Core-shell particle, method, and composition

1. A method of forming a core-shell particle, comprising:

forming a polyorganosiloxane core by polymerizing a polydialkylsiloxane precursor in the presence of water and a first emulsifying agent and in the absence of a tri- or tetraalkoxysilane;

crosslinking the polyorganosiloxane core by reacting a tri- or tetraalkoxysilane with the polyorganosiloxane core;

forming a graftlinker-functionalized crosslinked polyorganosiloxane core by reacting the crosslinked polyorganosiloxane core with a graftlinking agent comprising an alkoxysilane group and an aliphatic carbon-carbon double or triple bond; and

forming a core-shell particle by polymerizing a shell-forming monomer in the presence of the graftlinker functionalized crosslinked polysiloxane core and a second emulsifying agent different from the first emulsifying agent; wherein the shell-forming monomer comprises an alkenyl aromatic compound;

wherein the core-shell particle has a mean diameter of 220 to 300 nanometers.

2. The method of claim 1 , wherein the polymerizing a polydialkylsiloxane precursor is conducted in the absence of a graftlinking agent.

3. The method of claim 1 , wherein the crosslinking the polyorganosiloxane core is conducted in the absence of a graftlinking agent.

4. The method of claim 1 , wherein the polydialkylsiloxane precursor comprises a cyclic dimethylsiloxane oligomer or polymer comprising 4 to 12 dimethylsiloxane units.

5. The method of claim 1 , wherein the polydialkylsiloxane precursor comprises octamethylcyclotetrasiloxane.

6. The method of claim 1 , wherein the polydialkylsiloxane precursor is used in an amount of about 50 to 90 weight percent based on the total weight of the polydialkylsiloxane precursor, the tri- or tetraalkoxysilane, the graftlinking agent, and the shell-forming monomer.

7. The method of claim 1 , wherein the first emulsifying agent comprises dodecylbenzenesulfonic acid.

8. The method of claim 1 , wherein the first emulsifying agent is used in an amount of 0.5 to 1.5 weight percent based on the total weight of the water and the polydialkylsiloxane precursor.

9. The method of claim 1 , wherein the water is used in an amount of 40 to 90 weight percent based on the total weight of the polydialkylsiloxane precursor, the tri- or tetraalkoxysilane, the graftlinking agent, the shell-forming monomer, and the water.

10. The method of claim 1 , wherein the tri- or tetraalkoxysilane reacted with the polyorganosiloxane core is selected from the group consisting of tetraethyl orthosilicate, methyltrimethoxysilane, methyltriethoxysilane, tetramethoxysilane, tetrapropoxysilane, and mixtures thereof.

11. The method of claim 1 , wherein the tri- or tetraalkoxysilane reacted with the polyorganosiloxane core comprises tetraethyl orthosilicate.

12. The method of claim 1 , wherein the tri- or tetraalkoxysilane reacted with the polyorganosiloxane core is used in an amount of 2 to 30 weight percent based on the total weight of the polydialkylsiloxane precursor, and the tri- or tetraalkoxysilane.

13. The method of claim 1 , wherein the graftlinking agent is selected from the group consisting of methacryloxypropyltrimethoxysilane, methacryloxypropyltriethoxysilane, methacryloxypropylmethyldimethoxysilane, 3-mercaptopropyltrimethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, vinyltris(2-methoxyethoxy)silane, and mixtures thereof.

14. The method of claim 1 , wherein the graftlinking agent comprises methacryloxypropyltrimethoxysilane.

15. The method of claim 1 , wherein the graftlinking agent is used in an amount of 1 to 7.5 weight percent based on the total weight of the polydialkylsiloxane precursor, the tri- or tetraalkoxysilane, the graftlinking agent, and the shell-forming monomer.

16. The method of claim 1 , wherein the alkenyl aromatic monomer comprises styrene.

17. The method of claim 1 , wherein the shell forming monomer further comprises an acrylate monomer, acrylonitrile, methacrylonitrile, or a mixture thereof.

