Aqueous dispersions of comb copolymers and coatings produced therefrom
An aqueous coating composition comprising a comb copolymer is disclosed. A method of forming a coating from the aqueous coating composition, and a coating formed by that method are also disclosed, as is a method of forming the comb copolymer. The comb copolymer is characterized in that aqueous dispersions of the comb copolymer have a Hard/Soft Balance Advantage value of at least 25%. The aqueous coating composition is capable of producing coatings having an excellent balance of hard and soft properties.
1. A method of forming a dry coating comprising the steps of:
(A) preparing a plurality of comb copolymer particles by a polymerization method comprising the steps of:
(a) forming a macromonomer aqueous emulsion comprising a plurality of water-insoluble particles of macromonomer, wherein:
said step of forming said macromonomer comprises polymerizing in an aqueous emulsion at least one first ethylenically unsaturated monomer in the presence of a transition metal chelate chain transfer agent and a free radical initiator; and
said macromonomer comprises polymerized units of at least one first ethylenically unsaturated monomer, said macromonomer further having:
(i) a degree of polymerization of from 10 to 1000;
(ii) at least one terminal ethylenically unsaturated groups;
(iii) less than 5 weight percent polymerized acid-containing monomer, based on said macromonomer; and
(iv) no polymerized mercaptan-olefin compounds;
(b) forming a monomer composition comprising at least one second ethylenically unsaturated monomer;
(c) combining at least a portion of said macromonomer aqueous emulsion and at least a portion of said monomer composition to form a polymerization reaction mixture; and
(d) polymerizing said macromonomer with said second ethylenically unsaturated monomer in the presence of an initiator to produce said plurality of comb copolymer particles;
(B) forming an aqueous coating composition comprising said plurality of comb copolymer particles;
(C) applying said coating composition to a substrate; and
(D) drying, or allowing to dry, said applied coating composition.
2. The method of claim 1 , wherein said polymerizing in an aqueous emulsion further comprises said polymerizing in an aqueous emulsion in the presence of a macromolecular organic compound.