Polyester/polycarbonate alloy resin composition and molded product made using the same
Disclosed are a polyester/polycarbonate alloy resin composition that includes: (A) a mixed resin including (A-1) a polycarbonate resin having a weight average molecular weight ranging from about 30,000 to about 200,000 g/mol and (A-2) a polyester resin having an intrinsic viscosity of about 0.85 to about 1.52 dl/g; (B) an acryl-based resin; and (C) an impact-reinforcing agent, and a molded product made using the polyester/polycarbonate alloy resin composition.
1. A polyester/polycarbonate alloy resin composition comprising:
(A) about 100 parts by weight of a mixed resin including (A-1) about 10 to about 60 wt % of a polycarbonate resin having a weight average molecular weight ranging from about 30,000 to about 200,000 g/mol, and (A-2) about 40 to about 90 wt % of a polyester resin having an intrinsic viscosity of about 0.85 to about 1.52 dl/g;
(B) about 0.1 to about 10 parts by weight of an acryl-based resin, wherein the acryl-based resin (B) is a terpolymer comprising an alkyl ester (meth)acrylate monomer, an ester (meth)acrylate monomer, or a combination thereof; an aromatic vinyl monomer comprising styrene, o-ethyl styrene, m-ethyl styrene, p-ethyl styrene, alpha methyl styrene or a combination thereof; and an unsaturated nitrile monomer comprising acrylonitrile, methacrylonitrile, ethacrylonitrile, or a combination thereof; and
(C) about 1 to about 30 parts by weight of an impact-reinforcing agent.
2. The polyester/polycarbonate alloy resin composition of claim 1 , wherein the polycarbonate resin (A-1) has a weight average molecular weight ranging from about 30,000 to about 50,000 g/mol.
3. The polyester/polycarbonate alloy resin composition of claim 1 , wherein the polycarbonate resin (A-1) is prepared by reacting one or more diphenols with phosgene, halogen formate, carbonate ester, or a combination thereof.
4. The polyester/polycarbonate alloy resin composition of claim 1 , wherein the polyester resin (A-2) comprises polybutylene terephthalate.
5. The polyester/polycarbonate alloy resin composition of claim 1 , wherein the polyester resin (A-2) has an intrinsic viscosity [η] of about 1.03 to about 1.22 dl/g.
6. The polyester/polycarbonate alloy resin composition of claim 1 , wherein the impact-reinforcing agent (C) comprises a core-shell type copolymer, a linear olefin-based copolymer, or a combination thereof.
7. The polyester/polycarbonate alloy resin composition of claim 6 , wherein the core-shell type copolymer comprises a rubbery polymer obtained by polymerizing a monomer comprising a diene-based monomer, an acryl-based monomer, a silicon-based monomer, or a combination thereof and at least one unsaturated monomer grafted thereon, wherein the unsaturated monomer comprises an acryl-based monomer, an aromatic vinyl monomer, a unsaturated nitrile monomer, or a combination thereof.
8. The polyester/polycarbonate alloy resin composition of claim 6 , wherein the linear olefin-based copolymer comprises a copolymer of an olefin-based monomer and an acryl-based monomer.
9. The polyester/polycarbonate alloy resin composition of claim 1 , wherein the polyester/polycarbonate alloy resin composition further comprises an additive comprising an antibacterial agent, a heat stabilizer, an antioxidant, a release agent, a light stabilizer, a compatibilizer, a dye, an inorganic material additive, a surfactant, a coupling agent, a plasticizer, an admixture, a colorant, a stabilizer, a lubricant, an antistatic agent, a pigment, a flameproofing agent, a weather-resistance agent, a ultraviolet (UV) blocking agent, a filler, a nucleating agent, an adhesion aid, an adhesive, a flame retardant, or a combination thereof.
10. A molded product made using the polyester/polycarbonate alloy resin composition according to claim 1 .