Polyacetal resin composition
Polyacetal resin compositions, including a polyacetal copolymer, 0.2 to 2 parts by mass of a hindered amine material and 0.2 to 10 parts by mass of powdery aluminum, with respect to 100 parts by mass of a polyacetal copolymer, and 0.3 to 10 parts by mass of a fatty acid having a carbon number of 10 to 30, with respect to 100 parts by mass of the powdery aluminum. Methods of making the compositions, and end products including the resin compositions are also provided.
1. A polyacetal resin composition comprising:
a polyacetal copolymer;
0.2 to 2 parts by mass of a hindered amine material and 0.2 to 10 parts by mass of powdery aluminum, with respect to 100 parts by mass of the polyacetal copolymer; and
0.3 to 10 parts by mass of a fatty acid having a carbon number of 10 to 30, with respect to 100 parts by mass of the powdery aluminum.
2. The polyacetal resin composition according to claim 1 , wherein the polyacetal copolymer has a melt mass flow rate (MFR) of 2.5 to 40 g/10 minutes.
3. The polyacetal resin composition according to claim 1 , further comprising 0.3 to 3 parts by mass of a polyalkylene glycol, with respect to 100 parts by mass of the polyacetal copolymer.
4. The polyacetal resin composition according to claim 3 , wherein the polyalkylene glycol is a polyethylene glycol having a number average molecular weight of 800 to 500,000.
5. The polyacetal resin composition according to claim 1 , further comprising 0.03 to 0.25 part by pass of a hydrazide compound, with respect to 100 parts by mass of the polyacetal copolymer.
6. The polyacetal resin composition according to claim 1 , wherein the hindered amine material has a piperidine derivative structure represented by a general formula (3);
where R 1 to R 4 are identical or different alkyl groups.
7. The polyacetal resin composition according to claim 1 , wherein the powdery aluminum has a discoidal or scale-like shape.
8. The polyacetal resin composition according to claim 1 , wherein the powdery aluminum has an average particle diameter of 3 to 80 μm.
9. The polyacetal resin composition according to claim 1 , wherein the powdery aluminum has a particle diameter distribution [Dw/Dn] of 1.1 to 2.0.
10. The polyacetal resin composition according to claim 1 , wherein the powdery aluminum has an average particle thickness of 0.4 μm or greater.
11. The polyacetal resin composition according to claim 1 , wherein the powdery aluminum includes at least two aluminum powders, each aluminum powder having an average particle diameter, wherein the average particle diameter of the at least two aluminum powders differs by 20 μm or greater.
12. A molded body formed from the polyacetal resin composition according to claim 1 .
13. The molded body according to claim 12 , wherein the molded body is used as a part for office automation equipment, an audio, video, or information device, a communication device, an industrial part used for office furniture or housing equipment, or a vehicle interior/exterior component.
14. The molded body according to claim 12 , wherein the part is a handle, a shift knob, a lever, a switch, or a button.
15. The molded body according to claim 12 , wherein a design surface of the part is partially or entirely grain processed.
16. A method of producing the polyacetal resin composition according to claim 1 , the method comprising:
mixing the powdery aluminum and the fatty acid;
pre-melt-kneading the polyacetal copolymer and the hindered amine material; and
mixing the mixtures obtained from the mixing and the pre-melt-kneading.
17. The method of producing the polyacetal resin composition according to claim 16 , wherein the powdery aluminum is dried, and then mixed with the fatty acid.
18. The polyacetal resin composition according to claim 2 , further comprising 0.3 to 3 parts by mass of a polyalkylene glycol, with respect to 100 parts by mass of the polyacetal copolymer.