Polymer composition and process for producing the same
A polymer composition which comprises a polymer, a phosphorus compound (a), and a phenol compound (b). The phosphorus compound (a) is, e.g., at least one member selected from compounds represented by the following formula (1). The phenol compound (b) is, e.g., at least one member selected from compounds represented by the following general formula (4), wherein in the general formula (1), the R 1 represents C 1-20 alkyl, allyl, cycloalkyl, phenyl, or alkoxyalkyl and n is 1 or 2, provided that when two R 1 's are present, then the R 1 's may be the same or different, wherein in the general formula (4), the R 4 's each independently represents C 1-20 alkyl, allyl, cycloalkyl, phenyl, alkoxy, or alkylthiomethyl.
1. A polymer composition comprising:
syndiotactic 1,2-polybutadiene;
2-ethylhexyl acid phosphate;
2,2′-dihydroxy-3,3′-bis(methylcyclohexyl)-5,5′-dimethyldiphenylmethane; and
didodecyl-3,3′-thiodipropionate,
wherein the content of 2-ethylhexyl acid phosphate is 0.03-0.1 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the content of 2,2′-dihydroxy-3,3′-bis(methylcyclohexyl)-5,5′-dimethyldiphenylmethane is 0.1 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene, and
wherein the content of didodecyl-3,3′-thiodipropionate is 0.2 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene.
2. A polymer composition comprising:
syndiotactic 1,2-polybutadiene;
2-ethylhexyl acid phosphate;
pentaerythritoltetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]; and
pentaerythritoltetrakis(β-laurylthiopropionate),
wherein the content of 2-ethylhexyl acid phosphate is 0.05 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the content of pentaerythritoltetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] is 0.3 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene, and
wherein the content of pentaerythritoltetrakis(βlaurylthiopropionate) is 0.2 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene.
3. A polymer composition comprising:
syndiotactic 1,2-polybutadiene;
2-ethylhexyl acid phosphate;
n-octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate; and
distearyl-3,3′-thiodipropionate,
wherein the content of 2-ethylhexyl acid phosphate is 0.05 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the content of n-octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate is 0.1 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene, and
wherein the content of distearyl-3,3′-thiodipropionate is 0.1 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene.
4. A polymer composition comprising:
syndiotactic 1,2-polybutadiene;
2-ethylhexyl acid phosphate;
n-octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate;
4,6-bis(octylthiomethyl)-o-cresol; and
dilauryl-3,3′-thiodipropionate,
wherein the content of 2-ethylhexyl acid phosphate is 0.05 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the content of n-octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate is 0.15 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the content of 4,6-bis(octylthiomethyl)-o-cresol is 0.1 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene, and
wherein the content of dilauryl-3,3′-thiodipropionate is 0.2 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene.
5. A polymer composition comprising:
syndiotactic 1,2-polybutadiene;
2-ethylhexyl acid phosphate;
2,2′-dihydroxy-3,3′-bis(methylcyclohexyl)-5,5′-dimethyldiphenylmethane; and
didodecyl-3,3′-thiodipropionate,
wherein the content of 2-ethylhexyl acid phosphate is 0.01-2.0 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the content of 2,2′-dihydroxy-3,3′-bis(methylcyclohexyl)-5,5′-dimethyldiphenylmethane is 0.01-2.0 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene, and
wherein the content of didodecyl-3,3′-thiodipropionate is 0.01-2.0 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene.
6. The polymer composition according to claim 5 ,
wherein the content of 2-ethylhexyl acid phosphate is 0.03-1.6 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the content of 2,2′-dihydroxy-3,3′-bis(methylcyclohexyl)-5,5′-dimethyldiphenylmethane is 0.03-1.6 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene, and
wherein the content of didodecyl-3,3′-thiodipropionate is 0.03-1.6 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene.
7. A polymer composition comprising:
syndiotactic 1,2-polybutadiene;
2-ethylhexyl acid phosphate;
pentaerythritoltetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]; and
pentaerythritoltetrakis(β-laurylthiopropionate),
wherein the content of 2-ethylhexyl acid phosphate is 0.01-2.0 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the content of pentaerythritoltetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] is 0.01-2.0 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene, and
wherein the content of pentaerythritoltetrakis(β-laurylthiopropionate) is 0.01-2.0 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene.
8. The polymer composition according to claim 7 ,
wherein the content of 2-ethylhexyl acid phosphate is 0.03-1.6 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the content of pentaerythritoltetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] is 0.03-1.6 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene, and
wherein the content of pentaerythritoltetrakis(β-laurylthiopropionate) is 0.03-1.6 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene.
9. A polymer composition comprising:
syndiotactic 1,2-polybutadiene;
2-ethylhexyl acid phosphate;
n-octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate; and
distearyl-3,3′-thiodipropionate,
wherein the content of 2-ethylhexyl acid phosphate is 0.01-2.0 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the content of n-octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate is 0.01-2.0 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene, and
wherein the content of distearyl-3,3′-thiodipropionate is 0.01-2.0 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene.
10. The polymer composition according to claim 9 ,
wherein the content of 2-ethylhexyl acid phosphate is 0.03-1.6 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the content of n-octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate is 0.03-1.6 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene, and
wherein the content of distearyl-3,3′-thiodipropionate is 0.03-1.6 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene.
11. A polymer composition comprising:
syndiotactic 1,2-polybutadiene;
2-ethylhexyl acid phosphate;
n-octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate;
4,6-bis(octylthiomethyl)-o-cresol; and
dilauryl-3,3′-thiodipropionate,
wherein the content of 2-ethylhexyl acid phosphate is 0.01-2.0 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the combined content of n-octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate and 4,6-bis(octylthiomethyl)-o-cresol is 0.01-2.0 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene, and
wherein the content of dilauryl-3,3′-thiodipropionate is 0.01-2.0 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene.
12. The polymer composition according to claim 11 ,
wherein the content of 2-ethylhexyl acid phosphate is 0.03-1.6 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene,
wherein the combined content of n-octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate and 4,6-bis(octylthiomethyl)-o-cresol is 0.03-1.6 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene, and
wherein the content of dilauryl-3,3′-thiodipropionate is 0.03-1.6 wt. % based on 100 wt. % of syndiotactic 1,2-polybutadiene.