Marker composite for medical implants
An x-ray marker for medical implants made of a biocorrodible metallic material, wherein the x-ray marker composite includes 1-40 weight parts of a carrier matrix having a melting point greater than or equal to 43° C., which comprises 90 weight-percent or more at least one triglyceride; and 60-99 weight parts of a radiopaque marker component which is embedded in the carrier matrix.
1. A marker composite for medical implants, the marker composite comprising:
(a) 1-40 weight parts of a carrier matrix formed from at least one triglyceride having a melting point greater than or equal to 43° C., the carrier matrix comprising 90 weight-percent or more at least one triglyceride; and
(b) 60-99 weight parts of a radiopaque marker component which is embedded in the carrier matrix,
wherein the marker composite is suitable for use as a coating for a medical implant,
wherein the medical implant is made of a biocorrodible metallic magnesium alloy material.
2. The marker composite of claim 1 , wherein the carrier matrix comprises 90 weight-percent or more of a hydrogenated soybean oil having a proportion of palmitic acid in the fatty acids of the triglyceride in the range from 9-16 weight-percent and a proportion of stearic acid in the fatty acids of the triglyceride in the range from 79-89 weight-percent.
3. The marker composite of claim 1 , wherein the marker component is a metal powder having a mean particle size less than or equal to 3 μm.
4. The marker composite of claim 3 , wherein the metal powder is an element selected from the group consisting of Au, Ir, Pt, and Ta.
5. The marker composite of claim 1 , wherein the carrier matrix further comprises tocopherol as an additive which lowers the viscosity.
6. A medical implant, coated and/or filled with a marker composite, comprising:
(a) 1-40 weight parts of a carrier matrix having a melting point greater than or equal to 43° C., which comprises 90 weight-percent or more at least one triglyceride; and
(b) 60-99 weight parts of a radiopaque marker component, which is embedded in the carrier matrix,
wherein the medical implant is made of a biocorrodible metallic material.
7. A medical implant, coated and/or filled with a marker, comprising:
(a) 1-40 weight parts of a carrier matrix having a melting point greater than or equal to 43° C., which comprises 90 weight-percent or more at least one triglyceride; and
(b) 60-99 weight parts of a radiopaque marker component, which is embedded in the carrier matrix,
wherein the medical implant is made of a biocorrodible magnesium alloy.
8. A medical implant, coated and/or filled with a marker composite, comprising:
(a) 1-40 weight parts of a carrier matrix having a melting point greater than or equal to 43° C., which comprises 90 weight-percent or more at least one triglyceride; and
(b) 60-99 weight parts of a radiopaque marker component, which is embedded in the carrier matrix;
wherein the carrier matrix comprises 90 weight-percent or more of a hydrogenated soybean oil having a proportion of palmitic acid in the fatty acids of the hydrogenated soybean oil in the range from 9-16 weight-percent and a proportion of stearic acid in the fatty acids of the hydrogenated soybean oil in the range from 79-89 weight-percent,
wherein the medical implant is made of a biocorrodible metallic material.