Colored glass compositions and-automotive vision panels with-reduced transmitted-color shift
A neutral gray colored glass composition for automotive vision panels having reduced transmitted color shift characteristics is provided. The glass composition has a base portion including 65 to 75 weight percent SiO 2 , 10 to 20 weight percent Na 2 O, 5 to 15 weight percent CaO, 0 to 5 weight percent MgO, 0 to 5 weight percent Al 2 O 3 , and 0 to 5 weight percent K 2 O. The composition also includes major colorants including 0.30 to 0.75 weight percent Fe 2 O 3 , 0 to 15 ppm CoO, and 1 to 15 ppm Se. The glass has a luminous transmittance of at least 65 percent at a thickness of 3.9 mm, a redox ratio of 0.2 to 0.675, a TSET of less than or equal to 65 percent, and a standard color shift of less than 6.
1. A neutral gray colored glass composition for automotive vision panels having reduced transmitted color shift characteristics, the glass composition having a base portion comprising:
SiO 2
65 to 75
weight percent
Na 2 O
10 to 20
weight percent
CaO
5 to 15
weight percent
MgO
0 to 5
weight percent
Al 2 O 3
0 to 5
weight percent
K 2 O
0 to 5
weight percent
and major colorants comprising:
Fe 2 O 3 (total iron)
0.30 to 0.75
weight percent
CoO
0 to 15
ppm
Se
1 to 15
ppm
wherein the glass has a luminous transmittance of at least 65 percent at a thickness of 3.9 mm, a redox ratio of equal to or greater than 0.4, a TSET of less than or equal to 65 percent, a dominant wavelength ranging from 480 nm to 560 nm and a standard transmitted color shift of less than 6.
2. The glass composition according to claim 1 , wherein the glass composition is essentially free of nickel.
3. The glass composition according to claim 1 , wherein the glass composition includes one or more additional components selected from chromium oxide, manganese oxide, titanium oxide, cerium oxide, zinc oxide, molybdenum oxide, or iron polysulfide.
4. The glass composition according to claim 1 , wherein the total iron is greater than 0.5 weight percent up to 0.07 weight percent.
5. The glass composition according to claim 1 , wherein the CoO is less than 12 ppm.
6. The glass composition according to claim 1 , wherein the Se is less than 8 ppm.
7. The glass composition according to claim 1 , wherein the standard transmitted color shift is less than or equal to 4.
8. The glass composition according to claim 1 , wherein the TSET is less than or equal to 60 percent.
9. The glass composition according to claim 1 , wherein the excitation purity is less than 8 percent.
10. The glass composition according to claim 1 , wherein the excitation purity is less than 3 percent.
11. The glass composition according to claim 1 , further including additional ultraviolet absorbing material.
12. The glass composition according to claim 11 , wherein the additional ultraviolet absorbing material is an oxide of a material selected from the group cerium, zinc, tin, vanadium, titanium, molybdenum or combinations thereof.
13. The glass composition according to claim 11 , wherein the additional ultraviolet material is less than or equal to 3 weight percent of the glass composition.
14. The glass composition according to claim 1 , wherein the total iron is greater than 0.5 and up to 0.72 weight percent, the CoO is less than 9 ppm, and the Se is 1 to 6 ppm.
15. The glass composition according to claim 1 , wherein the total iron is 0.3 to 0.5 weight percent.
16. The glass composition according to claim 15 , wherein the redox ratio is 0.4 to 0.675.
17. The glass composition according to claim 15 , wherein the Se is 3 to 6 ppm.
18. The glass composition according to claim 15 , wherein the total iron is 0.3 to 0.5 weight percent, the redox ratio is 0.4 to 0.675, the CoO is 0 ppm, and the Se is 4 to 5 ppm.