18. The method of claim 1 , wherein the shell-forming monomer further comprises a functionalized monomer comprising a carbon-carbon double or triple bond and at least one other functional group selected from the group consisting of hydroxy, glycidyl, and nitrile.

19. The method of claim 18 , wherein the functionalized monomer is selected from the group consisting of glycidyl methacrylate, 2-hydroxyethyl methacrylate, acrylonitrile, and mixtures thereof.

20. The method of claim 1 , wherein the shell-forming monomer is used in an amount of 10 to 50 weight percent based on the total weight of the polydialkylsiloxane precursor, the tri- or tetraalkoxysilane, the graftlinking agent, and the shell-forming monomer.

21. The method of claim 1 , wherein the second emulsifying agent comprises sodium dodecylbenzenesulfonate.

22. The method of claim 1 , wherein the second emulsifying agent is used in an amount of 0.2 to 5 weight percent based on the weight of the shell-forming monomer.

23. The method of claim 1 , wherein the core-shell particle comprises a core having a mean diameter of 200 to 280 nanometers.

24. The method of claim 1 , wherein the core shell particle has a gel content of 80 to 95 percent measured after 48 hours immersion in toluene at 23° C.

25. The method of claim 1 , wherein the core shell particle exhibits a first glass transition temperature of −134 to −124° C. and a second glass transition temperature of 103 to 113° C., measured by differential scanning calorimetry using a rate of temperature change of 20° C. per minute.

26. The method of claim 1 , wherein the core shell particle exhibits at least 90 weight percent residue at 300° C. and at least 10 weight percent residue at 600° C. when analyzed by thermogravimetric analysis using an air atmosphere and a rate of temperature change of 20° C. per minute.

27. The method of claim 1 ,

wherein the polydialkylsiloxane precursor comprises octamethylcyclotetrasiloxane;

wherein the tri- or tetraalkoxysilane reacted with the polyorganosiloxane core comprises tetraethyl orthosilicate;

wherein the first emulsifying agent comprises dodecylbenzenesulfonic acid;

wherein the graftlinking agent comprises methacryloxypropyltrimethoxysilane;

wherein the alkenyl aromatic compound comprises styrene; and

wherein the core-shell particle has a gel content of 85 to 95 percent measured after 48 hours immersion in toluene at 23° C.

28. A method of forming a core-shell particle, comprising:

forming a polyorganosiloxane core by polymerizing a polydialkylsiloxane precursor in the presence of water and a first emulsifying agent;

crosslinking the polyorganosiloxane core by reacting a tri- or tetraalkoxysilane with the polyorganosiloxane core;

forming a graftlinker-functionalized crosslinked polyorganosiloxane core by reacting the crosslinked polyorganosiloxane core with a graftlinking agent comprising an alkoxysilane group and an aliphatic carbon-carbon double or triple bond; and

forming a core-shell particle by polymerizing a shell-forming monomer in the presence of the graftlinker functionalized crosslinked polysiloxane core and a second emulsifying agent different from the first emulsifying agent; wherein the shell-forming monomer comprises an alkenyl aromatic compound; wherein the shell-forming monomer further comprises a functionalized monomer comprising a carbon-carbon double or triple bond and at least one other functional group selected from the group consisting of hydroxy, glycidyl, and nitrile; and wherein the functionalized monomer comprises glycidyl methacrylate;

wherein the core-shell particle has a mean diameter of 220 to 300 nanometers.

