Styrene copolymers with improved resistance to chemicals
The invention relates to the use of phyllosilicates for improving the chemicals resistance, reducing the swelling, and improving the stress-cracking resistance of styrene copolymers, and to corresponding styrene copolymers, and to a process for their preparation.
1. A method for improving the chemicals resistance, reducing the swelling, and improving the stress-cracking resistance of styrene-acrylonitrile copolymers having a proportion of acrylonitrile of less than 28% by weight, comprising the step of adding phyllosilicates to said styrene-acrylonitrile copolymers, wherein the styrene-acrylonitrile copolymers have been built up from components A, C, and, where appropriate, and E, using:
a: as component A, from 20 to 100% by weight, based on the entirety of components A+B, of a hard component made from one or more copolymers of styrene and/or α-methylstyrene with acrylonitrile, the proportion of acrylonitrile being from 10 to less than 28% by weight,
b: from 0 to 80% by weight, based on the entirety of components A+B, of at least one graft copolymer B made from
b1: as component B1, from 10 to 90% by weight of at least one elastomeric particulate graft base with a glass transition temperature below 0° C., and
b2: as component B2, from 10 to 90% by weight of at least one graft made from polystyrene or from a copolymer of styrene and/or α-methylstyrene with acrylonitrile, the proportion of acrylonitrile being from 10 to less than 28% by weight,
where the entirety of the components A+B used is from 10 to 100 parts by weight, based on the total weight of the components used,
c: as component C, from 0.05 to 5 parts by weight, based on the total weight of the components used, of a phyllosilicate, and
e: as component E, from 0 to 20 parts by weight, based on the total weight of the components used, of other conventional auxiliaries and fillers, and
wherein the phyllosilicate is mica.
2. The method as claimed in claim 1 , wherein the chemical resistance is improved with respect to chemicals selected from alcohols, C 3 –C 8 alkanes, gasoline, premium gasoline, diesel, halogenated hydrocarbons, hypochlorite salts, and sodium dichloroisocyanate dihydrate.
3. The method as claimed in claim 1 , wherein the proportion of acrylonitrile is from 18 to 27% by weight.
4. A thermoplastic molding composition built up from components A, C, and where appropriate, and E, using
a: as component A, from 20 to 100% by weight, based on the entirety of components A+B, of a hard component made from one or more copolymers of styrene and/or α-methylstyrene with acrylonitrile, the proportion of acrylonitrile being from 10 to less than 28% by weight,
b: from 0 to 80% by weight, based on the entirety of components A+B, of at least one graft copolymer B made from
b1: as component B1, from 10 to 90% by weight of at least one elastomeric particulate graft base with a glass transition temperature below 0° C., and
b2: as component B2, from 10 to 90% by weight of at least one graft made from polystyrene or from a copolymer of styrene and/or α-methylstyrene with acrylonitrile, the proportion of acrylonitrile being from 10 to less than 28% by weight,
where the entirety of the components A+B used is from 10 to 100 parts by weight, based on the total weight of the components used,
c: as component C, from 0.05 to 5 parts by weight, based on the total weight of the components used, of a phyllosilicate,
e: as component E, from 0 to 20 parts by weight, based on the total weight of the components used, of other conventional auxiliaries and fillers,
wherein the phyllosilicate is mica.
5. A thermoplastic molding composition as claimed in claim 4 , wherein the proportion of acrylonitrile is from 18 to 27% by weight.
6. A process for preparing the styrene polymers with improved chemical resistance as claimed in claim 4 , which comprises separately preparing components A and C, and, where appropriate, components B, and E, combining component A with component C, and intimately mixing and then extruding the same with components B, and E, as appropriate.
7. A method for improving the chemicals resistance, reducing the swelling, and improving the stress-cracking resistance of styrene copolymers, which comprises adding to said copolymers an effective amount of mica.
8. A method as claimed in claim 1 , wherein the amount of mica is from 0.15 to 3 parts by weight.
9. A thermoplastic molding composition as claimed in claim 4 , wherein the amount of mica is from 0.15 to 3 parts by weight.
10. A process for preparing the styrene polymers with improved chemical resistance as claimed in claim 9 , which comprises separately preparing components A and C, and, where appropriate, components B, and E, combining component A with component C, and intimately mixing and then extruding the same with components B, and E, as appropriate.
11. A method as claimed in claim 7 , wherein the amount of mica is from 0.15 to 3 parts by weight.
12. A method as claimed in claim 1 , wherein the amount of component E is from 0 to 15 parts by weight.
13. A thermoplastic molding composition as claimed in claim 4 , wherein the amount of component E is from 0 to 15 parts by weight.
14. A process for preparing the styrene polymers with improved chemical resistance as claimed in claim 13 , which comprises separately preparing components A and C, and, where appropriate, components B, and E, combining component A with component C, and intimately mixing and then extruding the same with components B, and E, as appropriate.
15. A method as claimed in claim 7 , wherein the styrene copolymers comprise from 0 to 15 parts by weight of other conventional auxiliaries and fillers.
16. A method as claimed in claim 8 , wherein the amount of component E is from 0 to 15 parts by weight.
17. A thermoplastic molding composition as claimed in claim 9 , wherein the amount of component E is from 0 to 15 parts by weight.
18. A process for preparing the styrene polymers with improved chemical resistance as claimed in claim 17 , which comprises separately preparing components A and C, and, where appropriate, components B, and E, combining component A with component C, and intimately mixing and then extruding the same with components B, and E, as appropriate.
19. A method as claimed in claim 11 , wherein the styrene copolymers comprise from 0 to 15 parts by weight of other conventional auxiliaries and fillers.