Desulfurization catalyst for catalytic cracked gasoline and method for desulfurizing catalytic cracked gasoline using the same
The desulfurization catalyst for catalytic cracked gasoline according to the present invention has high performance in removal of sulfur compounds in gasoline fractions. This catalyst contains particulate vanadium oxide having the average particle diameter in the range from 0.1 to 10 μm at the content in the range from 0.3 to 3 weight % calculated as that of V 2 O 5 . The porous spherical particles of inorganic oxide are made of crystalline aluminosilicate zeolite and a porous inorganic oxide matrix, and furthermore contain antimony.
1. A desulfurization catalyst for catalytic cracked gasoline comprising porous spherical particles of inorganic oxide, and vanadium oxide particles present in the porous spherical particles,
wherein an average particle diameter of the spherical particles is in a range from 40 to 90 μm, and an average particle diameter of the vanadium oxide particles is in a range from 1 to 10 μm, and
a content of the vanadium oxide particle as calculated as that of V 2 O 5 is in a range from 0.5 to 2 weight %.
2. The desulfurization catalyst for catalytic cracked gasoline according to claim 1 , wherein the porous spherical particles of inorganic oxide contain antimony.
3. The desulfurization catalyst for catalytic cracked gasoline according to claim 1 , wherein the porous spherical particles of inorganic oxide are made of a crystalline aluminosilicate zeolite and a porous matrix of inorganic oxide.
4. A method of desulfurizing catalytic cracked gasoline, wherein a catalytic cracking reaction and a desulfurization reaction are simultaneously performed by contacting heavy hydrocarbon oil and/or vacuum gas oil under fluidized catalytic cracking conditions to mixture catalysts prepared by mixing the desulfurization catalyst for catalytic cracked gasoline according to claim 1 and catalyst for catalytic cracked hydrocarbon at a weight ratio in a range from 5/95 to 50/50.
5. The desulfurization catalyst for catalytic cracked gasoline according to claim 1 , wherein the average particle diameter of the vanadium oxide particles is 2.1 to 6.5 μm.
6. A desulfurization catalyst for catalytic cracked gasoline comprising porous spherical particles of inorganic oxide, and vanadium oxide particles present in the porous spherical particles,
wherein an average particle diameter of the spherical particles is in a range from 40 to 90 μm, and an average particle diameter of the vanadium oxide particles is in a range from 1 to 10 μm, and
the vanadium oxide particles are present in the particulate state without being homogeneously distributed in the porous spherical particles to improve affinity of the vanadium oxide to organic sulfur compounds.
7. The desulfurization catalyst for catalytic cracked gasoline according to claim 6 , wherein the porous spherical particles of inorganic oxide comprises 5-50 wt % of a crystalline aluminosilicate zeolite and a porous matrix of inorganic oxide.