Magnetic recording medium containing particles with a core containing a Fe
A magnetic recording medium comprising a nonmagnetic support and a magnetic layer formed on the support and containing a magnetic powder and a binder, wherein said magnetic powder comprises substantially spherical or ellipsoidal particles and at least one element selected from the group consisting of rare earth elements, silicon and aluminum, and has a Fe 16 N 2 phase, an average particle size of 5 to 30 nm and an axis ratio (a ratio of a major axis to a minor axis) of 1 to 2. This magnetic recording medium achieves a high output and has excellent short wavelength recording properties, since it uses a magnetic powder having a very small particle size and has a very high coercive force and a saturation magnetization suitable for high density recording.
1. A magnetic recording medium comprising a nonmagnetic support and a magnetic layer formed on the support and containing a magnetic powder and a binder, wherein said magnetic powder comprises substantially spherical or ellipsoidal particles and said particles have an outer layer containing at least one element selected from the group consisting of rare earth elements, silicon and aluminum, and a core containing a Fe 16 N 2 phase and wherein said particles have an average particle size of 5 to 50 nm, wherein said particles have an axis ratio (a ratio of a major axis to a minor axis) of 1 to 2 and said particles have a saturation magnetization of 80–160 emu/g.
2. The magnetic recording medium according to claim 1 , wherein said particles have an average particle size of 5 to 30 nm.
3. The magnetic recording medium according to claim 1 , wherein a content of nitrogen is from 1.0 to 20.0 atomic % based on the amount of iron in the magnetic powder.
4. The magnetic recording medium according to claim 1 , wherein the rare earth element is at least one element selected from the group consisting of yttrium, samarium and neodymium.
5. The magnetic recording medium according to claim 1 , wherein a content of the rare earth element is from 0.05 to 20.0 atomic % based on the amount of iron in the magnetic powder.
6. The magnetic recording medium according to claim 1 , wherein a total content of silicon and aluminum is from 0.1 to 20.0 atomic % based on the amount of iron in the magnetic powder.
7. The magnetic recording medium according to claim 1 , which has a coercive force (Hc) of 79.6 to 318.4 kA/m (1,000 to 4,000 Oe), a squareness ratio (Br/Bm) of 0.6 to 0.9 both in the longitudinal direction, and a product (Bm·t) of a saturated magnetic flux density and a thickness of a magnetic layer of 0.001 to 0.1 μTm.
8. The magnetic recording medium according to claim 1 , which further comprises a primer layer comprising at least one nonmagnetic powder and a binder, wherein said magnetic layer has a thickness of 10 to 300 nm.