Coated cutting tool
The present invention relates to a coated cutting tool ( 1 ) including a substrate ( 8 ) and a coating ( 9 ) formed on the substrate ( 8 ), wherein the coating ( 9 ) includes a first coating ( 10 ) composed of TiCN and a second coating ( 11 ) composed of α-Al 2 O 3 , the first coating ( 10 ) is positioned between the substrate ( 8 ) and the second coating ( 11 ) and has tensile stress S 1 , the second coating ( 11 ) has compressive stress S 2 , and the tensile stress S 1 and the compressive stress S 2 are defined by the following equation (I): 400 MPa≦| S 2 −S 1|≦3500 MPa (I).
1. A coated cutting tool comprising a substrate, comprising cemented carbides, and a coating formed on the substrate,
wherein the coating includes a first coating composed of TiCN and a second coating composed of α-Al2O3,
both the first and second coatings are formed by a chemical vapor deposition (CVD) method,
the first coating is positioned between the substrate and the second coating and has tensile stress S 1 ,
the second coating has compressive stress S 2 ,
the tensile stress S 1 is 5 MPa to 300 MPa, and
the tensile stress S 1 and the compressive stress S 2 are defined by the following equation (I):
400 MPa≦| S 2− S 1|≦3500 MPa (I).
2. The coated cutting tool according to claim 1 , wherein the ratio of surface area increase of a portion concerned in cutting is 0.0005 to 0.07.
3. The coated cutting tool according to claim 1 , wherein the first coating has a columnar structure with an aspect ratio of 3 or more and a crystal structure with an average grain diameter of 0.05 μm to 1.5 μm.
4. The coated cutting tool according to claim 1 , wherein the first coating has a thickness of 2 to 20 μm, and the second coating has a thickness of 0.5 to 20 μm.
5. The coated cutting tool according to claim 1 , wherein the first coating further contains oxygen.
6. The coated cutting tool according to claim 1 , wherein the first coating further contains at least one element selected from the group consisting of the group IVa elements, group Va elements, and group VIa elements in the periodic table, Si, Y, B, and S.
7. The coated cutting tool according to claim 1 , wherein the second coating further contains at least one element selected from the group consisting of the group IVa elements, group Va elements, and group VIa elements in the periodic table, Si, Y, B, and S.