19. The glass composition according to claim 15 , including up to 10 ppm of iron polysulfide.
20. A neutral gray colored glass composition having reduced transmitted color shift characteristics as an automotive vision panels, the glass composition having a base portion comprising:
SiO 2
65 to 75
weight percent
Na 2 O
10 to 20
weight percent
CaO
5 to 15
weight percent
MgO
0 to 5
weight percent
Al 2 O 3
0 to 5
weight percent
K 2 O
0 to 5
weight percent
and major colorants comprising:
Fe 2 O 3 (total iron)
0.30 to 0.75
weight percent
CoO
0 to 15
ppm
Se
1 to 15
ppm
and essentially free of at least one of lanthanum oxide and cerium oxide, wherein the glass has a luminous transmittance of at least 65 percent at a thickness of 3.9 mm, a redox ratio of equal to or greater than 0.4, a TSET of less than or equal to 65 percent, a dominant wavelength ranging from 480 nm to 560 nm and a standard transmitted color shift of less than 6.
21. A neutral gray colored glass composition having reduced transmitted color shift characteristics as an automotive vision panel, the glass composition having a base portion comprising:
SiO 2
65 to 75
weight percent
Na 2 O
10 to 20
weight percent
CaO
5 to 15
weight percent
MgO
0 to 5
weight percent
Al 2 O 3
0 to 5
weight percent
K 2 O
0 to 5
weight percent
and major colorants comprising:
Fe 2 O 3 (total iron)
0.30 to 0.70
weight percent
CoO
0 to 15
ppm
Se
1 to 15
ppm
wherein the glass has a luminous transmittance of at least 65 percent at a thickness of 3.9 mm, a redox ratio of equal or greater than 0.4, a TSET of less than or equal to 65 percent, a dominant wavelength ranging from 480 nm to 560 nm and a standard transmitted color shift of less than 6.
22. An automobile having an interior and at least one vision panel having reduced transmitted color shift characteristics, the vision panel formed from a glass composition having a base portion comprising:
SiO 2
65 to 75
weight percent
Na 2 O
10 to 20
weight percent
CaO
5 to 15
weight percent
MgO
0 to 5
weight percent
Al 2 O 3
0 to 5
weight percent
K 2 O
0 to 5
weight percent
and major colorants comprising:
Fe 2 O 3 (total iron)
0.30 to 0.70
weight percent
CoO
0 to 15
ppm
Se
1 to 15
ppm
wherein the glass has a luminous transmittance of at least 65 percent at a thickness of 3.9 mm, a redox ratio of equal to or greater than 0.4, a TSET of less than or equal to 65 percent, a dominant wavelength ranging from 480 nm to 560 nm and a standard color shift of less than 6.
23. A transparency made from the glass composition recited in claim 1 .
24. The transparency of claim 23 , wherein the transparency has a thickness of 1 mm to 20 mm.
25. The transparency of claim 24 , including a solar control coating deposited over at least a portion of the transparency.
26. The transparency of claim 24 , wherein the transparency is an automotive vision panel.
27. A neutral gray colored glass composition for automotive vision panels having reduced transmitted color shift characteristics, the glass composition having a base portion comprising:
SiO 2
65 to 75
weight percent
Na 2 O
10 to 20
weight percent
CaO
5 to 15
weight percent
MgO
0 to 5
weight percent
Al 2 O 3
0 to 5
weight percent
K 2 O
0 to 5
weight percent
and major colorants comprising:
Fe 2 O 3 (total iron)
0.30 to 0.70
weight percent
CoO
0 to 15
ppm
Se
1 to 15
ppm
wherein the glass has a luminous transmittance of at least 65 percent at a thickness of 3.9 mm, a redox ratio of equal to or greater than 0.4, a TSET of less than or equal to 65 percent, a dominant wavelength ranging from 480 nm to 560 nm and a standard transmitted color shift of less than 4.
28. A neutral gray colored glass composition for automotive vision panels having reduced transmitted color shift characteristics, the glass composition having a base portion comprising:
SiO2
65 to 75
weight percent
Na 2 O
10 to 20
weight percent
CaO
5 to 15
weight percent
MgO
0 to 5
weight percent
Al 2 O 3
0 to 5
weight percent
K 2 O
0 to 5
weight percent
and major colorants consisting essentially of:
Fe 2 O 3 (total iron)
0.30 to 0.75
weight percent
CoO
0 to 15
ppm
Se
1 to 15
ppm
wherein the glass has a luminous transmittance of at least 65 percent at a thickness of 3.9 mm, a redox ratio of equal to or greater than 0.4, a TSET of less than or equal to 65 percent, a dominant wavelength ranging from 480 nm to 560 nm and a standard transmitted color shift of less than 6.