Catalyst for polymerization and copolymerization of ethylene
A solid titanium complex catalyst for polymerization and copolymerization of ethylene is prepared by the process comprising: (1) preparing a magnesium solution by reacting a halogenated magnesium compound with an alcohol; (2) reacting the magnesium solution with a phosphorus compound and a silicon compound having at least one alkoxy group to produce a magnesium composition; and (3) producing a solid titanium catalyst through recrystallization by reacting the magnesium composition solution with a mixture of a titanium compound and a haloalkane compound; and optionally reacting the solid titanium catalyst with an additional titanium compound. The solid titanium complex catalyst for polymerization and copolymerization of ethylene according to present invention exhibits high polymerization activity, and may be advantageously used in the polymerization and copolymerization of ethylene to produce polymers of high bulk density and narrow molecular weight distribution.
1. A catalyst for polymerization and copolymerization of ethylene, prepared by a method comprising:
(1) preparing a magnesium solution by reacting a halogenated magnesium compound with an alcohol;
(2) reacting the magnesium solution with a phosphorus compound and a silicon compound having at least one alkoxy group to produce a magnesium composition solution; and
(3) producing a solid titanium catalyst by reacting the magnesium composition solution with a mixture of a titanium compound and a haloalkane compound.
2. The catalyst of claim 1 , wherein the method further comprises reacting the solid titanium catalyst with an additional titanium compound.
3. The catalyst of claim 1 , wherein the phosphorus compound is represented by the following general formula:
PX a R 1 b (OR 2 ) c or POX d R 3 e (OR 4 ) f
where X is a halogen atom, and R 1 ,R 2 ,R 3 and R 4 are hydrocarbyls having 1˜20 carbon atoms, each of which is the same or different from one another, and a, b, c, d, e and f are integers between 0 and 3 satisfying a+b+c=3 and d+e+f=3.
4. The catalyst of claim 1 , wherein the silicon compound having an alkoxy group is a compound represented by the general formula of R 1 a R 2 b R 3 c Si(OR 5 ) e , and wherein each of R 1 ,R 2 ,R 3 and R 5 independently are a hydrocarbyl group having about 1˜12 carbon atoms, and wherein a, b, and c are integers between 0 and 4, e is an integer between 1 and 4 and wherein a, b, c, and e satisfy the equation a+b+c+d+e=4.
5. The catalyst of claim 1 , wherein the titanium compound is represented by the general formula of Ti(OR) a X 4a , and wherein R is an alkyl group having 1˜10 carbon atoms, X is a halogen atom, and a is an integer between 0 and 4.
6. The catalyst of claim 1 , wherein the haloalkane compound is a hydrocarbon compound which contains at least one halogen and has 1˜20 carbon atoms.
7. The catalyst of claim 1 , wherein the amount of the mixture of titanium compound and haloalkane compound is about 0.1˜200 mol of total titanium compound plus haloalkane per one mole of magnesium compound, and wherein the mixing molar ratio of the haloalkane compound to the titanium compound is about 0.05˜0.95.
8. A method of preparing a catalyst for polymerization and copolymerization of ethylene, comprising:
(1) preparing a magnesium solution by reacting a halogenated magnesium compound with an alcohol;
(2) reacting the magnesium solution with a phosphorus compound and a silicon compound having at least one alkoxy group to produce a magnesium composition solution; and
(3) producing a solid titanium catalyst by reacting the magnesium composition solution with a mixture of a titanium compound and a haloalkane compound.
9. The method of claim 8 , wherein the method further comprises reacting the solid titanium catalyst with an additional titanium compound.
10. The method of claim 8 , wherein the phosphorus compound is the one represented by the following general formula:
PX a R 1 b (OR 2 ) c or POX d R 3 e (OR 4 ) f
where X is a halogen atom, and R 1 ,R 2 ,R 3 and R 4 are hydrocarbyls having 1˜20 carbon atoms, each of which is the same or different from one another, and a, b, c, d, e and f are integers between 0 and 3 satisfying a+b+c=3 and d+e+f=3.
11. The method of claim 8 , wherein the silicon compound having an alkoxy group is a compound represented by the general formula of R 1 a R 2 b R 3 c Si(OR 5 ) e and wherein each of R 1 ,R 2 ,R 3 and R 5 independently are a hydrocarbyl group having about 1˜12 carbon atoms, and wherein a, b, c, d, and e are integers between 0 and 4, e is an integer between 1 and 4 and wherein a, b, and c, satisfy the equation a+b+c+e=4.
12. The method of claim 8 , wherein the titanium compound is represented by the general formula of Ti(OR) a X 4-a , and wherein R is an alkyl group having 1˜10 carbon atoms, X is a halogen atom, and a is an integer between 0 and 4.
13. The method of claim 8 , wherein the haloalkane compound is a hydrocarbon compound which contains at least one halogen and has 1˜20 carbon atoms.
14. The method of claim 8 , wherein the amount of the mixture of titanium compound and haloalkane compound is about 0.1˜200 mol of total titanium compound plus haloalkane per one mole of magnesium compound, and wherein the mixing molar ratio of the haloalkane compound to the titanium compound is about 0.05˜0.95.