Aluminum alloy fin material for heat exchangers and heat exchanger including the fin material
View Patent ↗The present invention provides an aluminum alloy fin material for heat exchangers which has a thickness of 80 μm (0.08 mm) or less and excels in joinability to a tube material and in intergranular corrosion resistance. The aluminum alloy fin material is an aluminum alloy bare fin material or a brazing fin material which has a thickness of 80 μm or less and is incorporated into a heat exchanger made of an aluminum alloy manufactured by brazing through an Al—Si alloy filler metal. The structure of the core material before brazing is a fiber structure, and the crystal grain diameter of the structure after brazing is 50–250 μm. The Si concentration in the Si dissolution area on the surface of the fin material and at the center of the thickness of the fin material after brazing is preferably 0.8% or more and 0.7% or less, respectively.
1. An aluminum alloy fin material for heat exchangers which has a thickness of no greater than 80 μm and is incorporated into a heat exchanger made of an aluminum alloy manufactured by brazing through an Al—Si alloy filler metal, wherein the structure of the fin material before brazing is a fiber structure, the crystal grain diameter of the structure of the fin material after brazing is 50–250 μm and the Si concentration in an Si dissolution area in a brazed section at the center of the thickness of the fin material after brazing is no greater than 0.7 mass %.
2. An aluminum alloy fin material for heat exchangers comprising the fin material as defined in claim 1 as a core material and an Al—Si alloy filler metal clad on both sides of the core material.
3. The aluminum alloy fin material for heat exchangers as defined in claim 2 , wherein the Si concentration in an Si dissolution area in a brazed section on the surface of the fin material after brazing is at least 0.8 mass %.
4. A heat exchanger comprising the aluminum alloy fin material as defined in claim 1 which is joined by brazing.
5. An aluminum alloy fin material for heat exchangers which has a thickness of no greater than 80 μm and is incorporated into a heat exchanger made of an aluminum alloy manufactured by brazing through an Al—Si alloy filler metal, wherein the fin material is made of an aluminum alloy comprising 0.82–2.0 mass % of Mn, 0.05–0.8 mass % of Fe, Si in an amount not exceeding 1.5 mass %, Cu in an amount not exceeding 0.2 mass % and 0.5–4 mass % of Zn, with the balance being Al and impurities, the structure of the fin material before brazing is a fiber structure and the crystal grain diameter of the structure of the fin material after brazing is 50–250 μm.
6. The aluminum alloy fin material for heat exchangers as defined in claim 5 , wherein the Cu content in the fin material is 0.03% or less.
7. The aluminum alloy fin material for heat exchangers as defined in claim 5 , wherein the fin material further comprises at least one of 0.05–0.3% of Zr and 0.05–0.3% of Cr.
8. An aluminum alloy fin material for heat exchangers which has a thickness of no greater than 80 μm and is incorporated into a heat exchanger made of an aluminum alloy manufactured by brazing through an Al—Si alloy filler metal, wherein a core material comprises the fin material, an Al—Si alloy filler material is clad on both sides of the core material, the structure of the fin material before brazing is a fiber structure, the crystal grain diameter of the structure of the fin material after brazing is 50–250 μm, the fin material is made of an aluminum alloy which comprises 0.8–2.0 mass % of Mn, 0.05–0.8 mass % of Fe, no more than 1.5 mass % of Si and 0.5–4 mass % of Zn, with the balance being Al and impurities, and the filler metal is clad on each side of the core material respectively at a thickness of 3–20% of the total thickness of the fin material and the filler metal.
9. The aluminum alloy fin material for heat exchangers as defined in claim 8 , wherein the core material comprises 0.03% or less of Cu, and the filler metal comprises 0.1% or less of Cu.
10. The aluminum alloy fin material for heat exchangers as defined in claim 8 , wherein the core material further comprises at least one of 0.05–0.3% of Zr and 0.05–0.3% of Cr.
11. The aluminum alloy fin material for heat exchangers as defined in claim 8 , wherein the filler metal further comprises 0.5–6% of Zn.