29. A method of forming a core-shell particle, comprising:

forming a polyorganosiloxane core by polymerizing a polydialkylsiloxane precursor in the presence of water and a first emulsifying agent; wherein the polydialkylsiloxane precursor comprises octamethylcyclotetrasiloxane; wherein the first emulsifying agent comprises dodecylbenzenesulfonic acid;

crosslinking the polyorganosiloxane core by reacting a tri- or tetraalkoxysilane with the polyorganosiloxane core; wherein the tri- or tetraalkoxysilane comprises tetraethyl orthosilicate;

forming a graftlinker-functionalized crosslinked polyorganosiloxane core by reacting the crosslinked polyorganosiloxane core with a graftlinking agent comprising an alkoxysilane group and an aliphatic carbon-carbon double or triple bond; wherein the graftlinking agent comprises methacryloxypropyltrimethoxysilane; and

forming a core-shell particle by polymerizing a shell-forming monomer in the presence of the graftlinker functionalized crosslinked polysiloxane core and a second emulsifying agent different from the first emulsifying agent; wherein the shell-forming monomer comprises an alkenyl aromatic compound; wherein the polymerizing a shell forming monomer comprises copolymerizing styrene and glycidyl methacrylate;

wherein the core-shell particle has a mean diameter of 220 to 300 nanometers; and

wherein the core-shell particle has a gel content of 85 to 95 percent measured after 48 hours immersion in toluene at 23° C.

30. A core-shell particle, comprising:

a crosslinked polydimethylsiloxane core;

a shell comprising a styrene homopolymer or copolymer; and

covalent linkages between the crosslinked polydimethylsiloxane core and the shell;

wherein the core-shell particle has a mean diameter of 220 to 300 nanometers; and

wherein the core-shell particle has a gel content of 85 to 95 percent measured after 48 hours immersion in toluene at 23° C.

31. The core-shell particle of claim 30 , wherein the crosslinked polydimethylsiloxane core has a mean diameter of 200 to 280 nanometers.

32. A core shell particle, comprising:

a crosslinked polydimethylsiloxane core; wherein the crosslinked polydimethylsiloxane core is the product of copolymerizing reactants comprising octamethylcyclotetrasiloxane and tetraethyl orthosilicate;

a shell comprising a styrene homopolymer or copolymer; wherein the shell is a homopolymer of styrene or a copolymer of styrene and glycidyl methacrylate; and

covalent linkages between the crosslinked polydimethylsiloxane core and the shell; wherein the covalent linkages are reaction products of a graftlinking agent comprising methacryloxypropyltrimethoxysilane;

wherein the core-shell particle has a mean diameter of 240 to 270 nanometers;

wherein the core-shell particle has a gel content of 85 to 95 percent measured after 48 hours immersion in toluene at 23° C.

33. A thermoplastic composition, comprising:

a polymer; and

a core-shell particle, comprising

a crosslinked polydimethylsiloxane core;

a shell comprising a styrene homopolymer or copolymer; and

covalent linkages between the crosslinked polydimethylsiloxane core and the shell;

wherein the core-shell particle has a mean diameter of 220 to 300 nanometers; and

wherein the core-shell particle has a gel content of 85 to 95 percent measured after 48 hours immersion in toluene at 23° C.

34. The thermoplastic composition of claim 33 , wherein the crosslinked polydimethylsiloxane core has a mean diameter of 200 to 280 nanometers.

35. The thermoplastic composition of claim 33 , comprising 5 to 20 weight percent of the core-shell particle, based on the total weight of the composition.

36. The thermoplastic composition of claim 33 , wherein the polymer comprises a poly(arylene ether).

37. The thermoplastic composition of claim 33 , wherein the polymer comprises a poly(arylene ether) and at least one additional polymer selected from the group consisting of polystyrenes, rubber-modified polystyrenes, unhydrogenated or hydrogenated block copolymers of an alkenyl aromatic compound and a conjugated diene, polyamides, polyimides, polyethers, polyetherimides, polyolefins, and polyesters.

38. The method of claim 1 , wherein the shell-forming monomer further comprises glycidyl methacrylate.

39. The core-shell particle of claim 30 , wherein the shell comprises the styrene copolymer, and wherein the styrene copolymer comprises a copolymer of styrene and glycidyl methacrylate.

40. The thermoplastic composition of claim 33 , wherein the shell comprises the styrene copolymer, and wherein the styrene copolymer comprises a copolymer of styrene and glycidyl methacrylate.