Porous wet friction material utilizing a compliant epoxide resin binder system
A wet friction material is disclosed bonded to a plate for transmission of motion, with the friction material made up of a porous fiber substrate, which is at least partially impregnated with a catalyzed resorcinol diglycidyl ether resin to improve properties.
1. A wet friction material comprising a base containing fibers, and a resin at least partially impregnating said base, said resin having a Tg of 145° F. or less and comprising at least 60 percent of a catalyzed resorcinol diglycidyl ether, said resin having a purity of 80% or higher, said resin being catalyzed with one of a Lewis acid and Lewis base, with homopolymerization of said resin, said wet friction material having a coefficient of friction higher than a wet friction material of the same physical construction but based on a phenol resin.
2. The wet friction material of claim 1 , wherein the resin is diluted in a solvent prior to application to the base, and the solvent is evaporated.
3. The wet friction material of claim 1 , wherein the material is generally thermosetting.
4. The friction material of claim 1 , wherein the base comprises cellulose fibers.
5. The friction material of claim 1 , wherein the friction material is generally a flat disk, and a rigid flat plate adhered to the flat disk.
6. A wet friction material as in claim 1 , wherein said wet friction material has a dynamic coefficient of friction greater than a wet friction material of the same physical construction but based on a phenol resin.
7. A wet friction material as in claim 1 , wherein said wet friction material has a coefficient of friction about 40% or higher than a wet friction material of the same physical construction, but based on a phenol resin.
8. A wet friction material as in claim 7 , wherein said wet friction material has a dynamic coefficient of friction about 40% or higher than a wet friction material of the same physical construction but based on a phenol resin.
9. A wet friction material as in claim 8 , wherein said resin is diluted in a solvent prior to application to the base, and the solvent is evaporated, said wet friction material being generally thermosetting, said base comprising cellulose fibers.
10. A wet friction material as in claim 9 , wherein the friction material is generally a flat disk, and a rigid flat plate adhere to the flat disk.
11. A wet friction material as in claim 1 , wherein said resin is diluted in a solvent prior to application to the base, and the solvent is evaporated, said wet friction material being generally thermosetting, said base comprising cellulose fibers.
12. A wet friction material as in claim 11 , wherein the friction material is generally a flat disk, and a rigid flat plate adhere to the flat disk.
13. A wet friction material as in claim 1 , wherein said wet friction material has a coefficient of friction about 40% or higher than a wet friction material of the same physical construction but based on a phenol resin, and dynamic coefficient of friction about 40% or higher than a wet friction material of the same physical construction but based on a phenol resin, said resin being diluted in a solvent prior to application to the base, and the solvent is evaporated, said wet friction material being generally thermosetting, said base comprising cellulose fibers.
14. A wet friction material as in claim 13 , wherein the friction material is generally a flat disk, and a rigid flat plate adhere to the flat disk.
15. A wet friction material as in claim 14 , wherein said Tg is in a range of 130-145° F.
16. A wet friction material as in claim 1 , wherein said Tg is in a range of 130-145° F.
17. The friction material as in claim 1 , wherein said material is mounted on each side of one or more a ring shaped metal support disks, a plurality of said ring shaped metal support disks being interleaved in relation with bare metal reaction disks, said ring shaped metal support disks and said bare metal reaction disks being movable in and out of engagement and running in lubricating oil.
18. The friction material as in claim 17 , which can conform to the bare metal reaction disks to maximize surface contact during engagement.
19. The friction material as in claim 1 , having an energy capacity at least 40-50% higher than a wet friction material of the same physical construction but based on a phenol resin.
20. The friction material as in claim 19 , wherein said comparison is made under the SAE J2487 stepped power level test.
21. The friction material as in claim 1 , wherein the remainder of the resin may include another resin.
22. The friction material as in claim 21 , comprising 70-80% RDGE and 30-10% epoxy Novolac resin.
23. The friction material as in claim 21 , further comprising about 70% RDGE, about 20% epoxy novolac resin and about 10% CTBN.
24. A friction material as in claim 1 , when tested under SAE J2487 completes more levels with less wear than a wet friction material of the same physical construction but based on a phenol resin.
25. A friction material as in claim 24 , completing at least two levels more than a wet friction material of the same physical construction but based on a phenol resin.
26. A friction material as in claim 1 , having 70% or less wear than a wet friction material of the same physical construction but based on a phenol resin.
27. A friction material as in claim 1 , having a lower “S” (Storage Modulus) than a wet friction material of the same physical construction but based on a phenol resin.
28. A friction material as in claim 27 , wherein said “S” (Storage Modulus) is less than about ½ to about ¼ of that of a wet friction material of the same physical construction but based on a phenol resin.
29. The friction material as in claim 1 , wherein said material is mounted on each side of one or more a ring shaped metal support disks, a plurality of said ring shaped metal disks being interleaved in relation with bare metal reaction disks, said ring shaped metal support disks and said bare metal reaction disks being movable in and out of engagement and running in lubricating oil, said friction material can conform to the bare metal reaction disks to maximize surface contact during engagement, said friction material having an energy capacity at least 40-50% higher than a wet friction material of the same physical construction but based on a phenol resin, comparison being made under the SAE J2487 stepped power level test, said friction material includes another resin, said friction material tested under SAE J2487 completes more levels with less wear than a wet friction material of the same physical construction but based on a phenol resin, and at least two levels more than a wet friction material of the same physical construction but based on a phenol resin, 70% or less wear than a wet friction material of the same physical construction but based on a phenol resin, a lower “S” (Storage Modulus) than a wet friction material of the same physical construction but based on a phenol resin, said “S” (Storage Modulus) is about ½ to about ¼ of that of a wet friction material of the same physical construction but based on a phenol resin.