Planar, rolled semi-finished product of aluminum alloys
A flat, rolled semi-finished product made of an aluminum alloy and a method of producing the product are disclosed. The aluminum alloys has the following alloy proportions in weight percentages: 2≦Mg≦5, Mn≦0.5, Cr≦0.35, Si≦0.4, Fe≦0.4, Cu≦0.3, Zn≦0.3, Ti≦0.15, other elements totaling no more than 0.15 and separately not exceeding 0.05, and the remainder consists of Al. The semifinished product is rolled from a bar and, during the rolling process, is subjected to at least one intermediate tempering between two cold reduction passes and to a final soft-annealing in a chamber furnace. A semi-finished product of this type does not have any flow lines after shaping or deep-drawing if the degree of reshaping before the first intermediate tempering is equal to at least 50%, the degree of reshaping before the final soft-annealing is no greater than 30%, and the semifinished product is drawn by 0.1 to 0.5% after the final soft-annealing.
1. A method for the production of a planar, rolled semi-finished product made of aluminum alloys, wherein the aluminum alloys have the following alloy proportions in weight-%:
2≦Mg≦5;
Mn≦0.5;
Cr≦0.35;
Si≦0.4;
Fe≦0.4;
Cu≦0.3;
Zn≦0.3;
Ti≦0.15; and
others at a sum of a maximum of 0.15, individually at a maximum of 0.05, residual Al,
wherein the semi-finished product is rolled off of an ingot, and during the rolling process is subjected to at least one intermediate soft annealing in a batch furnace between two cold roll passes and one final soft annealing in a batch furnace after the two cold roll passes, wherein the degree of deformation before the first intermediate soft annealing is at least 50%, the degree of deformation before the final soft annealing is not more than 30%, and the semi-finished product is stretch-formed by 0.1 to 0.5% after the final soft annealing.
2. The method of claim 1 , wherein the method does not include soft annealing in a continuous annealing furnace between the first cold roll pass and the stretch-forming; and
the method does not include quenching between the first cold roll pass and the stretch-forming.
3. A method for the production of a planar, rolled semi-finished product that resists the formation of flow lines upon subsequent deformation or deep-drawing, the method comprising:
providing a strip formed by hot rolling an ingot that comprises at least one aluminum alloy, the at least one aluminum alloy having the following weight-% alloy proportions:
2≦Mg≦5;
Mn≦0.5;
Cr≦0.35;
Si≦0.4;
Fe≦0.4;
Cu≦0.3;
Zn≦0.3;
Ti≦0.15; and
others at a sum of a maximum of 0.15, individually at a maximum of 0.05, residual Al;
cold rolling the strip to a degree of deformation of at least 50% in a first cold rolling step;
subjecting the strip to at least one intermediate soft anneal in a batch furnace after the first cold rolling step;
cold rolling the strip to a degree of deformation of less than 30% in a second cold rolling step after subjecting the strip to the at least one intermediate soft anneal;
subjecting the strip to a final soft annealing in a batch furnace after the second cold rolling step; and
stretch-forming the strip or a sheet made of the strip by 0.1 to 0.5% after the final soft annealing to form a semi-finished product that resists formation of flow lines upon subsequent deformation or deep-drawing;
wherein the strip is not soft annealed in a continuous annealing furnace between the first cold rolling step and the stretch-forming; and the strip is not quenched between the first cold rolling step and the stretch-forming.