Magnetic tape
A magnetic tape comprising a non-magnetic support, a primer layer formed on one surface of the support, a magnetic layer formed on the primer layer, and a back layer formed on the other surface of the support, in which the tape has a total thickness of 4.0 to 5.4 μm, at least one of the primer layer and the magnetic layer contains a fatty acid amide, and an amount of the fatty acid amide extracted from the side of the magnetic layer with n-hexane is from 0.5 to 1.5 mg/cm 3 .
1. A magnetic tape comprising a non-magnetic support, a primer layer formed on one surface of said support and containing a non-magnetic powder and a binder, a magnetic layer formed on said primer layer and containing a magnetic powder and a binder, and a back layer formed on the other surface of said support,
wherein said tape has a total thickness of 4.0 to 5.4 μm,
at least one of said primer layer and said magnetic layer contains a fatty acid amide,
an amount of the fatty acid amide extracted from the side of the magnetic layer with n-hexane is from 0.5 to 1.5 mg/cm 3 ,
said fatty acid amide has a melting point of at least 70° C., and
E TD ·t 3 is at least 2.0×10 −6 N·m, and E MD /E TD is larger than 0.5 and less than 0.9, in which E MD and E TD are the Young's moduli (unit: Pa) of a magnetic tape in the machine and transverse directions of said magnetic tape, respectively and t is a thickness (unit: μm) of said magnetic tape.
2. A method for producing the magnetic tape of claim 1 , said method comprising adding the fatty acid amide to at least one of a non-magnetic coating composition of a primer layer and a magnetic coating composition for a magnetic layer.
3. The method according to claim 2 , wherein said fatty acid amide is added to said at least one of the coating compositions in the form of a dispersion in an organic solvent.
4. The method according to claim 2 , wherein said fatty acid amide is added to said at least one of the coating compositions before said coating composition is dispersed.
5. The magnetic tape according to claim 1 , wherein the fatty acid amide is added to the magnetic layer.
6. The magnetic tape according to claim 1 , wherein the fatty acid amide is selected from the group consisting of lauric acid amide, myristic acid amide, palmitic acid amide, stearic acid amide and oleic acid amide.
7. A magnetic tape comprising a non-magnetic support, a primer layer formed on one surface of said support and containing a non-magnetic powder and a binder, a magnetic layer formed on said primer layer and containing a magnetic powder and a binder, and a back layer formed on the other surface of said support,
wherein said tape has a total thickness of 4.0 to 5.4 μm,
at least one of said primer layer and said magnetic layer contains at least one fatty acid amide selected from the group consisting of lauric acid amide, myristic acid amide, palmitic acid amide, stearic acid amide and oleic acid amide,
an amount of the fatty acid amide extracted from the side of the magnetic layer with n-hexane is from 0.5 to 1.5 mg/cm 3 ,
said fatty acid amide has a melting point of at least 70° C., and
wherein E TD ·t 3 is at least 2.0×10 −6 N·m, and E MD /E TD is larger than 0.5 and less than 0.9, in which E MD and E TD are the Young's moduli (unit: Pa) of a magnetic tape in the machine and transverse directions of said magnetic tape, respectively and t is a thickness (unit: μm) of said magnetic tape.