Method for manufacturing a filter body
The first step of a method for manufacturing polymer-bonded filter bodies is to produce a mixture of a sorptive agent, a liquid, and a polymer. This mixture is then pressed into a filter body by being placed in a compression mold and simultaneously applying a hot gas to it. The evaporation temperature of the liquid is lower than the melting temperature of the polymer while the temperature of the hot gas flowing through the mixture exceeds the evaporation temperature of the liquid. This inexpensive method can provide homogeneously structured high-performance filter bodies.
1. A method for producing a filter body in which a mixture of fine-grain meltable polymers and a granular material with a sorptive effect are pressed into a polymer-bonded molded piece by applying pressure and heat, characterized in that said mixture of said polymer and sorptive material is produced by adding a liquid medium, and in that a hot gaseous medium flows through said mixture in a compression mold causing substantially simultaneously a) said liquid medium to evaporate and be discharged and b) the polymer to melt, and in that the evaporation temperature of said liquid medium is not greater than the melting temperature of said polymer while the temperature of the supplied hot gaseous medium is above said evaporation temperature.
2. The method according to claim 1 characterized in that active charcoal is used as sorptive material and a fine-particle polyethylene is used for polymer bonding of the active charcoal while water is the liquid medium.
3. The method according to claim 2 , characterized in that the mixing ratio is 50 to 90 parts of active charcoal, 15 to 50 parts of water, and 2 to 10 parts of polyethylene.
4. The method according to claim 3 wherein the mixing ratio of active charcoal, water, and polyethylene is 70:30:5.
5. The method according to claim 1 , characterized in that first the liquid medium is added to said sorptive material and adsorbed to its surface, then the polymer is added.
6. The method according to claim 1 wherein air is used as the gaseous medium.
7. The method according to claim 6 , characterized in that the temperature of the air supplied is in the range from 125° C. to 165° C.
8. The method according to claim 1 , characterized in that said adsorptive and/or absorptive material is impregnated with a material that has a chemisorptive and/or cata-lytic effect.
9. A method for producing a filter body in which a mixture of a fine-grain meltable polymer and a granular material with a sorptive effect are pressed in to a polymer-bonded molded piece by applying pressure and heat, consisting essentilly of the steps of flowing a hot gaseous medium through said mixture of a polymer and sorptive material, thereby melting said polymer and applying pressure.
10. The method according to claim 9 , characterized in that the temperature of the air supplied as a gaseous medium is in the range from 125° C. to 165° C.
11. The method according to claim 9 , characterized in that said granular material is impregnated with a material that has a chemisorptive and/or catalytic effect.