Light fixture with reflective polymeric composition and pigment package
View Patent ↗The present invention provides a light reflecting polymeric composition that includes at least one halogenated-flame-retardant-additive-free polymer having dispersed therein a pigment package including a combination of Sb 2 O 3 and TiO 2 . The Sb 2 O 3 and TiO 2 preferably have an average particle size within the range of from about 0.05 μm to about 1.0 μm, and more preferably about 0.2 μm. When used in combination, the Sb 2 O 3 and TiO 2 pigments synergistically interact together to provide a polymeric composition exhibiting a reflectivity that is substantially higher than can be obtained by the use of either of the pigments alone.
1. A lighting fixture comprising a light source and a reflector disposed adjacent to said light source, said reflector being formed from a light reflecting polymeric composition comprising at least one halogenated-flame-retardant-additive-free polymer having dispersed therein a pigment package comprising a combination of about 10 wt % to about 60 wt % of particles of Sb 2 O 3 and about 40 wt % to about 90 wt % of particles of TiO 2 , wherein the ratio of polymer to pigment package is from about 100:1 to about 3:1 by weight, and wherein the Sb 2 O 3 and TiO 2 , in said pigment package both have an average particle size of about 0.05 micron to about 1 micron.
2. The lighting fixture according to claim 1 wherein said light source comprises a fluorescent lamp.
3. The lighting fixture according to claim 1 wherein the average particle size of the Sb 2 O 3 in said pigment package is from about 0.1 micron to about 0.3 micron.
4. The lighting fixture according to claim 1 wherein the average particle size of the TiO 2 in said pigment package is from about 0.1 micron to about 0.3 micron.
5. The lighting fixture according to claim 1 wherein said polymer comprises a polyolefin.
6. The lighting fixture according to claim 5 wherein said polyolefin comprises polypropylene.
7. The lighting fixture according to claim 1 wherein an organic optical brightener is dispersed in the polymer.
8. The lighting fixture according to claim 1 wherein one or more antioxidants is dispersed in the polymer.
9. A lighting fixture having a polymeric composition comprising from about 75 to about 95 parts by weight of a halogenated-flame-retardant-additive-free polyolefin having dispersed therein from about 5 to about 25 parts by weight of a pigment package comprising a combination of Sb 2 O 3 and TiO 2 , wherein said pigment package comprises from about 10% to about 60% Sb 2 O 3 by weight and from about 40% to about 90% TiO 2 by weight.
10. The light fixture according to claim 9 wherein the Sb 2 O 3 and TiO 2 in said pigment package both have an average particle size within the range of from about 0.1 micron to about 0.3 micron.
11. The light fixture according to claim 10 wherein an organic optical brightener is dispersed in the polyolefin.
12. The light fixture according to claim 11 wherein one or more antioxidants are dispersed in the polyolefin.
13. The fixture according to claim 9 wherein said polyolefin comprises a homopolymer of polypropylene.
14. A lighting fixture comprising a light source and a reflector disposed adjacent to said light source, said reflector being formed from a light reflecting polymeric composition comprising a polymer having dispersed therein a pigment package comprising a combination of from about 10% to about 60% by weight of particles of Sb 2 O 3 and from about 40% to about 90% by weight of particles of TiO 2 , wherein the ratio of polymer to pigment package is from about 100:1 to about 3:1 by weight, and wherein the Sb 2 O 3 and TiO 2 in said pigment package both have an average particle size within the range of from about 0.1 μm to about 0.3 μm.