Battery
A battery is provided which has a high capacity and can improve battery characteristics, such as cycle characteristics. The battery includes a spirally wound electrode body, wherein a cathode and an anode are wound with a separator in between. The anode includes, for example, simple substances, alloys, compounds of metal elements or metalloid elements capable of forming an alloy with Li, the like and combinations thereof. An electrolytic solution wherein an electrolyte salt is dissolved in a solvent is impregnated in the separator. For the electrolyte salt, a light metallic salt having B—O bond or P—O bond, such as difluoro[oxalato-O,O′]lithium borate and tetra fluoro[oxalato-O,O′]lithium phosphate, can be used. By forming a stable coating, decomposition reaction of the solvent can be inhibited, and reaction between the anode and the solvent can be prevented.
1. A battery comprising:
a cathode;
an anode having an anode active material including silicon deposited on a current collector material by vapor-phase deposition, wherein the silicon is alloyed with at least part of the current collector, and
an electrolyte,
wherein the electrolyte includes
a light metallic salt having M-X bond where M represents a transition metal element or a 3B Group element, a 4B Group element, or a 5B Group element in a short-period periodic table and where X represents oxygen (O) or sulfur (S),
at least one or more additional light metallic salts selected from the group consisting of LiPF 6 , LiBF 4 , LiClO 4 , LiAsF 6 , a lithium salt expressed by Chemical formula 11, and a lithium salt expressed by Chemical formula 12, where Chemical formulas 11 and 12 are provided as follows:
LiN(C m F 2m+1 SO 2 )(C n F 2n+1 SO 2 ) Chemical formula 11
where m and n are integer numbers ranging from 1 or greater
LiC(C p F 2p+1 SO 2 )(C q F 2q+1 SO 2 )(C r F 2r+1 SO 2 ) Chemical formula 12
where p, q, and r are integer numbers ranging from 1 or greater, and
wherein the anode active material excludes a binder.
2. The battery according to claim 1 , wherein the light metallic salt has B—O bond or P—O bond.
3. The battery according to claim 1 , wherein the light metallic salt has O—B—O bond or O—P—O bond.
4. The battery according to claim 1 , wherein the light metallic salt is a cyclic compound.
5. The battery according to claim 1 , wherein the electrolyte further includes a solvent, and the content of the light metallic salt ranges from about 0.01 mol/kg to about 2.0 mol/kg in relation to the solvent.
6. The battery according to claim 1 , wherein the electrolyte further includes one or more additional light metallic salts in addition to the light metallic salt.
7. The battery according to claim 1 , wherein the electrolyte further includes a high molecular weight compound or an ion conductive inorganic compound.
8. The battery according to claim 1 , wherein the cathode includes a lithium-containing compound containing lithium (Li), at least one selected from the group consisting of cobalt (Co), nickel (Ni), and manganese (Mn), and oxygen (O).
9. The battery according to claim 1 , wherein a surface roughness of the anode current collector is about 0.1 μm or more by arithmetic average roughness.
10. The battery according to claim 1 , wherein the light metallic salt and the additional light metallic salts are in a ratio of from 9:1 to 1:9.
11. The battery according to claim 1 , wherein the anode active material including silicon has a thickness of approximately 4 μm or less.
12. A battery comprising:
a cathode;
an anode having an anode active material including silicon deposited on a current collector material by vapor-phase deposition, wherein the silicon is alloyed with at least part of the current collector, and
an electrolyte, wherein the electrolyte includes a light metallic salt having M-X bond where M represents a transition metal element or a 3B Group element, a 4B Group element, or a 5B Group element in a short-period periodic table and where X represents oxygen (O) or sulfur (S),
at least one or more additional light metallic salts selected from the group consisting of LiPF 6 , LiBF 4 , LiClO 4 , LiAsF 6 , a lithium salt expressed by Chemical formula 11, and a lithium salt expressed by Chemical formula 12, where Chemical formulas 11 and 12 are provided as follows:
LiN(C m F 2m+1 SO 2 )(C n F 2n+1 SO 2 ) Chemical formula 11
where m and n are integer numbers ranging from 1 or greater
LiC(C p F 2p+1 SO 2 )(C q F 2q+1 SO 2 )(C r F 2r+1 SO 2 ) Chemical formula 12
where p, q, and r are integer numbers ranging from 1 or greater, and
wherein the anode active material including silicon has a thickness of approximately 4 μm or less, and
wherein the anode active material excludes a binder.