Aluminum alloy clad sheet for a heat exchanger and its production method
Disclosed herein is an aluminum alloy clad sheet for a heat exchanger including a core layer, a sacrificial layer formed on one surface of the core layer, and a filler layer including an Al—Si based alloy formed on the other surface of the core layer. The core layer includes a predetermined amount of Si, Cu, Mn, Ti, and Mg, the remainder including Al and inevitable impurities, and the sacrificial layer includes a predetermined amount of Si, Mn, and Zn, the remainder including Al and inevitable impurities. The core layer has a crystal grain size after the brazing heat treatment at 595° C. for 3 minutes of at least 50 μm and less than 300 μm. The filler layer and the sacrificial layer are defined for their thickness, and the number of intermetallic compounds in the core layer is also defined to a predetermined range. By such constitution, the aluminum alloy clad sheet has improved fatigue life and post-braze strength, high corrosion resistance, and excellent erosion resistance and brazeability.
1. An aluminum alloy clad sheet for a heat exchanger comprising a core layer, a sacrificial layer formed on one surface of the core layer, and a filler layer comprising an Al—Si based alloy formed on the other surface of the core layer, wherein
the core layer comprises 0.5 to 1.1 mass % Si, 0.5 to 1.1 mass % Cu, at least 0.05 mass % and less than 0.6 mass % Mn, 0.05 to 0.25 mass % Ti, up to 0.45 mass % Mg, and the remainder of Al and inevitable impurities,
the sacrificial layer comprises in excess of 0.5 mass % and up to 1.1 mass % Si, 0.001 to 1.7 mass % Mn, 3.0 to 6.0 mass % Zn, and the remainder of Al and inevitable impurities,
the core layer has a crystal grain size after brazing heat treatment at 595° C. for 3 minutes of at least 50 μm and less than 300 μm
the filler layer has a thickness of 20 to 55 μm, and the sacrificial layer has a thickness of 25 to 50 μm, and
grains of intermetallic compounds selected from the group consisting of Al—Mn, Al—Mn—Si, Al—Fe, Al—Fe—Si, and Al—Mn—Fe—Si-based intermetallic compounds having a grain diameter of at least 0.65 μm are present in the core layer and are distributed such that those having a grain diameter of 0.65 to 15 μm are present in the core layer in an amount not exceeding 5×10 3 grains per mm 2 , and those having a grain diameter in excess of 15 μm are present in the core layer in an amount not exceeding 50 grains per mm 2 .
2. An aluminum alloy clad sheet for a heat exchanger comprising a core layer, a sacrificial layer formed on one surface of the core layer, and a filler layer comprising an Al—Si based alloy formed on the other surface of the core layer, wherein
the core layer comprises:
Si: 0.5 to 1.1 mass %,
Cu: 0.5 to 1.1 mass %,
Mn: at least 0.05 mass % and less than 0.6 mass %,
Ti: 0.05 to 0.25 mass %,
Mg: up to 0.45 mass %, and
the remainder of Al and inevitable impurities;
the sacrificial layer comprises:
Si: in excess of 0.5 mass % and up to 1.1 mass %,
Mn: 0.001 to 1.7 mass %,
Zn: 3.0 to 6.0 mass %, and
the remainder of Al and inevitable impurities,
the core layer has a crystal grain size after brazing heat treatment at 595° C. for 3 minutes of at least 50 μm and less than 300 μm,
the filler layer has a thickness of 20 to 55 μm,
the sacrificial layer has a thickness of 25 to 50 μm, and
grains of intermetallic compounds selected from the group consisting of Al—Mn, Al—Mn—Si, Al—Fe, Al—Fe—Si, and Al—Mn—Fe—Si-based intermetallic compounds having a grain diameter of at least 0.65 μm are present in the core layer and are distributed such that those having a grain diameter of 0.65 to 15 μm are present in the core layer in an amount from 1035 to 5000 grains per mm 2 , and those having a grain diameter in excess of 15 μm are present in the core layer in an amount from 3 to 50 grains per mm 2 .
3. An aluminum alloy clad sheet for a heat exchanger according to claim 2 , wherein the amount of Si in the sacrificial layer is in excess of 0.6 mass % and up to 1.0 mass %.
4. An aluminum alloy clad sheet for a heat exchanger according to claim 2 , wherein the amount of Fe present in the core layer is up to 0.2 mass %.