mixture of a polyisocyanate and a monomeric diisocyanate.
5. The cross-linking agent of claim 1 , wherein said polyisocyanate has bad its chain extended or is branched.
6. The cross-linking agent of claim 1 , wherein said secondary 3-aminopropyltrialkoxysilane has the general formula I
R—NH—(CH 2 ) 3 —Si(OR 1 ) 3 (I)
wherein R denotes a n-alkyl, isoalkyl, tert-alkyl, cycloalkyl, or aryl group with 1 to 10 carbon atoms and the groups denoted by R 1 can be, independently of one another, an n-alkyl or isoalkyl group with 1 to 8 carbon atoms.
7. The cross-linking agent of claim 6 , wherein said secondary 3-aminopropyltrialkoxysilane is selected from the group consisting of n-butyl-3-aminopropyltriethoxysilane, n-butyl-3-aminopropyltri-i-propoxysilane, methyl-3-aminopropyltriethoxysilane, methyl-3-aminopropyltri-i-propoxysilane, phenyl-3-aminopropyltriethoxysilane, phenyl-3-aminopropyltrimethoxysilane, phenyl-3-aminopropyltri-i-propoxysilane, cyclohexyl-3-aminopropyltriethoxysilane, cyclohexyl-3-aminopropyltriethoxysilane, cyclohexyl-3-aminopropyltri-i-propoxysilane, and mixtures thereof.
8. The cross-linking agent of claim 1 , wherein said secondary 3-aminopropyltrialkoxysilane has the general formula I
R—NH—(CH 2 ) 3 —Si(OR 1 ) 3 (I)
wherein R is —(CH 2 ) 3 —Si(OR 1 ) 3 and the groups denoted by R 1 can be, independently of one another, an n-alkyl or isoalkyl group with 1 to 8 carbon atoms.
9. The cross-linking agent of claim 1 , wherein said secondary 3-aminopropyltrialkoxysilane has the general formula I
R—NH—(CH 2 ) 3 —Si(OR 1 ) 3 (I)
wherein R has the structure
—CHR 2 —CR 3 R 4 H
with R 2 =—H, Cl to C8 alkyl, —CO 2 R 1 ;
with R 3 =—H, methyl;
with R 4 =—CO 2 R 1 , —CN,
and the groups denoted by R 1 can be, independently of one another, an n-alkyl or isoalkyl group with 1 to 8 carbon atoms.
10. The cross-linking agent of claim 1 , wherein said blocking agent is selected from the group consisting of ketoximes, aldoximes, substituted and unsubstituted 1,2,4-triazoles, substituted and unsubstituted pyrazoles, 3,5-dimethylpyrazole, ε-caprolactam, malonic acid esters, acetic acid esters, phenol, substituted phenols, secondary amines, C1 to C10 monohydric alcohols, and mixtures thereof.
11. A cross-linking agent, prepared by a process, said process comprising reacting (A) at least one aliphatic and/or cycloaliphatic polyisocyanate compound having ≧2 to 6 NCO function groups, obtained by trimerization, dimerization or formation of biuret or allophanate, alone or in mixtures, and excluding polyisocyanates obtained from bis(4-isocyanatocyclohexyl)-methane, with
B) at least one secondary 3-aminopropyltrialkoxysilane, wherein 1 to 90 mol % of the originally free isocyanate groups of said polyisocyanate have been reacted with said 3-aminopropyltrialkoxysilane; and
C) at least one blocking agent, wherein 10 to 99 mol % of the originally free isocyanate groups of said polyisocyanate have been reacted with said blocking agent, and wherein the molar proportions of the reacted isocyanate groups add up to at least 95 mol %.