Ceramic casting mold for casting metal and process for production thereof
View Patent ↗Casting mold for metal casting, in particular precision casting of fine parts of steel, in which at least the main part of the casting mold is made of porous ceramic with a high thermal coefficient of expansion which corresponds to the metal, and produced by generative rapid prototyping process, as well as generative rapid prototyping processes and coated powders particularly suitable therefore, as well as uses of the casting mold for tools and their components, in particular of steel.
1. A process for producing a casting mold for metallic foundry or for precision casting of fine metal parts, wherein the casting mold, or at least a part thereof, is produced by a generative rapid prototyping process, said process comprising:
a) forming a layer of a mixture of ceramic coarse particles and sinterable ceramic fine particles, wherein the average particle diameter of the coarse particles is above 10 μm, the average particle diameter of the ceramic fine particles is below 5 μm, and the average particle diameter of the ceramic coarse particles is at least 10 fold of the average particle diameter of the ceramic fine particles,
b) melting or sintering the ceramic fine particle under the influence of intensive radiation without substantially melting the ceramic coarse particles such that the fine particles form bridges binding the coarse particles, and
c) repeating steps a) and b) to form successive layers until a casting mold, or at least a part thereof, comprised of a porous ceramic in the sintered state is formed,
wherein the thermal coefficient of expansion of the thus produced ceramic casting mold or part is above approximately 8.5*10 −6 K −1 .
2. The process as in claim 1 , wherein said intensive radiation is laser radiation.
3. The process as in claim 1 , wherein the fine particles and coarse particles are the same material.
4. The process as in claim 1 , wherein the coarse particles are oxide ceramics based on Al, Zr, and/or Mg, while the fine ceramic particles are based on SiO 2 and/or silicates.
5. The process as in claim 1 , wherein said coarse particles are coated with an organic binder, and wherein fine particles are incorporated in said organic binder.
6. The process as in claim 5 , wherein the proportion of binder phase to ceramic phase is 7% or less.
7. The process as in claim 1 , wherein the sintering temperature of the fine particles is at least 50° C. below that of the coarse particles.
8. The process according to claim 1 , wherein the casting mold includes reinforcing ribs produced using a generative rapid prototyping process.
9. The process for according to claim 1 , wherein, at least during casting, the casting mold is back-fed with a fill of ceramic material.
10. A process for producing a casting mold for metallic foundry or for precision casting of fine metal parts,
wherein the casting mold, or at least a part thereof, is produced by a 3D binder printing process comprising
a) forming a layer of a mixture of ceramic coarse particles coated with a binder and ceramic fine particles,
b) dissolving or melting the binder in areas corresponding to the casting mold, or part thereof, so as to cause said coated particles in said areas to adhere,
c) repeating steps a) and b) to form successive layers until a green casting mold, or part thereof, is formed,
d) sintering said green casting mold, or part thereof, to sinter the fine particles without substantially melting the coarse particles such that the fine particles form bridges between the coarse particles, such that said mold or part thereof is comprised of a porous ceramic in the sintered state, and wherein the thermal coefficient of expansion of the ceramic mold is above approximately 8.5*10 −6 K −1 .
11. The process according to claim 10 , wherein the green casting mold includes 0.5 to 10 wt. % organic binder.
12. The process according to claim 10 , wherein the proportion of binder phase to ceramic phase is 7% or less.
13. The process according to claim 10 , wherein the average particle diameter of the coarse particles is above 10 μm, the average particle diameter of the fine particles is below 5 μm, and the average particle diameter of the coarse particles is at least 10 fold of the average particle diameter of the fine particles.
14. The process according to claim 10 , wherein said fine particles are incorporated in the binder coating the coarse particles.
15. The process according to claim 10 , wherein the fine particles and coarse particles are the same material.
16. The process according to claim 10 , wherein the sintering temperature of the fine particles is at least 50° C. below that of the coarse particles.
17. The process according to claim 10 , wherein the ceramic mold includes as a main component aluminum oxide, zirconium oxide, magnesium silicate, spinel and/or magnesium oxide.
18. The process according to claim 10 , wherein the binder coating the coarse particles is an organic polymer.
19. The process according to claim 18 , wherein the organic polymer is readily soluble in organic solvent.
20. The process according to claim 16 , wherein the ceramic coarse particles include oxides of the elements Mg, Al, and/or Zr, and the ceramic fine particles are comprised essentially of SiO 2 and/or silicates.